A nickel-cobalt alloy electroplating solution and an electroplating method

A technology of cobalt alloy and electroplating solution, applied in the field of electroplating solution, can solve the problems of low hardness of nickel coating, difficulty in meeting multi-directional requirements, poor wear resistance, etc.

Inactive Publication Date: 2015-04-15
WUXI HUAYE IRON & STEEL
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the nickel coating of a single metal has low hardness and poor wear resistance, which makes it difficult to meet the multi-faceted needs of the industrial field for materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A nickel-cobalt alloy electroplating solution and an electroplating method
  • A nickel-cobalt alloy electroplating solution and an electroplating method
  • A nickel-cobalt alloy electroplating solution and an electroplating method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The formula of nickel-cobalt alloy electroplating solution is as follows:

[0020] Table 1-1 Plating solution formula

[0021]

[0022] Table 1-2 brightener formula

[0023]

Embodiment 2

[0025] The formula of nickel-cobalt alloy electroplating solution is as follows:

[0026] Table 2-1 Plating solution formula

[0027]

[0028] Table 2-2 brightener formula

[0029]

Embodiment 3

[0031] The formula of nickel-cobalt alloy electroplating solution is as follows:

[0032] Table 3-1 Plating solution formula

[0033]

[0034] Table 3-2 brightener formula

[0035]

[0036]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A nickel-cobalt alloy electroplating solution and an electroplating method are disclosed. The electroplating solution comprises 260-300 g / L of nickel sulfate, 40-60 g / L of nickel chloride, 25-40 g / L of boric acid, 5-15 g / L of cobaltous sulfate, 0.5-2 mL / L of a brightener and 0.05-0.2 g / L of an emulsifier, wherein the brightener is a mixture of a BE nickel plating brightener, propynol ethoxylate, propargyl sulfonate and saccharin. Divalent cobalt ions and divalent nickel ions in the electroplating solution are co-deposited on the surface of a workpiece to be plated in a cathode. The cobalt element introduced into a plating reduces porosity of the plating and enhances hardness, wear resistance and brightness of the plating.

Description

technical field [0001] The invention relates to the technical field of electroplating solutions, in particular to a nickel-cobalt alloy electroplating solution. Background technique [0002] Electroplating is a metal electrodeposition method, which refers to the process of reducing the metal ions in the electrolyte under the action of direct current and depositing them on the surface of the workpiece to form a metal coating with certain properties. Compared with other surface treatment technologies such as coating and vapor deposition, electroplating has the advantages of fast deposition speed, uniform coating thickness, and thin coating, so it has become a common way of metal corrosion protection today. [0003] Nickel has excellent physical, chemical and mechanical properties. Nickel-coated film materials prepared by electroplating have been widely used in ten lamps, vehicles, batteries, printing and other industrial fields, playing an important role in the protection and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C25D3/56
CPCC25D3/562
Inventor 张明
Owner WUXI HUAYE IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap