Assembly type lightweight thin wall integrated pipe gallery and production method thereof
A comprehensive pipe gallery and prefabricated technology, applied in the field of municipal comprehensive pipelines, can solve the problems of small self-weight, achieve low cost, reduce the amount of foundation excavation and backfill, and reduce the thickness of the structure
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0062] Example 1
[0063] A fabricated lightweight and thin-walled comprehensive pipe gallery is cast by using ultra-high performance powder concrete, which includes the following components by weight:
[0064] 900 parts of 42.5 grade ordinary Portland cement with an average particle size of 30~60μm;
[0065] 100 parts of micro silicon powder with an average particle size of 5-20μm and SiO2 content ≥85%;
[0066] 45 parts of limestone powder with an average particle size of 10~30μm;
[0067] 30 parts of nanometer calcium carbonate powder;
[0068] 550 parts of continuously graded ceramic sand with a particle size of 2.5 or less;
[0069] 16 copies of superplasticizer with a water reduction rate greater than 30%;
[0070] 220 parts of water;
[0071] The average diameter is 0.20mm, and the length is 12~15mm. 130 parts of copper-plated fiber;
[0072] 80 parts of copper-plated fiber with an average diameter of 0.12mm and a length of 6-10mm;
[0073] The pipe gallery is formed by splicing 4 circ...
Example Embodiment
[0083] Example 2
[0084] A fabricated lightweight and thin-walled comprehensive pipe gallery is cast by using ultra-high performance powder concrete, which includes the following components by weight:
[0085] 950 parts of 42.5 grade ordinary Portland cement with an average particle size of 30~60μm;
[0086] 120 parts of microsilica powder with an average particle size of 5-20μm and SiO2 content ≥85%;
[0087] 50 parts of limestone powder with an average particle size of 10~30μm;
[0088] 35 parts of nanometer calcium carbonate powder;
[0089] 600 parts of continuously graded ceramic sand with a particle size of 2.5 or less;
[0090] 18 copies of superplasticizer with water reduction rate greater than 30%;
[0091] 230 parts of water;
[0092] The average diameter is 0.20mm, and the length is 12~15mm. 130 parts of copper-plated fiber;
[0093] 80 parts of copper-plated fiber with an average diameter of 0.12mm and a length of 6-10mm;
[0094] Such as Figure 5~8 As shown, the pipe gallery is...
Example Embodiment
[0100] Example 3
[0101] Except that the formula ratio of ultra-high performance powder concrete is different, the others are the same as in Example 1;
[0102] The ultra-high performance powder concrete includes the following components by weight:
[0103] 1000 copies of 42.5 grade ordinary Portland cement with an average particle size of 30~60μm;
[0104] 130 parts of microsilica powder with an average particle size of 5-20μm and SiO2 content ≥85%;
[0105] 53 parts of limestone powder with an average particle size of 10~30μm;
[0106] 40 parts of nanometer calcium carbonate powder;
[0107] 630 parts of continuously graded ceramic sand with a particle size of 2.5mm or less;
[0108] 19 copies of superplasticizer with water reduction rate greater than 30%;
[0109] 240 parts of water;
[0110] The average diameter is 0.20mm, and the length is 12~15mm. 130 parts of copper-plated fiber;
[0111] 80 parts of copper-plated fiber with an average diameter of 0.12mm and a length of 6-10mm;
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap