High-performance moisture-proof wooden floor special paint
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A wood floor, high-performance technology, used in anti-corrosion coatings, coatings, epoxy coatings, etc., can solve problems affecting floor paint, mold, expansion, etc., and achieve good corrosion resistance, water resistance, and gloss. high effect
Inactive Publication Date: 2015-09-23
QINGDAO ENGAO MOTION CONTROL TECH
View PDF0 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Because we often use water to wipe the floor, the floor will become gray and dull after wiping, and if it is wiped for a long time, it will seriously affect the original paint surface of the floor, and it is very necessary for the floor to be moisture-proof. The water damage and natural resin contained in it are gradually lost, which will greatly affect the service life of the floor after a long time. The floor is easy to be damp and moldy, which will cause the floor to deform and expand. Therefore, the floor paint is required to have good moisture resistance
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0008] A special paint for high-performance moisture-proof wood floors, which is made of the following raw materials in parts by weight:
[0009] 20 Chinese parts of E-12 epoxy resin, 4 parts of mica powder, 7 parts of dioctyl ester, 6 parts of tripropylene glycol diacrylate, 2 parts of butadiene, 3 parts of polyisobutylene, 4 parts of aluminum sulfate, hydroxyl acrylic resin 8 parts, 0.5 parts of leveling agent, 8 parts of limonene, 12 parts of ethylene glycol monoethyl ether, 4 parts of zeolite powder, 25 parts of phenolic resin, 8 parts of non-leafing aluminum powder slurry, 3 parts of cellulose acetate, 7 parts of polybutylacrylate Parts, 3 parts of crosslinking agent TAC, 4 parts of triethylamine.
Embodiment 2
[0011] A special paint for high-performance moisture-proof wood floors, which is made of the following raw materials in parts by weight:
[0012] 36 parts of E-12 epoxy resin, 6 parts of mica powder, 12 parts of dioctyl ester, 10 parts of tripropylene glycol diacrylate, 3 parts of butadiene, 5 parts of polyisobutylene, 6 parts of aluminum sulfate, 15 parts of hydroxyl acrylic resin 1.5 parts of leveling agent, 14 parts of limonene, 18 parts of ethylene glycol monoethyl ether, 5 parts of zeolite powder, 32 parts of phenolic resin, 14 parts of non-leafing aluminum powder slurry, 6 parts of cellulose acetate, 10 parts of polybutylacrylate , 4 parts of cross-linking agent TAC, 6 parts of triethylamine.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
Disclosed is a high-performance moisture-proof wooden floor special paint. The raw materials of the paint include, by weights: 20 to 36 parts of E-12 epoxy resin, 4 to 6 parts of mica powder, 7 to 12 parts of dioctylester, 6 to 10 parts of tripropylene glycol diacrylate, 2 to 3 parts of butadiene, 3 to 5 parts of polyisobutylene, 4 to 6 parts of aluminum sulfate, 8 to 15 parts of hydroxyl acrylic acid resin, 0.5 to 1.5 part of flatting agent, 8 to 14 parts of limonene, 12 to 18 parts of ethylene glycol monoethyl ether, 4 to 5 parts of zeolite powder, 25 to 32 parts of phenolic resin, 8 to 14 parts of non-floating aluminum slurry, 3 to 6 parts of acetate fiber, 7 to 10 parts of PBA, 3 to 4 parts of crosslinking agent and 4 to 6 parts of triethylamine. The paint has the advantages of fine corrosion resistance, effective moisture-proof property, fine water resistance, high glossiness, high strength and wear resistance, damage of environment and human body is avoided, and the paint is environment-friendly.
Description
technical field [0001] The invention relates to a high-performance moisture-proof special paint for wooden floors. Background technique [0002] In China's 2010 development goals, the construction industry will become one of the pillar industries of China's national economy. With the development of the construction industry, the interior decoration industry will have greater development, and wood flooring will also develop as one of the important materials for interior decoration. With the vigorous development of China's economy and the improvement of residents' living standards, wooden flooring has become the first choice for people's floor decoration due to its outstanding advantages such as comfortable feet, warmth, and elegance, and its market demand is also showing a linear upward trend. . Because we often use water to wipe the floor, the floor will become gray and dull after wiping, and if it is wiped for a long time, it will seriously affect the original paint surfa...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more