Rapid-solidifying composite cementing compound of solar component back plate and preparation method thereof
A composite adhesive and solar module technology, applied in the field of solar module backsheet composite adhesive and its preparation, can solve the problems of restricting the production efficiency and production capacity of backsheet manufacturers, slow curing speed, etc., and improve the curing reaction speed and hydrolysis resistance. , Good hydrolysis resistance, good UV resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0015] The embodiment of the present invention provides a fast-curing solar cell module backplane composite adhesive and a preparation method thereof. The prepared composite adhesive has the characteristics of fast curing speed, high heat resistance, high humidity resistance and ultraviolet light resistance. The method includes the following steps:
[0016] Main ingredient preparation:
[0017] Put triethylene glycol, hydroxypivalic acid neopentyl glycol monoester, and 1,4-cyclohexanedimethanol into the esterification reaction kettle, fill with nitrogen protection, heat, dissolve and mix, and then put in terephthalic acid and phthalic anhydride , 1,12-lauric acid, gradually warming up the esterification reactor to 220°C, and the esterification reaction will start when the water is distilled from the esterification reactor. If the water output of the esterification reaction reaches the theoretical water output, the esterification reaction will be completed; The hydroxyl value a...
Embodiment 1
[0023] Prepare the main ingredient:
[0024] Put 11 kg of triethylene glycol, 19 kg of hydroxypivalate neopentyl glycol monoester, and 20.5 kg of 1,4-cyclohexanedimethanol into the esterification reaction kettle, fill with nitrogen protection, heat to 120°C to dissolve and mix , and then put in 12 kilograms of terephthalic acid, 19 kilograms of phthalic anhydride, and 18.5 kilograms of 1,12-lauric acid to gradually raise the temperature of the esterification reactor to 220 ° C. When the esterification reactor distills water, the esterification reaction begins. When the water output reaches the theoretical water output, the esterification reaction is completed; the hydroxyl value of the product measured by sampling is 13.2 mgKOH / g, and the acid value is 19.5 mgKOH / g. Add 20 grams of tetraisopropyl titanate catalyst to maintain the temperature of the esterification reaction kettle Vacuum at 220-230°C for polycondensation reaction, keep at -0.06Mpa vacuum for 1 hour; then evacuat...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap