Composition for texture coating of automobile parts and automobile parts comprising same

A technology for automotive parts and texture coatings, applied in vehicle parts, polyester coatings, polycarbonate coatings, etc., can solve the problem that texture coatings cannot feel soft, and achieve excellent reliability, improve commerciality, and scratch resistance. Excellent effect of sex

Active Publication Date: 2017-06-16
HYUNDAI MOBIS CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with the improved sensibility quality, the two-dimensional texture embodied at present is only an improved elastic state compared with the time when the texture paint was introduced, and the characteristics of the texture paint cannot feel the soft feel (softfeel)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composition for texture coating of automobile parts and automobile parts comprising same
  • Composition for texture coating of automobile parts and automobile parts comprising same
  • Composition for texture coating of automobile parts and automobile parts comprising same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] The resin, microspheres, pigments, additives, and solvents were mixed according to the contents described in the following Table 1 (unit: parts by weight) to prepare a texture coating composition. The prepared composition was coated on a center trim, which is a plastic part for automotive interiors, which is injection-coated with a PC / ABS material, and dried at 95° C. for 40 minutes to form a coating film layer.

[0056] Such as Figure 4 As shown, it can be confirmed that fluffing is completed, the surface gloss is lost due to the drying of the coating film, and a part of the swollen microspheres is exposed to the surface of the coating film due to the expansion of the microspheres, thereby achieving a surface texture. In addition, plastic parts were attached to the cockpit module (Cockpit Module) to conduct a heat resistance cycle test of the module. The test method is to measure the distance and step difference between the center decoration and the surrounding plast...

Embodiment 2

[0058] In Example 2, except having changed each component as shown in Table 1 below, the coating film was formed by the same method.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
oil absorptionaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a composition for texture coating of automobile parts and an automobile part comprising a coating film formed from the composition. The composition for texture coating of automobile parts comprises: 20 to 50% by weight of a thermosetting resin; 1 to 10% by weight 3 to 20% by weight of pigments; 1 to 20% by weight of additives; and the remaining amount of solvent; and 5 to 20% by weight of hardener can be added subsequently.

Description

technical field [0001] The present invention relates to a composition for texture coating of automobile parts and an automobile part comprising the composition. Background technique [0002] Currently, soft resins and surface texture modifiers are used in texture-forming paints used for automotive interior / exterior parts. Texture-forming paints are applied to automotive parts materials to express a certain texture. [0003] Texture paints containing polyester resin and silicon as well as urethane or acrylic beads have high softness due to the use of polyester alone, which can maximize the texture perceived by consumers, but poly The characteristic of ester is that it has low weather resistance, so if it is exposed to sunlight for a long time, it may cause discoloration, cracks and other defects in the coating film. Furthermore, although the paint containing polyester and polycarbonate diol has better physical properties than a composition containing polyester alone, it is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/28C09D7/12
CPCC09D7/40C09D5/28C09D127/06C09D133/00C09D167/00C09D169/00C08L2203/14C09D175/04C08G18/44C08K7/22B60R11/00C09D201/00
Inventor 吴祐政河禹镇金铉敦全勇房世润
Owner HYUNDAI MOBIS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap