Chlorinated butyl rubber and silicone rubber blended material

A technology of chlorinated butyl rubber and silicone rubber, which is applied in the field of chemical materials and can solve the problems of large skin irritation, easy deformation, and poor air tightness

Inactive Publication Date: 2016-01-20
SHANXI XINHUA CHEM
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the 65, 69, 87, 08, 09 and other generations of gas masks that have been developed in our country mainly use natural rubber in the early stage, which has the problem of poor anti-virus performance, while the butyl rubber used in the later stage is easy to deform and wear. Problems such as poor comfort, low assembly qualification rate, poor air tightness, and large skin irritation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chlorinated butyl rubber and silicone rubber blended material
  • Chlorinated butyl rubber and silicone rubber blended material
  • Chlorinated butyl rubber and silicone rubber blended material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Chlorobutyl rubber and silicone rubber blend materials, comprising the following components by weight:

[0039] Chlorobutyl rubber 85 parts,

[0040] 12 parts of silicone rubber,

[0041] Zhongchao wear-resistant carbon black n22045 parts,

[0042] High wear-resistant carbon black n33030 parts,

[0043] 10 parts of zinc oxide,

[0044] 6 parts of magnesium oxide,

[0045] Accelerator TT5 parts,

[0046] Accelerator ZDC8 parts,

[0047] Vulcanizing agent DCP5 parts,

[0048] 6 parts of stearic acid,

[0049] Antioxidant methylidene 442610 parts,

[0050] Anti-aging agent MB6 parts.

[0051] The mixing process of mixed materials is as follows:

[0052] XK-160mm open rubber mixing machine is used for mixing rubber materials, and the speed ratio of the rollers is 1:1.25. When mixing chlorinated butyl rubber, the temperature of the front roll should be 50-55°C, and the temperature of the rear roll should be slightly higher, preferably 60-62°C. The mixing process ...

Embodiment 2

[0061] Chlorobutyl rubber and silicone rubber blend materials, comprising the following components by weight:

[0062] Chlorobutyl rubber 80 parts,

[0063] 10 parts of silicone rubber,

[0064] Zhongchao wear-resistant carbon black n22030 parts,

[0065] High wear-resistant carbon black n33010 parts,

[0066] 12 parts of zinc oxide,

[0067] Magnesium oxide 1 part,

[0068] Accelerator TT0 part,

[0069] Accelerator ZDC 2 parts,

[0070] Vulcanizing agent DCP6 parts,

[0071] 8 parts of stearic acid,

[0072] Antioxidant methylidene 442612 parts,

[0073] 2 copies of antioxidant MB.

[0074] The preparation method of the blended material is the same as in Example 1.

Embodiment 3

[0076] Chlorobutyl rubber and silicone rubber blend materials, comprising the following components by weight:

[0077] Chlorobutyl rubber 70 parts,

[0078] 5 parts of silicone rubber,

[0079] Zhongchao wear-resistant carbon black n22040 parts,

[0080] High wear-resistant carbon black n33025 parts,

[0081] Zinc oxide 5 parts,

[0082] 8 parts of magnesium oxide,

[0083] Accelerator TT4 parts,

[0084] Accelerator ZDC5 parts,

[0085] Vulcanizing agent DCP8 parts,

[0086] 4 parts stearic acid,

[0087] 44262 parts of antioxidant methylidene,

[0088] Anti-aging agent MB7 parts.

[0089] The preparation method of the blended material is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of chemical materials, in particular to a chlorinated butyl rubber and silicone rubber blended material applied to a body material of a gas mask body. The chlorinated butyl rubber and silicone rubber blended material is prepared from, by weight, 50-100 parts of chlorinated butyl rubber, 5-50 parts of silicon rubber, 30-50 parts of intermediate super abrasion furnace black n220, 20-40 parts of high abrasion furnace black n330, 5-15 parts of zinc oxide, 1-10 parts of magnesium oxide, 0-10 parts of accelerator TT, 2-10 parts of accelerator ZDC, 1-10 parts of vulcanizer DCP, 2-8 parts of stearic acid, 2-12 parts of antioxidant methylene 4426 and 2-10 parts of anti-aging agents MB. The blended material has good gas defense performance, biocompatibility is improved due to the addition of silicon rubber, and the wearing comfort is improved on the premise that the protection performance is ensured.

Description

technical field [0001] The invention relates to the field of chemical materials, in particular to a blended material of chlorinated butyl rubber and silicone rubber applied to the main body material of a gas mask. Background technique [0002] Early gas masks mostly used natural rubber as the cover material. With the development of biotechnology and genetic engineering technology, higher requirements are put forward for the protective performance of gas masks. Therefore, the performance requirements for gas mask cover materials are also increasing. High, countries have adopted synthetic rubber with excellent comprehensive performance as the cover material. At present, the 65, 69, 87, 08, 09 and other generations of gas masks that have been developed in our country mainly use natural rubber in the early stage, which has the problem of poor anti-virus performance, while the butyl rubber used in the later stage is easy to deform and wear. Poor comfort, low assembly pass rate, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L83/04C08K13/02C08K3/04C08K3/22C08K5/372C08K5/39C08K5/09
CPCC08L23/283C08K2201/014C08L83/04C08K13/02C08K3/04C08K2003/2296C08K2003/222C08K5/372C08K5/39C08K5/09
Inventor 齐嘉豪崔江舟王立功金世婧王慧雷小军常慧芳
Owner SHANXI XINHUA CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap