Purification method for carbon in life entity boneless tissues
A purification method and bone tissue technology are applied in the field of carbon purification, which can solve the problems of insufficient carbon purity and difficulty in extraction, and achieve the effect of good purification effect and high practicability.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0054] figure 1 The method for purifying carbon in the boneless tissue of a living body provided by Embodiment 1 of the present invention is shown. The boneless tissue is selected from human nails, which includes the following steps:
[0055] a. Isolate the air and dry the human nails, crush them to obtain 10g of powder;
[0056] b. Put 10g of powder into the container, isolate the air, and pass through nitrogen and hydrogen to remove the residual air in the container. The volume of hydrogen accounts for 5% of the total volume of the gas, and then heat the powder to 600°C. Carry out carbonization reaction at high temperature for 30 minutes, and then remove impurities to obtain crude carbon;
[0057] c. Adding the crude carbon product to 5% dilute hydrochloric acid by weight to dissolve it, reacting in a mixer with a rotating speed of 180rpm for 20min after dissolving, then filtering, cleaning the crude carbon product with distilled water, and adjusting the pH value of the cru...
Embodiment 2
[0060] Embodiment 2 of the present invention provides a method for purifying carbon in the boneless tissue of a living body. The boneless tissue is selected from flower petals, comprising the following steps:
[0061] a. Put the petals in the container, dry them in isolation from the air until their moisture content is 30%, and then crush them to a particle size of 20 μm to obtain 1000 g of powder;
[0062] b. Put 1000g of powder into a container, add 86.96g of magnesium metal to the powder, then isolate the air, and pass in argon to remove the residual air in the container, heat the mixture to 1200°C, at this temperature Carry out carbonization reaction 2h, remove impurity again, obtain carbon crude product;
[0063] c. Put the crude carbon product into a container, isolate the air, vacuumize, and introduce fluorine gas, then raise the temperature to 2000°C, and roast for 2 hours;
[0064] d. Carrying out elemental analysis on the obtained substance to detect the carbon puri...
Embodiment 3
[0066] Embodiment 3 of the present invention provides the method for purifying the carbon in the boneless tissue of the living body. The boneless tissue is selected from human hair, comprising the following steps:
[0067] a. Put human hair into a container, dry it in isolation from the air until its water content is 27%, then pulverize it to a particle size of 15 μm to obtain 1200g of powder, carry out elemental analysis on the powder, and find out that Contains 20% carbohydrates and proteins;
[0068] b. Put 1200g of powder into the container, add 24.49g of sodium metal to the powder, then isolate the air, and pass through helium to remove the residual air in the container, heat the mixture to 1000°C, at this temperature Carry out carbonization reaction for 1.3h, and then remove impurities to obtain carbon crude product;
[0069] c. Put the crude carbon product in an inner series graphitization furnace, purify it at 3300°C for 1.3h, then add the purified carbon crude produc...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |