Nano-mesoporous titanium dioxide anticorrosive coating

An anti-corrosion coating and nano-mesoporous technology, applied in the field of coatings, can solve the problems of high surface free energy, high intermolecular attraction and electrostatic attraction, easy agglomeration, etc. Good results

Inactive Publication Date: 2015-09-16
牛无畏
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, because nano-mesoporous titanium dioxide is very small, its specific surface area is large, its surface free energy is high, and its intermolecular and ele

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano-mesoporous titanium dioxide anticorrosive coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The nanometer mesoporous titanium dioxide anticorrosion coating of the present invention comprises the following components in parts by weight: 35 parts of water-based epoxy resin emulsion, 20 parts of nanometer mesoporous silicon dioxide particles, 5 parts of nanometer titanium dioxide, 8 parts of dispersant, ophthalmic 3 parts of dioctyl diformate, 12 parts of ethylene glycol ethyl ether, 4 parts of sodium bentonite, and 35 parts of deionized water.

Embodiment 2

[0021] The nanometer mesoporous titanium dioxide anticorrosion coating of the present invention comprises the following components in parts by weight: 45 parts of aqueous epoxy resin emulsion, 10 parts of nanometer mesoporous silicon dioxide particles, 15 parts of nanometer titanium dioxide, 2 parts of dispersant, 9 parts of dibutyl diformate, 2 parts of ethylene glycol butyl ether, 10 parts of organic bentonite, and 25 parts of deionized water.

Embodiment 3

[0023] The nanometer mesoporous titanium dioxide anticorrosion coating of the present invention comprises the following components in parts by weight: 40 parts of water-based epoxy resin emulsion, 15 parts of nanometer mesoporous silicon dioxide particles, 9 parts of nanometer titanium dioxide, 6 parts of dispersant, ophthalmic 5 parts of dioctyl diformate, 7 parts of alcohol ester twelve, 8 parts of diatomaceous earth, 28 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a nano-mesoporous titanium dioxide anticorrosive coating which comprises the following components in parts by weight: 35-45 parts of water-borne epoxy resin emulsion, 10-20 parts of nano-mesoporous silicon dioxide particles, 5-15 parts of nano titanium dioxide, 2-8 parts of dispersant, 3-9 parts of plasticizer, 2-12 parts of coalescing agent, 4-10 parts of thickening agent and 25-35 parts of deionized water. The nano-mesoporous titanium dioxide anticorrosive coating disclosed by the invention has excellent antibacterial and anticorrosive performance, high surface strain resistance and good weather resistance; and without organic solvents, the nano-mesoporous titanium dioxide anticorrosive coating is environment-friendly and non-toxic, avoids harm to the environment and human bodies, and is applicable to anticorrosive treatment on the metal surfaces of steel, aluminum products and the like.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a nanometer mesoporous titanium dioxide anticorrosion coating. Background technique [0002] With the continuous progress of nanomaterials science, the excellent properties of nanocomposite coatings have attracted increasing attention. According to the nano-size effect and huge specific surface area characteristics of nanoparticles, evenly dispersing nanoparticles in traditional anti-corrosion coatings to make nano-composite coatings can greatly improve the excellent performance of anti-corrosion coatings. [0003] Nano-mesoporous titanium dioxide is an excellent photocatalytic inorganic antibacterial material, non-toxic, tasteless, and non-irritating. Applying it to coatings and keeping them in a nano-scale state in the coating can improve the poor weather resistance and easy-sticking of existing coatings. Pollution and other shortcomings. [0004] However, because nano-mesoporous tita...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D7/12C09D5/08
Inventor 牛无畏
Owner 牛无畏
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap