A water-repellent finishing, silicone technology, applied in fiber processing, textiles and papermaking, etc., can solve the problems of not particularly obvious effect, increase the tearing strength of fabrics, etc., and achieve the effect of improving tearing strength, washable and water-repellent performance

Inactive Publication Date: 2015-04-22
赵立军
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This type of water repellent can be used in various fiber fabrics, but the effect of increasing the tear strength of the fabric, improving the feel and sewing performance of the fabric is not particularly obvious, and needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The technical solutions of the present invention will be further described in detail below in conjunction with specific examples, so that those skilled in the art can better understand the present invention and implement it, but the examples given are not intended to limit the present invention.

[0022] A formula for organosilicon water-repellent finishing, the raw material composition of the padding liquid is:

[0023] Zinc acetate: 8-12g / L;

[0024] Zirconium oxychloride: 5.5-5.9g / L;

[0025] Methylhydrosilane emulsion: 33-38g / L;

[0026] Aminated epoxy crosslinking agent: 20-23g / L;

[0027] Hydroxysilane emulsion: 72-75g / L;

[0028] Monoethanolamine: 5-6g / L.

[0029] Preferably, the concentration of the aminated epoxy crosslinking agent is 35-40%.

[0030] Preferably, the concentration of the methylhydrosilane emulsion is 27-29%.

[0031] A process for organosilicon water-repellent finishing, comprising the steps of:

[0032] S01: Carry out two dipping and tw...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a formula and a process of organosilicone water repellent finish. The formula is characterized in that the padding liquid raw material composition is as follows: 8-12g/L of zinc acetate, 5.5-5.9g/L of zirconium oxychloride, 33-38g/L of methyl hydrogen-containing silane emulsion, 20-23g/L of epoxidized aminate cross-linker, 72-75g/L of hydroxyl silane emulsion and 5-6g/L of monoethanolamine. A fabric has a good and washable water-repellent performance, and moreover, the tearing strength, hand feeling and sewing performance of the fabric can be obviously improved.

Description

technical field [0001] The invention relates to a formula and process for organosilicon water-repellent finishing. Background technique [0002] Water-repellent finishing is a finishing process that uses chemical water-repellent agents to form a water-repellent surface on fibers. Organosilicon is a washable and water-repellent finishing agent based on linear hydrogen-containing polymethylsiloxane developed in the 1950s, and its reaction performance is relatively active. In application, the organic silicon water-repellent finishing agent and catalysts such as zinc octylate or titanium organic compound are formulated into emulsion padding fabrics, dried and baked at 150°C for several minutes, and then washed with water. During the curing process, the hydromethicone forms a polymer network on the fibers. The methyl groups are arranged vertically and densely on the surface of the fiber, which makes the fabric have good and washable water repellency. This type of water repelle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/643D06M13/188D06M13/368D06M11/46
Inventor 赵立军
Owner 赵立军
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap