Glass welded metal composite vacuum plate and production method thereof

A metal composite, vacuum panel technology, applied in building components, thermal insulation, sound insulation, etc., can solve the problems of cold bridges, the thermal insulation performance is not in the best state, etc., and achieve the effect of thin thickness, firm and reliable combination, and high mechanical strength.

Inactive Publication Date: 2015-07-01
戴长虹
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a new type of glass welding A metal composite vacuum panel and a manufacturing method thereof, the manufacturing method of the glass-welded metal composite vacuum panel has a simple process, and the prepared metal composite vacuum panel can overcome the deficiencies of the existing heat insulation panels, vacuum insulation panels and thermal insulation panels, and can effectively Ensure the airtightness of the metal composite vacuum panel, prolong the service life, increase its strength, heat insulation, sound insulation, fire resistance, and also have a good decorative effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass welded metal composite vacuum plate and production method thereof
  • Glass welded metal composite vacuum plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Embodiment 1: see figure 1 The glass-welded metal composite vacuum panel is composed of a panel 1, a connecting layer 2, a vacuum chamber 3 and a support 4. The panel 1 is composed of a thin metal plate such as a stainless steel plate or an aluminum alloy plate with a thickness of 0.2-1.5mm; the connecting layer 2 For high temperature resistant adhesives, high temperature resistant phenolic resin adhesives, epoxy resin adhesives, silicone resin adhesives, polyimide and other organic adhesives, as well as commonly used inorganic adhesives or organic-inorganic composite adhesives, etc., which can be cured at room temperature or high temperature can be selected; Cavity 3 is welded by low-carbon steel plates with a thickness of 0.3-1.0mm; support 4 is made of metal, ceramics, glass or polymer, and is distributed in a lattice by printing, printing, spraying, mechanical layout, etc. In the vacuum chamber 3, the supporting height of the support 4 is preferably 0.15-1.0 mm, and...

Embodiment 2

[0041] Example 2: See Example 1 and figure 2 , is basically the same as Example 1, except that the low-carbon steel plate forming the vacuum chamber 3 is directly punched out of the support 4 and sealing grooves for edge sealing during stamping, and glass solder is placed in the sealing grooves.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a glass welded metal composite vacuum plate. The vacuum plate comprises a panel, a connecting layer and a vacuum cavity, and is characterized in that the panel is made from a a metal plate, the panel and the vacuum cavity are integrally connected by the connecting layer, the panel and / or the connecting layer are used for providing additional strength to the vacuum cavity to ensure the smoothness of the vacuum cavity in barometric pressure, and the vacuum cavity is formed by welding low carbon steel plates by a glass solder in the vacuum furnace at high vacuum and high temperature; the coefficients of thermal expansion of the low carbon steel plates and the glass solder are matched, and a support is arranged in the vacuum cavity and is separately made or directly formed in the vacuum cavity. A production method of the metal composite vacuum plate provided by the invention is simple in process, the defects of an existing insulation board and a vacuum insulated panel can be overcome by the prepared glass composite vacuum plate, the air-tightness of the vacuum cavity of the metal composite vacuum plate can be effectively ensured, the service life of the metal composite vacuum plate can be prolonged, and the strength, heat insulation, sound insulation and fire resistance can be enhanced.

Description

technical field [0001] The invention relates to the technical field of building energy conservation, in particular to a glass-welded metal composite vacuum panel and a manufacturing method thereof. Background technique [0002] At present, the materials used for building exterior wall insulation are divided into A-grade thermal insulation materials and B-grade thermal insulation materials. A-grade thermal insulation materials have good fire resistance, but their thermal insulation performance and water resistance are lower than B-grade thermal insulation materials, and there are high prices. Complex construction technology and other issues; B-grade thermal insulation materials have the advantages of low cost, good thermal insulation performance, and mature construction technology, but their durability is not good, heat resistance is poor, and they are easy to burn. Moreover, it can accelerate the spread of fire, so it is forbidden to use organic thermal insulation materials ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04B1/90E04B1/94E04F13/075
Inventor 戴长虹
Owner 戴长虹
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com