Automobile noncaking type sealant and preparation method thereof
A non-bonding, sealant technology, applied in the direction of adhesive types, chemical instruments and methods, non-polymer adhesive additives, etc., can solve problems such as being unfavorable to large-scale production, complex processes, etc., and achieve good sealing , the preparation process is simple, the production cost is low
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] (1), take by weighing 50 parts of EPDM rubber, 30 parts of polyurethane resin, 2 parts of talcum powder, 1 part of angelica oil, 1 part of paraffin wax, 2 parts of polyethylene glycol, join in the internal mixer, Mix at 120-130°C for 15-20 minutes, then add 1 part of foaming aid, 1 part of cross-linking accelerator, 2 parts of flame retardant, 0.5 parts of anti-yellowing agent and 3 parts of filler in sequence, at 120-130°C Next, mix for 15-20 minutes to form a uniform mixture and set aside;
[0023] (2) Add the mixture prepared in step (1) into a three-roller machine, grind for 2 to 3 times, filter through a filter, vacuumize and defoam for 20 minutes to obtain the product.
[0024] In this embodiment, the foaming aid is stearic acid, the crosslinking accelerator is zinc diethyldithiocarbamate, the filler is calcium carbonate, and the anti-yellowing agent is V76P.
Embodiment 2
[0026] (1), take by weighing 55 parts of EPDM rubber, 33 parts of polyurethane resin, 4 parts of talc powder, 1.2 parts of angelica oil, 1.2 parts of paraffin, 3 parts of polyethylene glycol, join in the internal mixer, Mix at 120-130°C for 15-20 minutes, then add 2 parts of foaming aid, 1 part of cross-linking accelerator, 4 parts of flame retardant, 0.7 parts of anti-yellowing agent and 5 parts of filler in sequence, at 120-130°C Next, mix for 15-20 minutes to form a uniform mixture and set aside;
[0027] (2) Add the mixture prepared in step (1) into a three-roller machine, grind for 2 to 3 times, filter through a filter, vacuumize and defoam for 20 minutes to obtain the product.
[0028] In this embodiment, the foaming aid is polyethylene wax, the crosslinking accelerator is dithiodimorpholine, the filler is calcium carbonate, and the anti-yellowing agent is V76P.
Embodiment 3
[0030] (1), take by weighing 60 parts of EPDM rubber, 35 parts of polyurethane resin, 4 parts of talc powder, 1.4 parts of angelica oil, 1.4 parts of paraffin, 3 parts of polyethylene glycol, join in the internal mixer, Mix for 15-20min at 120-130°C, then add 3 parts of foaming aid, 2 parts of cross-linking accelerator, 6 parts of flame retardant, 1 part of anti-yellowing agent and 7 parts of filler in sequence, at 120-130°C Next, mix for 15-20 minutes to form a uniform mixture and set aside;
[0031] (2) Add the mixture prepared in step (1) into a three-roller machine, grind for 2 to 3 times, filter through a filter, vacuumize and defoam for 20 minutes to obtain the product.
[0032] In this embodiment, the foaming aid is calcium silicate, the crosslinking accelerator is tetramethylthiuram disulfide, the filler is expanded vermiculite, and the anti-yellowing agent is V76P.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com