High-modulus flame-retardant antistatic safe protection belt and preparation method thereof

A flame-retardant, anti-static, safety protection technology, which is applied in the processing of textile materials, equipment configuration, textile materials processing, textiles and papermaking, etc., can solve the problem of inability to effectively guarantee the personal safety of users, protective belts without flame-retardant, anti-static, There are no problems such as preparation methods, and the effects of fast production speed, fast adjustment and strong versatility are achieved

Inactive Publication Date: 2015-11-18
HAINING JINGDA FABRIC
View PDF11 Cites 33 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the protective belt disclosed in this patent is easy to use and can be repeatedly cleaned and disinfected, the protective belt does not have functions such as flame retardancy and antistatic, and cannot effectively guarantee the personal safety of the user when used in a complex environment. Poor safety, and no preparation method, therefore, it is necessary to design a high modulus flame retardant antistatic safety protective tape and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-modulus flame-retardant antistatic safe protection belt and preparation method thereof
  • High-modulus flame-retardant antistatic safe protection belt and preparation method thereof
  • High-modulus flame-retardant antistatic safe protection belt and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] The preparation method of the high-modulus flame-retardant antistatic safety protection belt comprises the following steps:

[0052] A, take the required raw material by the weight part of above each component;

[0053] b. Add polyvinyl chloride and polycarbonate to an ordinary mixer, stir for 10 minutes, and the stirring speed is 200r / min;

[0054] c. Add solvent, magnesium oxide, zinc oxide, calcium carbonate, crosslinking agent, plasticizer, antistatic agent and antioxidant to a common mixer, stir for 15 minutes, and the stirring speed is 150r / min to prepare the coating;

[0055] d. Spray the paint on the base cloth layer by spraying equipment, and the spraying amount is 200g / m 2 , the paint layer formed by spraying is the strengthening layer;

[0056] e. Put the sprayed base cloth layer into an ordinary drying box, set 3 drying sections, and the temperature of the 3 drying sections is 80°C, 120°C, and 150°C in turn, and the base cloth is treated according to the a...

Embodiment 2

[0064] The preparation method of the high-modulus flame-retardant antistatic safety protection belt comprises the following steps:

[0065] A, take the required raw material by the weight part of above each component;

[0066] b. Add polyvinyl chloride and polycarbonate to an ordinary mixer, stir for 15 minutes, and the stirring speed is 250r / min;

[0067] c. Add solvent, magnesium oxide, zinc oxide, calcium carbonate, crosslinking agent, plasticizer, antistatic agent and antioxidant to a common mixer, stir for 17 minutes, and the stirring speed is 180r / min to prepare the coating;

[0068] d. Spray the paint on the base cloth layer by spraying equipment, and the spraying amount is 250g / m 2 , the paint layer formed by spraying is the strengthening layer;

[0069] e. Put the sprayed base cloth layer into an ordinary drying box, set 3 drying sections, and the temperature of the 3 drying sections is 80°C, 120°C, and 150°C in turn, and the base cloth is treated according to the a...

Embodiment 3

[0077] The preparation method of the high-modulus flame-retardant antistatic safety protection belt comprises the following steps:

[0078] A, take the required raw material by the weight part of above each component;

[0079] b. Add polyvinyl chloride and polycarbonate to an ordinary mixer, stir for 20 minutes, and the stirring speed is 300r / min;

[0080] c. Add solvent, magnesium oxide, zinc oxide, calcium carbonate, crosslinking agent, plasticizer, antistatic agent and antioxidant to a common mixer, stir for 20 minutes, and the stirring speed is 200r / min to prepare the coating;

[0081] d. Spray the paint on the base cloth layer by spraying equipment, and the spraying amount is 300g / m 2 , the paint layer formed by spraying is the strengthening layer;

[0082] e. Put the sprayed base cloth layer into an ordinary drying box, set 3 drying sections, and the temperature of the 3 drying sections is 80°C, 120°C, and 150°C in turn, and the base cloth is treated according to the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-modulus flame-retardant antistatic safe protection belt and a preparation method thereof, and solves the problems that when the conventional protection belt is used in a complex environment, the personnel safety of a user cannot be protected effectively as the conventional protection belt is not flame-retardant and antistatic, the safety is poor and no preparation methods is available. The high-modulus flame-retardant antistatic safe protection belt comprises a base cloth layer, wherein reinforcing layers are fixed on both sides of the base cloth layer; the reinforcing layers comprise the following ingredients by weight: 40 to 60 parts of polyvinyl chloride, 20 to 30 parts of polycarbonate, 6 to 10 parts of a solvent, 3 to 6 parts of magnesium oxide, 3 to 6 parts of zinc oxide, 5 to 10 parts of calcium carbonate, 2 to 4 parts of a cross-linking agent, 3 to 8 parts of a plasticizing agent, 5 to 8 parts of an antistatic agent, and 0.1 to 0.3 part of an anti-oxidant. The high-modulus flame-retardant antistatic safe protection belt and the preparation method have the advantages that the safety is high; the production is fast.

Description

technical field [0001] The invention relates to a protective belt, in particular to a high-modulus flame-retardant antistatic safety protective belt and a preparation method thereof. Background technique [0002] The protective belt is a belt-shaped braid, which mainly plays a protective role and can ensure the personal safety of the user. The defense belt has a wide range of applications, and can be applied to conveyor belts, slings, and driving belts used in various industries such as cargo handling, chemical industry, printing, and building materials. [0003] After retrieval, such as Chinese patent literature discloses a safety protective belt [application number: 201320043878.4; announcement number: CN203017210U]. The safety protection belt is characterized in that it consists of a main body and a tie belt, and the four corners of the main body are respectively fixedly connected with the tie belt. [0004] Although the protective belt disclosed in this patent is easy ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/248D06M15/513D06M11/44D06M11/76D06M11/51D06M13/335D06B1/02D06B23/20D06B23/24D06M101/32
Inventor 范跃良范忠良
Owner HAINING JINGDA FABRIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com