Low-smoke and non toxicity cable sheath

A cable skin and oil-resistant technology, applied in the field of cables, can solve the problems of dense, flammable and toxic smoke, and peculiar smell of cable skin, and achieve the effects of reducing toxic gas, not easy to burn, and reducing consumption

Inactive Publication Date: 2015-11-25
张凌
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Cable sheaths are widely used in the cable manufacturing process. They are often used to wrap single-strand or multi-strand wires and insulating layers. Now the composite performance of decoration materials is getting better and better. Although the appearance is beautiful, it will emit peculiar smell when heated, especially when encountering In the event of a fire, it is easier to burn and emit poisonous gas; the death rate due to suffocation due to poisonous gas in fires in my country currently accounts for more than 80%
However, the traditional cable sheath is flammable, toxic and dense in smoke due to the addition of too much PVC.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The preparation of the low-smoke and non-toxic cable sheath comprises the following steps:

[0015] 1) Ingredients

[0016] Take the following raw materials in parts by weight: 40 parts of SG-2 type resin, 25 parts of diisodecyl phthalate,

[0017] 2 parts of calcium / zinc composite stabilizer, 1 part of bisphenol A, the ingredients are refined, fully mixed, the fineness after refining is less than or equal to 70 μm, and the main ingredient after refining is obtained;

[0018] 2) Add filler

[0019] Add 50 parts of calcined calcium carbonate and 0.1 part of stearic acid to the main ingredient after refining, stir evenly and refine again, the fineness after refining is less than or equal to 60 μm, and obtain the main ingredient after refining again;

[0020] 3) Kneading

[0021] Control the temperature at 50°C, and knead the main ingredients after refining again for 4 minutes;

[0022] 4) Extrusion

[0023] Control the temperature at 140°C and extrude;

[0024] 5) P...

Embodiment 2

[0027] The preparation of the low-smoke and non-toxic cable sheath comprises the following steps:

[0028] 1) Ingredients

[0029] Take the following raw materials in parts by weight: 50 parts of SG-2 type resin, 30 parts of diisodecyl phthalate,

[0030] 4 parts of calcium / zinc composite stabilizer, 2 parts of bisphenol A, the ingredients are refined, fully mixed, the fineness after refining is less than or equal to 70 μm, and the main ingredient after refining is obtained;

[0031] 2) Add filler

[0032] Add 60 parts of calcined ceramic clay and 1 part of stearic acid to the main ingredient after refining, stir evenly and then refine again, the fineness after refining is less than or equal to 60 μm, and obtain the main ingredient after refining again;

[0033] 3) Kneading

[0034] Control the temperature at 75°C, and knead the main ingredients after refining again for 10 minutes;

[0035] 4) Extrusion

[0036] Control the temperature at 160°C and extrude;

[0037] 5) P...

Embodiment 3

[0040] The preparation of the low-smoke and non-toxic cable sheath comprises the following steps:

[0041] 1) Ingredients

[0042] Take the following raw materials in parts by weight: 85 parts of SG-2 type resin, 28 parts of diisononyl phthalate

[0043] 5 parts of calcium / zinc composite stabilizer, 2.5 parts of bisphenol A, the ingredients are refined, fully mixed, the fineness after refining is less than or equal to 70 μm, and the main ingredient after refining is obtained;

[0044] 2) Add filler

[0045] Add 40 parts of calcined ceramic soil and 20 parts of calcium carbonate to the main material after refining, stir evenly and then refine again, the fineness after refining is less than or equal to 60 μm, and obtain the main material after refining again;

[0046] 3) Kneading

[0047] Control the temperature at 70°C, and knead the main ingredients after refining again for 8 minutes;

[0048] 4) Extrusion

[0049] Control the temperature at 155°C and extrude;

[0050] 5...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a low-smoke and non toxicity cable sheath, and belongs to the technical field of cable lines. The low-smoke and non toxicity cable sheath is formed by carrying out a reaction on the following raw materials by weight: 40-50 parts of a suspension method polyvinyl chloride resin, 25-30 parts of a plasticizer, 2-4 parts of a composite stabilizing agent, 1-2 parts of an anti-oxidant, 50-60 parts of a filler and 0.1-1 part of a lubricant, wherein the filler is calcining ceramic clay and / or calcium carbonate, and the plasticizer is diisodecyl ortho-phthalate or diisononyl phthalate. According to the low-smoke and non toxicity cable sheath, combination of various raw materials can greatly reduce the usage of the suspension method polyvinyl chloride resin, combustion is difficult, the smoke is low even in a combustion process, poison gas is greatly reduced, basically, no toxin is generated, and the low-smoke and non toxicity cable sheath is suitable for popularization and application in public area, and has the advantage of environmental protection and is beneficial to health.

Description

technical field [0001] The invention belongs to the technical field of cables, and in particular relates to a low-smoke and non-toxic cable sheath. Background technique [0002] Cable sheaths are widely used in the cable manufacturing process. They are often used to wrap single-strand or multi-strand wires and insulating layers. Now the composite performance of decoration materials is getting better and better. Although the appearance is beautiful, it will emit peculiar smell when heated, especially when encountering In the event of a fire, it is easier to burn and emit poisonous gas; the death rate due to suffocation due to poisonous gas in fires in my country currently accounts for more than 80%. However, the traditional cable sheath is flammable, toxic and dense in smoke due to the addition of too much PVC. Contents of the invention [0003] Purpose of the invention: The purpose of the invention is to provide a low-smoke and non-toxic cable sheath, which is non-toxic an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K5/12C08K3/34C08K3/26
Inventor 张凌
Owner 张凌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com