High-ultraviolet-reflectivity reflective insulation coating and preparation method thereof

A reflective thermal insulation coating, reflectivity technology, applied in reflective/signal coatings, antifouling/underwater coatings, coatings, etc., can solve the problem of shortening the service life of the coating, accelerating the aging of the coating, and changing the coating temperature. problems, to avoid accelerated aging, strong adhesion, good heat insulation and weather resistance

Inactive Publication Date: 2015-03-25
SHENZHEN JIADA HIGH TECH IND DEV
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Judging from the disclosed prior art content, current anti-ultraviolet light coatings generally use ultraviolet absorbers to absorb ultraviolet light, which is easy to accelerate the aging of the coating, and causes a large change in coating temperature, thereby shortening the coating time. layer lifetime

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-ultraviolet-reflectivity reflective insulation coating and preparation method thereof
  • High-ultraviolet-reflectivity reflective insulation coating and preparation method thereof
  • High-ultraviolet-reflectivity reflective insulation coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] Correspondingly, an embodiment of the present invention also provides a preparation method of the above-mentioned high ultraviolet reflectivity reflective heat-insulating coating. This preparation method comprises the steps:

[0040] Step S01: Obtain each component separately according to the composition and content of the high ultraviolet reflectance reflective heat-insulating coating of the present invention;

[0041] Step S02: Mixing the weighed components.

[0042] Specifically, in the above step S01, the components of the high ultraviolet reflectance reflective heat-insulating paint are as described above, and will not be repeated here to save space.

[0043] The mixing process in the above step S02 is to make the weighed components mix uniformly to form a stable coating system.

[0044] In order to improve the dispersibility of each component and improve the stability of the high-ultraviolet reflectance reflective heat-insulating coating, in one embodiment, when...

Embodiment 1

[0048] The invention discloses a high ultraviolet reflectivity reflective heat-insulating paint component formula and a preparation method thereof. The reflective heat-insulating coating with high ultraviolet reflectivity contains the following components by weight:

[0049]

[0050]

[0051] Its preparation method comprises the following steps:

[0052] S11. Obtain each component according to the composition and content of the high ultraviolet reflectance reflective heat insulation coating described above;

[0053] S12. Add the components weighed in step S11 into water in order according to the following order for mixing treatment, so that the components are mixed evenly: bactericide, wetting agent, dispersant, antifreeze agent, defoamer, cellulose , Alkaline pH adjuster, titanium dioxide, filler, UV reflective slurry, emulsion, film-forming aid, mildew-proof additive, thickener.

Embodiment 2

[0055] The invention discloses a high ultraviolet reflectivity reflective heat-insulating paint component formula and a preparation method thereof. The reflective heat-insulating coating with high ultraviolet reflectivity contains the following components by weight:

[0056]

[0057]

[0058] Its preparation method comprises the following steps:

[0059] S21. Obtain each component according to the composition and content of the high ultraviolet reflectance reflective heat-insulating coating;

[0060] S22. Add the components weighed in step S21 into water in the following order for mixing treatment, so that the components are mixed evenly: bactericide, wetting agent, dispersant, antifreeze agent, defoamer, cellulose , Alkaline pH adjuster, titanium dioxide, filler, UV reflective slurry, emulsion, film-forming aid, mildew-proof additive, thickener.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a high-ultraviolet-reflectivity reflective insulation coating and a preparation method of the high-ultraviolet-reflectivity reflective insulation coating. The high-ultraviolet-reflectivity reflective insulation coating comprises, by weight, 20.0-25.0 parts of water, 1.0-3.0 parts of antifreezing agents, 0.1-0.5 part of sterilizing agent, 0.3-1.0 part of dispersing agent, 0.1-0.5 part of wetting agent, 0.1-0.5 part of antifoaming agent, 0.1-0.5 part of cellulose, 0.1-0.5 part of alkaline pH regulator, 10.0-20.0 parts of titanium dioxide, 15.0-30.0 parts of fillers, 10.0-20.0 parts of ultraviolet reflection pulp, 20.0-30.0 parts of emulsion, 1.0-3.0 parts of coalescing agents, 0.1-1 part of mildew preventive and 0.2-1.0 part of thickening agent. The high-ultraviolet-reflectivity reflective insulation coating is high in ultraviolet reflectivity, good in heat insulation property and weather fastness, high in adhesive force, good in antifreezing function and high in strength, saves energy and is environmentally friendly.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a high ultraviolet reflectance reflective heat-insulating coating and a preparation method thereof. Background technique [0002] In recent years, many reflective heat-insulating coatings have appeared on the market. According to relevant testing standards, such as JC / T 235-2014, the reflectivity in the wavelength range of 300-2500nm is mainly detected. In this wavelength range, the near-infrared region (780 -2500m) energy accounted for 50%, visible light region (400-780nm) energy accounted for 45%, ultraviolet light region (300-400nm) energy accounted for 5%; according to observation, ordinary reflective heat insulation coatings have extremely low reflectivity in ultraviolet light region , while the general reflective heat insulation coatings on the market only one-sidedly increase the reflectivity of its near-infrared light region, while ignoring the influence of ultraviolet light regio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D133/04C09D5/14C09D5/33C09D7/12
CPCC08K2003/2241C09D125/14C08K2201/003C09D5/004C09D5/14C09D7/20C09D7/61C09D7/62C09D7/63C09D133/00C09D133/04C08L1/284C08K13/06C08K9/00C08K2003/3045C08K2003/265C08K5/053
Inventor 伍文雍关有俊熊永强
Owner SHENZHEN JIADA HIGH TECH IND DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap