Preparation method of polyhedral color decorative lightweight wall material

A light-weight wall and color technology, applied to chemical instruments and methods, household walls, and other household appliances, can solve the problems of poor thermal insulation performance and decorative performance, high manufacturing cost, etc., achieve good thermal insulation effect, reduce costs, and improve craftsmanship simple effect

Inactive Publication Date: 2015-01-28
SHANDONG UNIV OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, building materials generally use clay hollow bricks, cement hollow blocks and aerated concrete blocks, etc. These building materials have poor thermal insulation performance and decorative performance. When applied to interior and exterior walls, additional tiles or wallpapers are required, which is a high manufacturing cost. building decoration materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polyhedral color decorative lightweight wall material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] a. Preparation of colored decorative layer (1): After uniformly mixing the Yellow River silt and basalt with a weight ratio of 50:50 and 5% ceramic pigments by weight, they are melted at a temperature of 1350°C in a frit furnace. Yellow River silt frit particles with a particle size of 0.1mm;

[0018] b. Preparation of the transition layer (2): the Yellow River silt frit particles prepared in step a plus 5% by weight mullite were evenly mixed and ground until the particle size was 10 μm to make the transition layer raw material;

[0019] c. Preparation of the insulation layer (3): After uniformly mixing the Yellow River silt and basalt with a weight ratio of 50:50 plus 5% coal gangue by weight, the insulation layer raw material with a particle size of 0.1mm is sprayed and granulated;

[0020] d. Preparation of multi-faceted colored decorative light wall materials: first use the setter plate (4) left, right, front, back and bottom to form a cube setter mold with an upper...

Embodiment 2

[0023] a. Preparation of the colored decorative layer (1): After uniformly mixing the Yellow River silt and basalt with a weight ratio of 70:30 plus ceramic pigments with a weight percentage of 18%, melt treatment at a temperature of 1400°C in a frit furnace. Yellow River silt frit particles with a particle size of 1mm;

[0024] b. Preparation of the transition layer (2): the Yellow River silt frit particles prepared in step a plus 12% by weight of mullite were uniformly mixed and ground until the particle size was 25 μm to make the transition layer raw material;

[0025] c. Preparation of the insulation layer (3): After uniformly mixing the Yellow River silt and basalt with a weight ratio of 70:30 plus 13% coal gangue by weight, the insulation layer raw material with a particle size of 0.3mm is sprayed and granulated;

[0026] d. Preparation of multi-faceted colored decorative light wall materials: first use the setter plate (4) left, right, front, back and bottom to form a c...

Embodiment 3

[0029] a. The preparation of the colored decorative layer (1): uniformly mix the Yellow River silt and basalt with a weight ratio of 90:10 plus ceramic pigments with a weight percentage of 30%, and melt it in a frit furnace at a temperature of 1450°C. Yellow River silt frit particles with a particle size of 2mm;

[0030] b. Preparation of the transition layer (2): the Yellow River silt frit particles prepared in step a plus 20% by weight of mullite were uniformly mixed and ground until the particle size was 50 μm to make the transition layer raw material;

[0031] c. Preparation of the insulation layer (3): After uniformly mixing the Yellow River silt and basalt with a weight ratio of 90:10 plus 30% coal gangue by weight, the insulation layer raw material with a particle size of 0.6 mm is sprayed and granulated;

[0032] d. Preparation of multi-faceted colored decorative light wall materials: first use the setter plate (4) left, right, front, back and bottom to form a cube set...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of polyhedral color decorative lightweight wall material. The preparation method is characterized in that the polyhedral color decorative lightweight wall material is formed by a color decorative layer (1), a transition layer (2) and an insulating layer (3). The prepared polyhedral color decorative lightweight wall material adopts one-time firing, and the transition layer is added between the color decorative layer and insulating layer, the defects that the pore diameter is oversize and the bonding strength and the heat impact resistance are low caused by inconsistent material melting points of the color decorative layer and the insulating layer are effectively solved; the inner wall and outer wall decorative material in single-color, composite color, and various patterns are prepared by adding ceramic toner without adding extra decoration; the production process is simple, the cost is low, the building insulating effect is good, and the material is energy-saving, waterproof and environment-friendly; the produced polyhedral color decorative lightweight wall material has all-in-one function of decorating, insulating, heat insulating, sound insulating and shockproof.

Description

technical field [0001] The invention relates to a preparation method of a multi-faceted colorful decorative light wall material, which belongs to the technical field of ceramic preparation. Background technique [0002] Multi-faceted color decorative light wall material is a new type of light wall material integrating decoration and heat preservation. It is a new type of wall material with integrated functions of decoration, heat preservation, waterproof, heat insulation, sound insulation and shock resistance. At present, building materials generally use clay hollow bricks, cement hollow blocks and aerated concrete blocks, etc. These building materials have poor thermal insulation performance and decorative performance. When applied to interior and exterior walls, additional tiles or wallpapers are required, which is a high manufacturing cost. building decoration materials. Contents of the invention [0003] The purpose of the present invention is to provide a method for ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B19/04C04B30/00
CPCB32B19/04B32B2607/00C04B30/00
Inventor 唐竹兴
Owner SHANDONG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap