Method for preparing cuprous oxide microcrystals by taking carbon quantum dots as reducing agent

A carbon quantum dot, cuprous oxide technology, applied in copper oxide/copper hydroxide and other directions, can solve the problem of high purity

Inactive Publication Date: 2015-04-01
JIANGSU UNIV
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] So far, no one has been found to use carbon quantum dots prepared from green grass as a reducing agent to prepare cuprous oxide b

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing cuprous oxide microcrystals by taking carbon quantum dots as reducing agent
  • Method for preparing cuprous oxide microcrystals by taking carbon quantum dots as reducing agent
  • Method for preparing cuprous oxide microcrystals by taking carbon quantum dots as reducing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Example 1 Preparation of carbon quantum dots

[0022] The preparation of carbon quantum dots adopts the hydrothermal synthesis method: weigh 4 g of green grass in a 50 mL polytetrafluoroethylene reactor, then add 20 mL of distilled water, and then place it at 180 o C was kept in a drying oven for 4 h, and the reaction kettle was taken out to cool down to room temperature naturally, and the solid impurities were filtered out to obtain a carbon quantum dot solution.

Embodiment 2

[0023] Example 2 Preparation of graded spherical cuprous oxide

[0024] 255 mg of Cu(NO 3 ) 3H 2 Dissolve O in 10 mL of distilled water, then add 10 mL of NaOH solution (1 mol / L), add 600 mg of polyethylene glycol 2000 and 8 mL of carbon quantum solution prepared after the dropwise addition, and mix the solution at 1500 r / min Stir for 10 min, then transfer to a 50 mL polytetrafluoroethylene reactor, put in an oven, 180 o C for 8 h, take out the reactor and cool to room temperature naturally; wash the obtained samples with deionized water and absolute ethanol for 3 times, centrifuge and place in a vacuum oven for 60 o C drying for 8 h.

Embodiment 3

[0025] Example 3 Preparation of spherical cuprous oxide

[0026] 255 mg of CuCl 2 2H 2 Dissolve O in 10 mL of distilled water, then add 20 mL of NaOH solution (1 mol / L), add 800 mg of polyethylene glycol 2000 and 8 mL of carbon quantum solution prepared after the dropwise addition, and mix the solution at 100 r / min Stir for 150 min, then transfer to a 50 mL polytetrafluoroethylene reactor, put in an oven, 200 o C for 6 h, take out the reactor and cool to room temperature naturally; wash the obtained samples with deionized water and absolute ethanol for 3 times, centrifuge and place in a vacuum oven for 60 o C drying for 8 h.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to cuprous oxide and provides a method for synthesizing cuprous oxide microcrystals with special appearance by taking carbon quantum dots as a reducing agent. The carbon quantum dots are prepared from grass as a raw material through a hydrothermal method. According to the synthesis of cuprous oxide, the carbon quantum dots are taken as the reducing agent, a copper salt is taken as a copper source, and in the presence of a surfactant and a NaOH solution, the cuprous oxide microcrystals with local special appearance are obtained by reaction through a hydrothermal method, then water washing, alcohol washing and centrifugal drying. Cuprous oxide prepared by the method is in micrometer size, the size and appearance distribution is uniform, and the purity is high.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Owner JIANGSU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2023 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap