Anti-pressure wear-resistant corrosion-resistant transformer sealing ring

A technology for transformers and sealing rings, which is applied in the fields of corrosion-resistant transformer sealing rings, wear resistance, and pressure resistance. It can solve problems such as difficulty in meeting the long-term operation needs of transformers, high temperature and corrosion of transformer oil, and short service life of rubber sealing tapes. Good insulation, good plasticity and high hiding power

Inactive Publication Date: 2016-01-20
LUOHE POWER SUPPLY OF HENAN ELECTRIC POWER CORP
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the invention patent with the application number 201010533517.9 authorized on July 4, 2012 provides a method for manufacturing a transformer sealing strip. The interface often breaks due to long-term pressure, and is susceptible to high temperature and corrosion of transformer oil. The service life of ordinary rubber sealing tape is short, which is difficult to meet the long-term operation needs of transformers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A pressure-resistant, wear-resistant and corrosion-resistant transformer sealing ring, made from the following raw materials in proportion by weight: 80 parts of nitrile rubber, 20 parts of carbon black, 35 parts of ceramic micropowder, 10 parts of silicon powder, and 15 parts of manganese powder , 10 parts of high-strength reclaimed rubber, 10 parts of polytetrafluoroethylene, 10 parts of zinc oxide, 10 parts of coumarone resin, 7 parts of rubber oil, 5 parts of clay, 5 parts of vulcanization activator, 1 part of anti-thermal oxygen aging anti-aging agent . Its production method comprises the following steps:

[0013] 1) Blank making: take the nitrile rubber, high-strength reclaimed rubber and coumarone resin of the stated weight parts to synthesize rubber in an internal mixer, and then add other raw materials of the stated weight parts to carry out kneading in an open mill Forming to obtain a ring-shaped blank suitable for the structure of the transformer to be seale...

Embodiment 2

[0018] A pressure-resistant, wear-resistant and corrosion-resistant transformer seal ring, made from the following raw materials in proportion by weight: 85 parts of nitrile rubber, 25 parts of carbon black, 40 parts of ceramic micropowder, 15 parts of silicon powder, and 20 parts of manganese powder 15 parts of high-strength reclaimed rubber, 12 parts of polytetrafluoroethylene, 12 parts of zinc oxide, 12 parts of coumarone resin, 9 parts of rubber oil, 7 parts of clay, 6 parts of vulcanization activator, 3 parts of anti-thermal and oxygen aging anti-aging agent .

[0019] Its production method, with embodiment one.

Embodiment 3

[0021] A pressure-resistant, wear-resistant and corrosion-resistant transformer seal ring, made from the following raw materials in proportion by weight: 88 parts of nitrile rubber, 26 parts of carbon black, 50 parts of ceramic micropowder, 22 parts of silicon powder, and 21 parts of manganese powder 18 parts of high-strength reclaimed rubber, 14 parts of polytetrafluoroethylene, 13 parts of zinc oxide, 12 parts of coumarone resin, 10 parts of rubber oil, 8 parts of clay, 7 parts of vulcanization activator, 4 parts of anti-heat and oxygen aging anti-aging agent .

[0022] Its production method, with embodiment one.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-pressure wear-resistant corrosion-resistant transformer sealing ring. Nitrile rubber is adopted to serve as the main raw material and combined with high-tenacity reclaimed rubber and coumarone resin to form synthetic rubber, and excellent oil resistance, wear resistance and heat resistance are achieved; carbon black, ultrafine ceramic powder, silica powder, manganese powder, polytef, zinc oxide, argil, vulcanizing activators and anti-aging agents capable of being resistant to thermo-oxidative aging serve as auxiliary materials, the properties such as tear resistance, the self-lubricating effect, compressive deformation resistance, heat resistance, corrosion resistance and friction resistance of the sealing ring can be effectively improved, and the service life of the sealing ring can be prolonged. Good sealing effect can be protected under severe cold and hot summer climatic environment, and compared with a traditional sealing ring, the service life is effectively prolonged by over one time.

Description

technical field [0001] The invention relates to the technical field of transformer sealing, in particular to a pressure-resistant, wear-resistant and corrosion-resistant transformer sealing ring. Background technique [0002] Since transformer oil is usually used in the transformer to cool down the temperature of the transformer, the seal between the transformer oil tank and the casing and the transformer cover is very important. Traditional transformer annular rubber seals usually use a strip-shaped sealing rubber row to connect the two The quality of the rubber row and the sealing quality of the rubber row interface directly affect the sealing performance of the transformer. For example, the invention patent with the application number 201010533517.9 authorized on July 4, 2012 provides a method for manufacturing a transformer sealing strip. The interface often breaks due to long-term pressure, and is susceptible to high temperature and corrosion of transformer oil. The se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L17/00C08L27/18C08L45/02C08K3/04C08K3/36C08K3/02C08K3/08C08K3/22C08K3/34
Inventor 智全中陈宏伟曹建奎张亮
Owner LUOHE POWER SUPPLY OF HENAN ELECTRIC POWER CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More