A kind of penetrating agent for mercerizing and preparation method thereof

A technology of mercerizing penetrant and initiator, applied in textiles and papermaking, fiber processing, plant fibers, etc., can solve the problems of high cost, general penetration, poor penetration of cationic surfactants, etc., to achieve good penetration, cost low effect

Active Publication Date: 2018-03-02
广东灵捷制造化工有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Penetration of octyl sulfonate is average, while cationic surfactants have poorer penetration and higher cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of penetrating agent for mercerizing and preparation method thereof
  • A kind of penetrating agent for mercerizing and preparation method thereof
  • A kind of penetrating agent for mercerizing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Add 16g of macromonomer, 56g of acrylic acid, 8g of dimethylaminoethyl acrylate, 0.8g of ammonium persulfate, and 320g of water into a 500ml four-neck flask, protect it with nitrogen, keep the temperature at 60°C for 12 hours, and obtain a light yellow transparent viscous body , 25 ℃ self-viscosity is 1000mp a.s That is, a polymer amphoteric surfactant with a concentration of 20%. In this embodiment, the general structural formula of the macromonomer adopted is: R 1 O(CH 2 CH 2 O) n CH 2 CH(OH)R 2 , where: R 1 for linear C 9 ~C 15 Alkyl, n=3~15; R 2 for CH 2 CH 2 CH=CH 2 、CH 2 CH=CH 2 , CH=CH 2 、CH 2 OCH 2 CH=CH 2 、CH 2 OCH=CH 2 or OCH=CH 2 .

Embodiment 2-7

[0031] Others are the same as in Example 1, but the cationic monomers used are respectively diethylaminoethyl acrylate 8g, dimethylaminoethyl methacrylate 8g, monoallylamine 8g, diallylamine 8g, triallyl Base amine 8g, dimethyl diallyl ammonium chloride 8g.

Embodiment 8

[0033] Add 8g of macromer, 56g of methacrylic acid, 16g of dimethylaminoethyl acrylate, 0.4g of ammonium persulfate, and 320g of water into a 500ml four-necked flask. Thick body, that is, a polymer amphoteric surfactant with a concentration of 20%. In this embodiment, the general structural formula of the macromonomer adopted is: R 1 O(CH 2 CH 2 O) n CH 2 CH(OH)R 2 , where: R 1 for linear C 9 Alkyl, n=3; R 2 for CH=CH 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a mercerizing penetrant used in cellulose fiber mercerizing and polyester alkali weight reduction process and a preparation method thereof. Calculated by weight percentage, the mercerizing penetrant includes 30-50% octyl phosphate; 10-30% JFC phosphate; 10-30% amphoteric polymer surfactant; 10-30% alkyl sugar anhydride. The mercerizing penetrant of the invention has an alkali resistance of 300g NaOH / l, and has excellent penetrating power in a solution of 180g NaOH / l-300g NaOH / l.

Description

technical field [0001] The invention relates to a mercerizing penetrant mainly used in cellulose fiber mercerizing and polyester alkali reduction processes and a preparation method thereof. technical background [0002] In cellulose fiber mercerizing process and polyester alkali weight reduction process, the NaOH concentration usually used is 180g NaOH / l-300g NaOH / l. In order to achieve good processing performance, mercerizing penetrant must be added. The mercerizing penetrant must be resistant to lye over 180g NaOH / l, and must also have good penetrating ability. [0003] Chinese patent 201010527958.8 discloses a highly alkali-resistant wet cloth mercerizing penetrant and its preparation method. The penetrant is isomeric tridecanol polyoxyethylene ether phosphate, which can be used in the wet cloth mercerizing process of cotton, linen fabrics and their blended fabrics. [0004] Chinese patent application 201510032538.5 discloses a phosphate ester mercerizing penetrant and i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M13/292D06M15/263D06M13/11C08F283/06C08F220/06D06M101/06
Inventor 魏焕曹
Owner 广东灵捷制造化工有限公司