Black top paint with high blackness and blue phase, and preparation method thereof

A blue-phase black topcoat and high blackness technology, which is applied in the preparation of high-blackness blue-phase black topcoat and the field of high-blackness blue-phase black topcoat, can solve the problem of not being able to meet the requirements of performance and blackness Appearance requirements for high-end cars, problems affecting the performance of topcoats, etc., to achieve excellent matching, high fullness, and good hardness

Inactive Publication Date: 2015-01-28
ZHENGZHOU YUTONG BUS CO LTD
4 Cites 16 Cited by

AI-Extracted Technical Summary

Problems solved by technology

However, ordinary polyurethane black topcoat has problems of insufficient blackness and reddish-brown phase, which cannot meet the appearance requirements of high-end cars; if the blackness requirement is met by increasing...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Abstract

The invention discloses a black top paint with high blackness and blue phase, and a preparation method thereof. The top paint is composed of the following components by weight: 55-75 parts of a hydroxyl acrylic resin, 10-15 parts of a hydroxyl polyester resin, 0.25-0.55 parts of a leveling agent, 1.5-4.0 parts of a light stabilizer, 2.0-3.0 parts of high coloring carbon black, 2.0-3.0 parts of a wetting dispersant, 0.2-0.4 part of a synergistic dispersant, 0.03-0.05 part of a catalyst and 12-16 parts of a solvent. The black top paint with high blackness and blue phase is compounded by the hydroxyl acrylic resin, the hydroxyl polyester resin and a plurality of auxiliary agents, and has the advantages of excellent overcoatability, good leveling property, good weather resistance, good hardness and good scratch resistance. Compared with conventional black top paint, the black top paint provided by the invention has high blackness, high blue phase, high glossiness, high distinctness and high fullness, and can meet requirements for high-grade black top paint by coating and repairing in car and automobile industries.

Application Domain

Technology Topic

Examples

  • Experimental program(6)
  • Comparison scheme(6)
  • Effect test(1)

Example Embodiment

[0037] Example 1
[0038] The high-blackness blue phase black topcoat of this embodiment is mainly composed of the following components by weight: 50 parts of high hydroxyl value hydroxy acrylic resin, 10 parts of medium hydroxyl value hydroxy acrylic resin, and 15 parts of hydroxy polyester resin , Acrylic leveling agent 0.3 parts, silicone leveling agent 0.1 parts, ultraviolet light absorber 3.0 parts, hindered amine light stabilizer 1.0 part, high pigment carbon black 2.5 parts, wetting and dispersing agent 2.5 parts, synergistic dispersing agent 0.3 parts, 0.04 parts of organotin catalyst, 8 parts of propylene glycol methyl ether acetate, 2 parts of butyl acetate, 3.26 parts of xylene, and 2 parts of mixed dimethyl nylate.
[0039] Wherein, the hydroxyl value of the high hydroxyl value hydroxy acrylic resin is 146mgKOH/g; the solid content is 80% (solvent is n-butyl acetate), the acid value is 11.0mgKOH/g, and the viscosity is 6000-9000cps/25°C. The hydroxyl value of the hydroxy acrylic resin with medium hydroxyl value is 100mgKOH/g; the solid content is 75% (solvent is n-butyl acetate), the acid value is 8.0mgKOH/g, and the viscosity is 4000-8000cps/25°C. The hydroxyl value of the hydroxyl polyester resin is 142 mgKOH/g; the solid content is 85% (solvent is n-butyl acetate), and the viscosity is 2000-3000 cps/25°C. The particle size of the high pigment carbon black is less than or equal to 5 nm (FW200 from Degussa).
[0040] The acrylic leveling agent is BYK358N (commercially available product, BYK Chemie, Germany); the silicone leveling agent is polyether modified polydimethylsiloxane; the ultraviolet light absorber is TINUVIN1130 (Commercial product, BASF (Ciba)); The hindered amine light stabilizer is YINUVIN292 (commercial product, BASF (Ciba)); The wetting and dispersing agent is BYK2000 (Commercial product, Germany Gram Chemical Company); the synergistic dispersant is BYK 2100 (commercial product, BYK Chemie, Germany); the organotin catalyst is T-12 catalyst (commercial product, Air Chemical Company).
[0041] The preparation method of the high-blackness blue phase black topcoat of this embodiment includes the following steps:
[0042] 1) Mix 8 parts by weight of propylene glycol methyl ether acetate, 1.6 parts by weight of butyl acetate, 2.5 parts by weight of wetting and dispersing agent, 2.5 parts by weight of high-pigment carbon black, and 0.3 parts by weight of synergistic dispersant, and stir at 500r/min After 5 minutes, add 50 parts by weight of hydroxy acrylic resin with high hydroxyl value, stir for 10 minutes at 500r/min and mix uniformly. After sealing and standing for 4 hours, place it in a sand mill for grinding to obtain mixture A and mixture A. Degree ≤10μm;
[0043] 2) Mix 0.04 parts by weight of organotin catalyst and 0.4 parts by weight of butyl acetate uniformly to obtain a mixed catalyst; take 10 parts by weight of hydroxy acrylic resin with medium hydroxyl value, 15 parts by weight of hydroxy polyester resin, and acrylic leveling agent 0.3 parts by weight, 0.1 parts by weight of silicone leveling agent, 3.0 parts by weight of ultraviolet light absorber, 1.0 part by weight of hindered amine light stabilizer and mixed catalyst, are added to the mixture A obtained in step 1) in sequence, and under the condition of 800r/min Stir for 20min and mix evenly to obtain mixture B;
[0044] 3) Take the mixture B obtained in step 2), add the remaining solvent of the formula (3.26 parts by weight of xylene, 2 parts by weight of mixed dimethyl nylonate), stir at 600r/min for 20 minutes and mix well, then use a 10 mesh sieve Net filter, that is.
[0045] The high blackness blue phase black topcoat of this embodiment is mixed with the curing agent at a ratio of 0.95:1 molar ratio of the hydroxyl groups of all resins in the black topcoat to the isocyanate groups in the curing agent during use. The curing agent is a mixture of isocyanate and mixed solvent B in a volume ratio of 55:45. The mixed solvent B is a mixture of four solvents, butyl acetate, xylene, trimethylbenzene, and mixed dimethyl nylate.

Example Embodiment

[0046] Example 2
[0047] The high blackness blue phase black topcoat of this embodiment is mainly composed of the following components by weight: 60 parts of high hydroxyl value hydroxy acrylic resin, 8 parts of medium hydroxyl value hydroxy acrylic resin, and 10 parts of hydroxy polyester resin , 0.2 parts of acrylic leveling agent, 0.05 parts of silicone leveling agent, 2.0 parts of ultraviolet light absorber, 0.7 parts of hindered amine light stabilizer, 2.5 parts of high pigment carbon black, 2.5 parts of wetting and dispersing agent, synergistic dispersing agent 0.3 parts, 0.04 parts of organotin catalyst, 7 parts of propylene glycol methyl ether acetate, 2 parts of butyl acetate, 2.71 parts of xylene, 2 parts of mixed dimethyl nylonate.
[0048] Wherein, the hydroxyl value of the high hydroxyl value hydroxy acrylic resin is 142 mgKOH/g; the solid content is 75% (solvent is n-butyl acetate), the acid value is 13.0 mgKOH/g, and the viscosity is 6000-8000cps/25°C. The hydroxyl value of the hydroxy acrylic resin with medium hydroxyl value is 106 mgKOH/g; the solid content is 70% (solvent is n-butyl acetate), the acid value is 9.0 mgKOH/g, and the viscosity is 4000-6000cps/25°C. The hydroxyl value of the hydroxyl polyester resin is 154 mgKOH/g; the solid content is 80% (the solvent is n-butyl acetate), and the viscosity is 2000-3000 cps/25°C. The particle size of the high pigment carbon black is less than or equal to 5 nm (FW200 from Degussa).
[0049] The acrylic leveling agent is BYK358N (commercially available product, BYK Chemie, Germany); the silicone leveling agent is polyester-modified polydimethylsiloxane; the ultraviolet light absorber is TINUVIN1130 (Commercial product, BASF (Ciba)); The hindered amine light stabilizer is YINUVIN292 (commercial product, BASF (Ciba)); The wetting and dispersing agent is BYK2000 (Commercial product, Germany Gram Chemical Company); the synergistic dispersant is BYK 2100 (commercial product, BYK Chemie, Germany); the organotin catalyst is T-12 catalyst (commercial product, Air Chemical Company).
[0050] The preparation method of the high-blackness blue phase black topcoat of this embodiment includes the following steps:
[0051] 1) Mix 7 parts by weight of propylene glycol methyl ether acetate, 1.5 parts by weight of butyl acetate, 2.5 parts by weight of wetting and dispersing agent, 2.5 parts by weight of high-pigment carbon black, and 0.3 parts by weight of synergistic dispersant, and stir under 400r/min After 10 minutes, add 60 parts by weight of hydroxy acrylic resin with high hydroxyl value, stir for 10 minutes at 400r/min and mix uniformly. After sealing and standing for 4 hours, place it in a sand mill for grinding to obtain mixture A and mixture A. Degree ≤10μm;
[0052] 2) Mix 0.04 parts by weight of organotin catalyst and 0.5 parts by weight of butyl acetate to obtain a mixed catalyst; take 8 parts by weight of hydroxyl acrylic resin, 10 parts by weight of hydroxyl polyester resin, and acrylic leveling agent 0.2 parts by weight, 0.05 parts by weight of organosilicon leveling agent, 2.0 parts by weight of ultraviolet light absorber, 0.7 parts by weight of hindered amine light stabilizer and mixed catalyst are added to the mixture A obtained in step 1) in sequence, and under 700r/min Stir for 30min and mix evenly to obtain mixture B;
[0053] 3) Take the mixture B obtained in step 2), add the remaining solvent of the formula (2.71 parts by weight of xylene, 2 parts by weight of mixed dimethyl nylate), stir for 10 minutes at 800r/min and mix well, then use a 10 mesh sieve Net filter, that is.
[0054] The high blackness blue phase black topcoat of this embodiment is mixed with the curing agent at a ratio of 1:1 in molar ratio of the hydroxyl groups of all resins in the black topcoat to the isocyanate groups in the curing agent. The curing agent is a mixture of isocyanate and mixed solvent B in a volume ratio of 55:45. The mixed solvent B is a mixture of four solvents, butyl acetate, xylene, trimethylbenzene, and mixed dimethyl nylate.

Example Embodiment

[0055] Example 3
[0056] The high blackness blue phase black topcoat of this embodiment is mainly composed of the following components by weight: 65 parts of high hydroxyl value hydroxy acrylic resin, 5 parts of medium hydroxyl value hydroxy acrylic resin, and 10 parts of hydroxy polyester resin , 0.4 part of acrylic leveling agent, 0.15 part of silicone leveling agent, 1.0 part of ultraviolet light absorber, 0.5 part of hindered amine light stabilizer, 2.5 part of high pigment carbon black, 2.5 part of wetting and dispersing agent, synergistic dispersing agent 0.3 parts, 0.04 parts of organotin catalyst, 6 parts of propylene glycol methyl ether acetate, 3.5 parts of butyl acetate, 1.61 parts of xylene, 1.5 parts of mixed dimethyl nylate.
[0057] Wherein, the hydroxyl value of the high hydroxyl value hydroxy acrylic resin is 145mgKOH/g; the solid content is 80% (solvent is n-butyl acetate), the acid value is 12.0mgKOH/g, and the viscosity is 6000-10000cps/25°C. The hydroxyl value of the hydroxy acrylic resin with medium hydroxyl value is 100mgKOH/g; the solid content is 70% (solvent is n-butyl acetate), the acid value is 11.0mgKOH/g, and the viscosity is 7000-9000cps/25°C. The hydroxyl value of the hydroxyl polyester resin is 152 mgKOH/g; the solid content is 100%, and the viscosity is 2000-4000 cps/25°C. The particle size of the high pigment carbon black is less than or equal to 5 nm (FW200 from Degussa).
[0058] The acrylic leveling agent is BYK358N (commercially available product, BYK Chemie, Germany); the silicone leveling agent is polyether modified polydimethylsiloxane; the ultraviolet light absorber is TINUVIN1130 (Commercial product, BASF (Ciba)); The hindered amine light stabilizer is YINUVIN292 (commercial product, BASF (Ciba)); The wetting and dispersing agent is BYK2000 (Commercial product, Germany Gram Chemical Company); the synergistic dispersant is BYK 2100 (commercial product, BYK Chemie, Germany); the organotin catalyst is T-12 catalyst (commercial product, Air Chemical Company).
[0059] The preparation method of the high-blackness blue phase black topcoat of this embodiment includes the following steps:
[0060] 1) Mix 6 parts by weight of propylene glycol methyl ether acetate, 3 parts by weight of butyl acetate, 2.5 parts by weight of wetting and dispersing agent, 2.5 parts by weight of high-pigment carbon black, and 0.3 parts by weight of synergistic dispersant, and stir at 600r/min After 5 minutes, add 65 parts by weight of hydroxy acrylic resin with high hydroxyl value, stir for 7 minutes at 600r/min and mix uniformly. After sealing and standing for 10 hours, place it in a sand mill for grinding to obtain mixture A and mixture A. Degree ≤10μm;
[0061] 2) Mix 0.04 parts by weight of organotin catalyst and 0.5 parts by weight of butyl acetate to obtain a mixed catalyst; take 5 parts by weight of hydroxy acrylic resin with medium hydroxyl value, 10 parts by weight of hydroxy polyester resin, and acrylic leveling agent 0.4 parts by weight, 0.15 parts by weight of silicone leveling agent, 1.0 parts by weight of ultraviolet light absorber, 0.5 parts by weight of hindered amine light stabilizer and mixed catalyst, are added to the mixture A obtained in step 1) in sequence, and under the condition of 1000r/min Stir for 20min and mix evenly to obtain mixture B;
[0062] 3) Take the mixture B obtained in step 2), add the remaining solvent of the formula (1.61 parts by weight of xylene, 1.5 parts by weight of mixed dimethyl nylate), stir at 500r/min for 20 minutes and mix well, then use a 10 mesh sieve Net filter, that is.
[0063] The high blackness blue phase black topcoat of this embodiment is mixed with the curing agent at a ratio of 0.97:1 molar ratio of the hydroxyl groups of all resins in the black topcoat to the isocyanate groups in the curing agent during use. The curing agent is a mixture of isocyanate and mixed solvent B in a volume ratio of 55:45. The mixed solvent B is a mixture of four solvents, butyl acetate, xylene, trimethylbenzene, and mixed dimethyl nylate.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Hydroxyl value146.0mgKOH/g
Acid value11.0mgKOH/g
Hydroxyl value100.0mgKOH/g
tensileMPa
Particle sizePa
strength10

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Similar technology patents

Tool slide

Owner:VOESTALPINE GIESSEREI LINZ

Condensed cyclic compound and organic light-emitting device including the same

InactiveUS20150263290A1Good matchingImprove color changeOrganic chemistrySolid-state devicesCyclic compoundPhotochemistry
Owner:SAMSUNG DISPLAY CO LTD

Plastic part undercoat

InactiveCN103819979AGood matchingReduce waste and hassleCoatingsSolventChemistry
Owner:ANHUI LAND GRP

Classification and recommendation of technical efficacy words

  • Good matching
  • Good leveling

Dual feedback control system for implantable hearing instrument

InactiveUS20070167671A1Reduce responseGood matchingImplantable hearing aidsElectrostatic transducersMicrophoneEngineering
Owner:COCHLEAR LIMITED

Method for matching an object model to a three-dimensional point cloud

InactiveUS20100310154A1Improve convergence propertyGood matchingImage analysisDetails involving 3D image dataObject modelPoint cloud
Owner:PILZ (COMPANY)

Aperture-coupled antenna

Owner:FRAUNHOFER GESELLSCHAFT ZUR FOERDERUNG DER ANGEWANDTEN FORSCHUNG EV

Personalised channel

ActiveUS20170339444A1Good matchingSelective content distributionPersonalizationContent delivery
Owner:PRJ HLDG CO LLC

Audio Communication System, An Audio Transmitter and An Audio Receiver

InactiveUS20130268278A1Improve linearityGood matchingSpeech analysisVolume compression/expansion in untuned/low-frequency amplifiersIntegrated circuitDigital audio signals
Owner:KTMICRO ELECTRONICS

Water-borne UV paint and preparation method thereof

ActiveCN105331279AHigh water and alcohol resistanceGood levelingAnti-corrosive paintsPolyurea/polyurethane coatingsPhotoinitiatorFluorocarbon
Owner:SHENYANG SHUNFENG NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products