Drawer slide assembly and method of manufacturing a composite assembly material
A manufacturing method and technology of slide rails, which are applied to drawers, furniture parts, household appliances, etc., can solve problems such as inability to slide open and close, wear of steel ball components, and lack of good load capacity, so as to reduce production costs and have good wear resistance The effect of resistance and joint strength
Inactive Publication Date: 2015-02-11
METAL INDS RES & DEV CENT
View PDF8 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
The known drawer slides are made of bent steel plates. Although they have a good load-bearing capacity, the weight of the drawer slides is too heavy due to the steel plate. In addition, the steel plate is replaced with an aluminum plate, although the weight of the drawer slides can be reduced. And achieve light weight, but it does not have a good load capacity
[0003] In addition to the above-mentioned problems, the known drawer components are connected inside the table body by drawer slide rails, so that the combined drawer table body forms a sliding opening and closing function that can be pulled out or pushed in. The sliding opening and closing function that can be pulled out or pushed in inside the body must be installed with a steel ball assembly as a sliding bearing. Due to the weight of the drawer itself and the fact that the drawer is a component that is frequently operated, the steel ball assembly is used as a sliding bearing. Continuous stress, uneven force will cause rapid wear of individual steel ball components or some steel ball components, or cause steel ball components to wear on the drawer slide rails, making it difficult for the drawer to slide open and close, or even unable to slide open and close. close
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0045] In order to make the structural features of the present invention and the achieved effects have a further understanding and recognition, preferred embodiments and detailed descriptions are specially used, which are described as follows:
[0046] The conventional drawer slides are made of steel plates, which can achieve high load capacity, but cannot achieve the purpose of light weight. If only aluminum plates are used, the purpose of light weight can be achieved, but the purpose of high load capacity cannot be achieved. In view of the above problems, the present invention provides a method for manufacturing a drawer slide rail and its composite assembly material. The drawer slide rail is assembled from a plurality of composite assembly materials, and each composite assembly material is composed of two lightweight materials. Drawer slides take into account the needs of high load capacity and light weight.
[0047] see figure 1 , which is a schematic diagram of the drawe...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The present invention provides a drawer slide assembly and a method of manufacturing a composite assembly material. Drawer slides through a complex combination of the present invention is made of composite material assembled. The composite assembly material is composed of two matierals, wherein the two kinds of materials are light metal with a high load capacity and the light metal with high wear resistance, and so make the assembly of these complex materials assembled from lightweight drawer slides not only meet, but also both a good load capacity, wear resistance and bonding strength.
Description
technical field [0001] The invention relates to a method for manufacturing a drawer slide rail and its assembly material, in particular to a drawer slide rail and a method for manufacturing the composite assembly material combined by using composite assembly materials. Background technique [0002] At present, sliding parts (such as slide rails) are used in furniture, kitchen utensils, storage, tool carts, molds and other product fields. The known drawer slides are made of bent steel plates. Although they have a good load-bearing capacity, the weight of the drawer slides is too heavy due to the steel plate. In addition, the steel plate is replaced with an aluminum plate, although the weight of the drawer slides can be reduced. And achieve lightweight, but it does not have a good load capacity. [0003] In addition to the above-mentioned problems, the known drawer components are connected inside the table body by drawer slide rails, so that the combined drawer table body for...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine