Noniron finishing method of silk fabric

A non-iron finishing and silk technology, applied in fiber treatment, animal fiber, biochemical fiber treatment, etc., can solve the problems of ineffectiveness and great influence on silk performance, and achieve the advantages of improving wrinkle resistance, retaining hand feeling, and improving mechanical strength. Effect

Inactive Publication Date: 2015-07-08
SUZHOU WILDER IND & TRADE
View PDF11 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen from the above prior art that the wrinkle resistance, shrinkage and durability of the silk fabric after finishing have all been improved, but the performance of the silk itself is greatly affected, and the desired effect cannot be achieved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Noniron finishing method of silk fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Wash the silk fabric twice with water at 45°C, refine and puff it with a pH value of 6.5, 2% (owf) IndisAeg super enzyme solution at 60°C for 20 minutes, and then rinse it with water at 35°C for 3 minutes to obtain puffed silk fabrics .

[0029] Dissolve the waste silk to obtain a 3% silk fibroin solution with a molecular weight of 50-100kDa, add 3% citric acid and 5g / L quaternary ammonium chitosan, mix well, and then add a penetrant in an amount of 5g / L , the consumption of softening agent is 2g / L, stirs to obtain non-ironing finishing agent.

[0030] Immerse the puffed silk fabric in the non-ironing finishing agent, bath ratio 1:30, dip for 5 minutes at 25°C, the padding rate is 70%, pre-steam the padded silk fabric with a mixture of ethanol and water at 75°C Bake for 5 minutes, the water content of the silk fabric is 15%, then the silk fabric is subjected to constant temperature tentering at 120° C. for 10 seconds, then baked at 120° C. for 3 minutes, finally washed...

Embodiment 2

[0032] The silk fabric was washed twice with water at 55°C, refined and puffed with a 3% (owf) trypsin solution at 60°C for 20 minutes with a pH value of 6.5, and then rinsed with water at 40°C for 2 minutes to obtain puffed silk fabrics.

[0033] Dissolving waste silk to obtain a 5% silk fibroin solution with a molecular weight of 50-100kDa, adding 4% citric acid and 5g / L quaternary ammonium chitosan, mixing evenly, and stirring to obtain a non-ironing finishing agent.

[0034] Immerse the puffed silk fabric in the non-ironing finishing agent, bath ratio 1:30, dip for 5 minutes at 30°C, the padding rate is 85%, pre-steam the padded silk fabric with a mixture of ethanol and water at 75°C Bake for 5 minutes, the moisture content of the silk fabric is 20%, then the silk fabric is subjected to constant temperature tentering at 100° C. for 10 seconds, then baked at 120° C. for 2 minutes, finally washed, dried, ironed and packaged to obtain a non-ironing silk fabric.

Embodiment 3

[0036] The silk fabric was washed twice with 50°C water, refined and puffed at 60°C with a pH value of 6.5, 2.5% (owf) trypsin solution at 60°C for 20 minutes, and then rinsed with 36°C water for 2 minutes to obtain puffed silk fabrics.

[0037] Dissolve the waste silk to obtain a 4% silk fibroin protein solution with a molecular weight of 50-100kDa, add 3% citric acid, 5g / L quaternary ammonium chitosan, mix well, and then add a penetrating agent in an amount of 2g / L , the consumption of softening agent is 1g / L, stirs to obtain non-ironing finishing agent.

[0038] Immerse the puffed silk fabric in the non-ironing finishing agent, bath ratio 1:30, dip for 5 minutes at 25°C, the padding rate is 80%, pre-steam the padded silk fabric with a mixture of ethanol and water at 75°C Bake for 5 minutes, the moisture content of the silk fabric is 17%, then the silk fabric is subjected to constant temperature tentering at 115° C. for 11 seconds, then baked at 120° C. for 2 minutes, finall...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
molecular weightaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses a noniron finishing method of a silk fabric. The noniron finishing method particularly comprises the following steps: moistening and rinsing the silk fabric with warm water twice, refining and expanding the silk fabric by using a biological enzyme, after rinsing with warm water, padding the expanded silk fabric in a wash and wear finisher containing silk fibroin, citric acid and chitosan quaternary ammonium salt, then predrying the silk fabric, tentering at constant temperature, baking at high temperature, washing with water and drying, and pressing-packaging to obtain the noniron finished silk fabric. According to the noniron finishing method, a biological enzyme technology is combined with a padding technology, the silk fabric is subjected to noniron finishing by using the silk fibroin, the citric acid and the chitosan quaternary ammonium salt, so that the noniron finishing method has the advantages of simple and effective, environmental-friendly and biological effects. The silk fabric prepared by adopting the noniron finishing method reaches a noniron degree, and has a good crease-resisting and deformation-resisting capabilities; the dyeing performance of the fabric is improved; the handfeel, the style and the mechanical property of the fabric are reserved, and thus the noniron finishing method is an ideal noniron finishing method of the silk fabric.

Description

Technical field: [0001] The invention belongs to the technical field of silk products, in particular to a non-ironing finishing method of silk fabrics. Background technique: [0002] In the process of use, the fabric will undergo large deformation or strain after repeated action or long-term friction and expansion, such as shrinkage, arching, wrinkling, bursting, draping, etc. This is because the fabric is connected by friction between fibers and fibers, yarns and yarns, and its mechanical properties are prone to deformation, anisotropy, and nonlinear mechanical properties. [0003] In order to maintain the stable shape and specific mechanical properties of the fabric, physical and chemical methods are often used. The physical method is to adopt a stable fabric structure, optimize the composition of the yarns in the fabric, the interweaving mode and the running direction of the yarns, and use the tenter frame or pre-shrinking machine to control the shrinkage of various fabr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M16/00D06M15/15D06M15/03D06M13/207D06M101/10
Inventor 刘玲
Owner SUZHOU WILDER IND & TRADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap