Emulsion type automotive polishing agent and preparation method thereof

A polishing agent and emulsified technology, which is applied in the field of emulsified vehicle polishing agent and its preparation, can solve the problems of increasing labor intensity, wasting resources, wasting time, etc., and achieve the effect of reducing manpower and saving resources

Inactive Publication Date: 2015-04-29
TIANJIN YICHENG LONGDA ENVIRONMENTAL PROTECTION TECH DEV
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the current car wash, the cleaning and polishing are separated, that is, the dust on the surface is cleaned, and then rinsed with water, and the cleaning solution is poured on it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] 1. Mix 10% beeswax and 6% oxidized microcrystalline wax in proportion, heat and melt, and then stir to form A solution.

[0017] 2. Dissolve 1% of emulsified silicone oil, 4% of sodium citrate, 3% of sodium azide, and 4% of sodium dihydrogen pyrophosphate in 46% of deionized water, heat to 60-70 degrees, and add kansui 1 % and kelp 3%, stir evenly to form B solution.

[0018] 3. Mix solution A and solution B, keep the temperature at 80-90 degrees, stir evenly, add quantitative sodium dialkylbenzene sulfonate 2%, linalool 5%, cerium oxide 1%, oxidation Antimony 4%, white arsenic 1%, malonic acid 2% and fragrance agent 1%, and the product was obtained.

Embodiment 2

[0020] 1. Mix 15% beeswax and 7% oxidized microcrystalline wax in proportion, heat and melt, and then stir to form A solution.

[0021] 2. Dissolve 2% of emulsified silicone oil, 5% of sodium citrate, 5% of sodium azide, and 4% of sodium dihydrogen pyrophosphate in 39% of deionized water, heat to 60-70 degrees, and add kansui 1 % and kelp 4%, stir evenly to form B solution.

[0022] 3. Mix solution A and solution B, keep the temperature at 80-90 degrees, stir evenly, add quantitative sodium dialkylbenzene sulfonate 2%, linalool 5%, cerium oxide 1%, oxidation Antimony 4%, white arsenic 2%, malonic acid 3% and fragrance agent 1%, and the product was obtained.

Embodiment 3

[0024] 1. Mix 20% beeswax and 8% oxidized microcrystalline wax in proportion, heat and melt, and then stir to form A solution.

[0025] 2. Dissolve 4% of emulsified silicone oil, 8% of sodium citrate, 8% of sodium azide, and 6% of sodium dihydrogen pyrophosphate in 8% of deionized water, heat to 60-70 degrees, and add Kansui 2 % and kelp 6%, stir evenly to form B solution.

[0026] 3. Mix solution A and solution B, keep the temperature at 80-90 degrees, stir evenly, add quantitative sodium dialkylbenzene sulfonate 4%, linalool 8%, cerium oxide 2%, oxidation Antimony 6%, white arsenic 2%, malonic acid 6% and fragrance agent 2%, and the product was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an emulsion type automotive polishing agent. The emulsion type automotive polishing agent is prepared from the following components in percentage by weight: 10-20% of bee wax, 6-8% of oxidized microcrystalline wax, 1-4% of emulsified silicone oil, 1-2% of euphorbia kansui, 2-4% of dialkyl sodium benzenesulfonate, 4-8% of sodium citrate, 3-6% of kelps, 1-2% of a freshener, 5-8% of linalool, 1-2% of cerium dioxide, 4-6% of antimony oxide, 1-2% of white arsenic, 2-6% of malonic acid, 3-8% of sodium azide, 4-6% of sodium dihydrogen pyrophosphate and the balance of deionized water. The emulsion type automotive polishing agent has the advantages that a certain protective film is formed on the surface of the product when the product has a good cleaning effect, a process of drying after the cleaning process, and then polishing the car body are omitted, a protective film is formed by directly repairing the car body in the cleaning process and then attaching, the labor cost is reduced and the resources are saved.

Description

technical field [0001] The invention relates to a polishing agent, in particular to an emulsified vehicle polishing agent and a preparation method thereof. Background technique [0002] In the current car wash, the cleaning and polishing are separated, that is, the dust on the surface is cleaned, and then rinsed with water, and the cleaning solution is poured on it to wipe it. After all the cleaning process is completed, it is dried, and then in the Car body is polished, and this method not only wastes time but also wastes resources, has also increased people's labor intensity. Contents of the invention [0003] In order to solve the above-mentioned technical problems, the technical scheme adopted by the present invention is: provide an emulsified vehicle polishing agent, which comprises: 10-20% beeswax, 6-8% oxidized microcrystalline wax, 1% emulsified silicone oil -4%, kansui 1-2%, sodium dialkylbenzene sulfonate 2-4%, sodium citrate 4-8%, kelp 3-6%, fragrance agent 1-2...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09G1/12C11D1/22C11D3/20
CPCC09G1/02C11D10/00
Inventor 李媛媛
Owner TIANJIN YICHENG LONGDA ENVIRONMENTAL PROTECTION TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap