Synthesis method of polymethacrylate pour point depressant
A technology of polymethacrylate and methacrylic acid, which is applied in the field of lubricating oil, can solve the problems of high freezing point of lubricating oil, poor low-temperature fluidity, and affecting performance, etc., and achieve low-temperature fluidity improvement, high yield, and depressing effect Good results
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0018] Example 1
[0019] A kind of synthetic method of polymethacrylate pour point depressant, described method comprises the following steps:
[0020] (1) esterification reaction, adding hexadecanol and water-carrying agent toluene into the three-necked flask, cooling water through the condenser tube, under mechanical stirring, heating in an oil bath, the temperature reaches 110-140 ° C, and methacrylic acid is added at this time. In the there-necked flask, the molar ratio of hexadecanol and methacrylic acid is 1:1.5; after it is mixed with alcohol, catalyst toluenesulfonic acid and polymerization inhibitor quinol are added, and the quality of the catalyst is the reaction monomer The total mass is 1.3%, and the quality of the polymerization inhibitor is 0.5% of the total mass of the reaction monomer; when the temperature is raised to the boiling point of the water-carrying agent toluene, the toluene will form an azeotrope with the water generated by the esterification reacti...
Example Embodiment
[0025] Example 2
[0026] (1) esterification reaction, adding hexadecanol and water-carrying agent toluene into the three-necked flask, cooling water through the condenser tube, under mechanical stirring, heating in an oil bath, the temperature reaches 110-140 ° C, and methacrylic acid is added at this time. In the there-necked flask, the mol ratio of hexadecanol and methacrylic acid is 1: 2.5; After it is mixed with alcohol, add catalyst toluenesulfonic acid and polymerization inhibitor benzenediol, and the quality of the catalyst is the reaction monomer The total mass is 2.0%, and the quality of the polymerization inhibitor is 1.0% of the total mass of the reaction monomer; when the temperature is raised to the boiling point of the water-carrying agent toluene, the toluene will form an azeotrope with the water generated by the esterification reaction, and pass The water separator is continuously separated, and the toluene solution of the water-carrying agent in the upper and...
Example Embodiment
[0031] Example 3
[0032] (1) esterification reaction, hexadecanol and water-carrying agent toluene are added into the three-necked flask, cooling water is passed through the condenser tube, and under mechanical stirring, the oil bath is heated, and the temperature reaches 125 ° C. At this time, methacrylic acid is added to the three-necked flask. In the flask, the mol ratio of hexadecanol and methacrylic acid is 1:2; after it is mixed with alcohol uniformly, catalyst toluenesulfonic acid and polymerization inhibitor benzenediol are added, and the quality of the catalyst is the total mass of the reaction monomers 1.8%, the quality of the polymerization inhibitor is 0.8% of the total mass of the reaction monomer; when the temperature is raised to the boiling point of the water-carrying agent toluene, the toluene will form an azeotrope with the water generated by the esterification reaction, and by dividing the water The toluene solution of the water-carrying agent in the upper ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap