Manufacture method of car bumper
A technology of automobile bumper and manufacturing method, which is applied in the field of auto parts, can solve the problems of poor impact resistance and sprayability, and achieve good impact resistance and good sprayability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0015] The manufacture method of this automobile bumper comprises the steps:
[0016] A. Weigh the weight of each raw material according to the following parts by weight: 50 parts of polypropylene, 10 parts of toughening agent, 3 parts of methacrylic acid-ethylene copolymer, 1 part of zinc stearate, 10 parts of talcum powder, lubricant 0.1 part, 0.5 part of antioxidant; Wherein, toughening agent is polyolefin elastomer, and lubricant is polyethylene wax;
[0017] B. Preheating mixer, the preheating temperature is 80°C, add methacrylic acid-ethylene copolymer, zinc stearate, talcum powder, polyethylene wax and antioxidant and mix evenly, then add polypropylene and polyolefin Elastomers are thoroughly mixed;
[0018] C. Add the mixed material into the extruder, melt and extrude to granulate, and the extrusion temperature is 180°C;
[0019] D. Dry the granulated material and add it to the injection molding machine. After the injection molding machine is heated and kept under pr...
Embodiment 2
[0022] A. Weigh the weight of each raw material according to the following parts by weight: 72 parts of polypropylene, 18 parts of toughening agent, 4 parts of methacrylic acid-ethylene copolymer, 2 parts of zinc stearate, 15 parts of talcum powder, lubricant 0.4 part, 0.6 part of antioxidant; Wherein, toughening agent is polyolefin elastomer, and lubricant is polyethylene wax;
[0023] B. Preheating mixer, the preheating temperature is 100°C, add methacrylic acid-ethylene copolymer, zinc stearate, talcum powder, polyethylene wax and antioxidant and mix well, then add polypropylene and polyolefin Elastomers are thoroughly mixed;
[0024] C. Add the mixed material into the extruder, melt and extrude to granulate, and the extrusion temperature is 210°C;
[0025] D. Dry the granulated material and add it to the injection molding machine. After the injection molding machine is heated and kept under pressure, the molten material is pushed into the mold. The injection temperature i...
Embodiment 3
[0028] A. Weigh the weight of each raw material according to the following parts by weight: 80 parts of polypropylene, 25 parts of toughening agent, 5 parts of methacrylic acid-ethylene copolymer, 3 parts of zinc stearate, 0 part of talcum powder, lubricant 0.5 part, 1 part of antioxidant; Wherein, toughening agent is polyolefin elastomer, and lubricant is polyethylene wax;
[0029] B. Preheating mixer, the preheating temperature is 80-100°C, add methacrylic acid-ethylene copolymer, zinc stearate, talcum powder, polyethylene wax and antioxidant and mix evenly, then add polypropylene and Polyolefin elastomers are thoroughly mixed;
[0030] C. Add the mixed material into the extruder, melt and extrude to granulate, and the extrusion temperature is 180-220°C;
[0031] D. Dry the granulated material and put it into the injection molding machine. After the injection molding machine is heated and kept under pressure, the molten material is pushed into the mold. The injection temper...
PUM
Property | Measurement | Unit |
---|---|---|
tensile strength | aaaaa | aaaaa |
bending strength | aaaaa | aaaaa |
surface tension | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com