Pervious concrete and construction method thereof

A technology of permeable concrete and construction method, which is applied to coagulation pavement, roads, buildings and other directions laid on site, can solve the problems of poor water permeability and low strength of permeable concrete, and achieves enhanced wrapping force, improved frost resistance, and improved durability. sexual effect

Active Publication Date: 2015-03-11
TIANYUAN CONSTR GROUP
View PDF3 Cites 53 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides a permeable concrete and its construction method to solve the technical problems of low strength and poor water permeability of the existing permeable concrete

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Embodiment 1, this permeable concrete, its raw material ratio by weight percentage is as follows:

[0048] Cement 15.9%;

[0049] River sand 15.6%;

[0050] Pebbles 59.6%;

[0051] Water 3.9%;

[0052] Admixture 5.0%;

[0053] The raw material proportioning of described admixture is as follows by weight percentage:

[0054] Ultrafine mineral powder 45%;

[0055] Heavy calcium 20%;

[0056] Gypsum powder 15%;

[0057] Polypropylene fiber 5%;

[0058] Polycarboxylate superplasticizer 7.8%;

[0059] Rubber powder 4.2%;

[0060] Pigment 3%.

Embodiment 2

[0061] Embodiment 2, this permeable concrete, its raw material proportioning by weight percentage is as follows:

[0062] Cement 13.1%;

[0063] River sand 12.7%;

[0064] Stone 66.0%;

[0065] Water 3.7%;

[0066]Admixture 4.5%;

[0067] The raw material proportioning of described admixture is as follows by weight percentage:

[0068] Ultrafine mineral powder 47%;

[0069] Heavy calcium 15%;

[0070] Gypsum powder 20%;

[0071] Polypropylene fiber 3%;

[0072] Polycarboxylate superplasticizer 5%;

[0073] Rubber powder 8%;

[0074] Pigment 2%.

Embodiment 3

[0075] Embodiment 3, this permeable concrete, its raw material proportioning by weight percentage is as follows:

[0076] Cement 14.5%;

[0077] River sand 13.8%;

[0078] Pebbles 63.1%;

[0079] Water 3.8%;

[0080] Admixture 4.8%;

[0081] The raw material proportioning of described admixture is as follows by weight percentage:

[0082] Ultrafine mineral powder 46%;

[0083] Heavy calcium 16.3%;

[0084] Gypsum powder 16.3%;

[0085] Polypropylene fiber 4%;

[0086] Polycarboxylate superplasticizer 7%;

[0087] Rubber powder 6.4%;

[0088] Pigment 4%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses pervious concrete and a construction method thereof. The pervious concrete comprises the following raw materials in percentage by weight: 13.1-15.9% of cement, 12.7-15.6% of river sand, 59.6-66.0% of stones, 3.7-3.9% of water and 4.5-5.0% of admixtures, wherein the admixtures comprise the following raw materials in percentage by weight: 45-50% of ultrafine mineral powder, 15-20% of heavy calcium carbonate, 15-20% of gypsum powder, 3-5% of polypropylene fiber, 5-10% of a polycarboxylate water reducing agent, 4.2-8.4% of adhesive powder and 2-5% of a pigment. The pervious concrete provided by the invention has relatively high water permeability, strength and durability; after the pervious concrete is applied to a practical engineering, the pervious concrete can greatly improve the problem of poor drainage of a hardened road surface, so that the development of the pervious concrete can be promoted.

Description

technical field [0001] The invention relates to a concrete pavement material and a construction method thereof. Background technique [0002] The surface of the modern city has been covered by reinforced concrete buildings and impermeable roads. Compared with natural soil pavement, ordinary concrete pavement lacks breathability, heat absorption and water permeability, which brings a series of environmental problems. At present, ordinary concrete has extremely poor water permeability, which puts great pressure on the drainage system of the road surface. The rainwater that cannot penetrate the ground can only be discharged into the river through the drainage system, which brings a great burden to urban rivers. [0003] Permeable concrete is a kind of concrete with continuous pores prepared through strict material research and optimization, and through a specific preparation process. Pervious concrete not only has a certain strength, but also has a certain water permeability....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B28/04C04B16/06C04B14/06E01C7/14
Inventor 卢忠淳郭玉顺梁荣建景帅帅田新鹏
Owner TIANYUAN CONSTR GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap