Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Corrosion-resistant high-toughness zinc-magnesium alloy implanting material capable of being absorbed by human body

A technology of implant materials and alloy materials, which is applied in the field of corrosion-resistant high-strength zinc-magnesium alloy implant materials, can solve the problems of poor corrosion resistance of magnesium alloys and inability to provide mechanical support time, so as to avoid pain, reduce degradation speed, and achieve high durability. erosive effect

Inactive Publication Date: 2015-05-06
XIAN ADVANCED MEDICAL TECH
View PDF2 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the corrosion resistance of magnesium alloy is very poor, it will be degraded and absorbed soon in the human body, and cannot provide enough mechanical support time (service period)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Adopting advanced smelting and processing technology, using high-vacuum electromagnetic melting and casting furnace for melting, the furnace material is suspended while being heated, which can not only avoid crucible pollution, but also achieve uniform mixing of alloy elements; complete casting under vacuum conditions, avoid Oxidation of the alloy; the content of the obtained alloy material is 99wt% of zinc and 1wt% of magnesium. Subsequently, the casting is subjected to multi-pass deformation processing and heat treatment, which greatly improves its toughness and strength.

Embodiment 2

[0021] The prepared alloy material contains 99.5 wt% of zinc and 0.5 wt% of magnesium. Other steps are the same as in Example 1.

Embodiment 3

[0023] The obtained alloy material contains 98wt% of zinc and 2wt% of magnesium. Other steps are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a corrosion-resistant high-toughness zinc-magnesium alloy implanting material capable of being absorbed by human body. The alloy material comprises 96-99.998 wt% of Zn and 0.002-4 wt% of Mg. According to the present invention, the alloy material of the present invention is applied for the absorbable medical implant, particularly the vascular stent and the orthopedic implant (bone nail or bone plate and the like); the prepared zinc-magnesium alloy material of the present invention can be absorbed in the human body environment, such that the pain of the secondary surgery on the patient can be avoided; the corrosion resistance of the prepared zinc-magnesium alloy material is much higher than the corrosion resistance of the magnesium alloy, the degradation speed is substantially reduced, and the long-term mechanical support can be provided, such that the failure of the vascular stent, the bone nail and other implants in advance can be avoided; and the mechanical strength of the prepared zinc-magnesium alloy material is much higher than the mechanical strength of the polymer, and the prepared zinc-magnesium alloy material has characteristics of high toughness, easy manufacturing, good elastic modulus matching with human body, and simultaneous high corrosion resistance and high toughness achieving.

Description

technical field [0001] The invention relates to a fully degradable corrosion-resistant high-strength zinc-magnesium alloy implant material, which belongs to the technical field of medical materials. Background technique [0002] Vascular stent is an implantable wire mesh device used to treat coronary heart disease and other vascular diseases, with a length of about 8-23 mm and a diameter of about 2.5-5 mm. The current mainstream drug-eluting stent (Drug Eluting Stent, DES) provides mechanical support for stenotic blood vessels by expandable cobalt-chromium alloy wire mesh. Lymphocyte growth reduces inflammatory and immune responses. For a long time, Chinese patients have not understood the product of stents, because the incidence of coronary heart disease in my country was extremely low in the past. With the increase of national income year by year, the improvement of people's living standards and the change of diet structure, coronary heart disease has been rising rapidly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L31/02A61L31/14C22C18/02C22C18/00A61F2/82A61B17/80A61B17/86
CPCA61L27/047A61L27/50A61L27/58A61L31/022A61L31/14A61L31/148C22C18/00
Inventor 周功耀屈功奇宫海波
Owner XIAN ADVANCED MEDICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com