Preparation method of porous carbon material for adsorbing malachite green in wastewater

A porous carbon material, malachite green technology, applied in the direction of adsorption water/sewage treatment, chemical instruments and methods, textile industry wastewater treatment, etc.

Inactive Publication Date: 2016-01-20
TIANJIN POLYTECHNIC UNIV
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation of porous carbon materials for adsorption of malachite green in wastewater from wheat husks has not been reported yet.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] Example 1: Dry and crush the wheat husks, mix the crushed wheat husks with potassium hydroxide in a mass ratio of 1:4 (Kg / Kg), react them at 400°C for 0.5 hours, and activate the reaction at 800°C After 1 hour, the solid was filtered, washed, and dried to obtain a porous carbon material. The prepared 0.02g porous carbon is mixed with 20mL malachite green solution of 500mg / L at room temperature, the pH value is adjusted to 6.5, and the adsorption measurement is carried out under the conditions of adsorption time of 200 minutes, and the adsorption amount of malachite green obtained is 453mg / L. g.

Embodiment 2

[0009] Example 2: The activation temperature was changed to 850° C., and the other conditions were the same as in Example 1. The prepared porous carbon had an adsorption capacity of 419 mg / g for malachite green.

Embodiment 3

[0010] Embodiment 3: changing wheat husk and potassium hydroxide are mixed by mass ratio 1: 3 (Kg / Kg), and other conditions are the same as embodiment 1, and the prepared porous carbon is 407mg / g to malachite green adsorption.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
adsorption capacityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of a porous carbon material for adsorbing malachite green in wastewater and particularly relates to a method for preparing the porous carbon material for efficiently adsorbing the malachite green in the wastewater. In the method, wheat husks are taken as raw materials and activation treatment is adopted under certain conditions. The preparation method comprises the specific steps: firstly, drying and crushing the wheat husks, and sufficiently mixing the crushed wheat husks with an activating reagent at a certain mass ratio; and after carrying out the activation treatment under the certain conditions, filtering, washing and drying solids to obtain the porous carbon material. The prepared porous carbon material has the performance of efficiently adsorbing the malachite green. The method has a simple process and the porous carbon material has a good adsorption effect.

Description

technical field [0001] The invention relates to a preparation method of a porous carbon material for absorbing malachite green in wastewater, in particular to a method for preparing porous carbon by chemical activation using wheat husks as a raw material, and using the porous carbon as an adsorbent to remove malachite green in dye wastewater new method. Background technique [0002] In recent years, with the continuous acceleration of industrialization, the problem of environmental pollution has become more and more serious. In the textile printing and dyeing industry, the discharge of dye wastewater is increasing year by year. Dye wastewater has high chroma, complex composition, high toxicity, and toxic substances are easy to accumulate in the environment. Entering water bodies will bring great threats to aquatic organisms and even affect human health. Malachite green is a synthetic toxic trityl compound, which is both a dye and a fungicide, and is widely used as a food c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/20B01J20/30C02F1/28C02F1/58C02F103/30
Inventor 王丽丽廖港杨坤龙逯文启
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap