Purification method for carbon in bone-containing tissue of life entity

A purification method and technology of bone tissue, applied in the field of carbon purification, can solve the problem of low carbon purity, achieve the effect of good purification effect, reduce funeral land and save natural resources

Inactive Publication Date: 2016-01-27
刘逸舟
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the present invention provides a method for purifying carbon in bone-containing tissues of living organisms, so as to improve the existing problem of low purity of carbon extracted from bone-containing tissues of living organisms

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Purification method for carbon in bone-containing tissue of life entity
  • Purification method for carbon in bone-containing tissue of life entity
  • Purification method for carbon in bone-containing tissue of life entity

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] figure 1 The method for purifying carbon in the bone-containing tissue of a living body provided by Embodiment 1 of the present invention is shown. The bone-containing tissue is selected from the ashes of all adults, including the following steps:

[0053] a. Grinding the ashes to a particle size of 10 μm to obtain 505 g of powder;

[0054] b. Dissolve the powder in a mixed solution of 50% sulfuric acid solution, 30% nitric acid solution, and 38% hydrochloric acid solution. The volume ratio of sulfuric acid solution, nitric acid solution, and hydrochloric acid solution is 2:1:1. Rotate at 100rpm and react for 30min, then filter, wash the crude carbon with distilled water, and adjust the pH of the crude carbon to 6;

[0055] c. Put the crude carbon product in an inner series graphitization furnace and purify it at 1800°C for 1.2h;

[0056] d. Carry out elemental analysis to the substance obtained in step c, and detect the carbon purity, and the carbon purity is 99.9%. ...

Embodiment 2

[0058] figure 2 The method for purifying carbon in the bone-containing tissue of a living body provided by Embodiment 2 of the present invention is shown. The bone-containing tissue is selected from all ashes of children, and includes the following steps:

[0059] a. Grinding the ashes to a particle size of 20 μm to obtain 350 g of powder;

[0060] b. Dissolve the powder in a sulfuric acid solution with a weight percentage of 60%, heat to 70°C, then pour the resulting mixture into a mixer, process it at a speed of 150rpm for 20min, and then pour out the mixture, with a weight percentage of 5 % potassium hydroxide solution for neutralization reaction, adjust the pH value to 6, filter, and then use distilled water to clean and filter the solid matter, then place the solid matter in a constant temperature drying furnace, and dry it at 110 ° C for 45 minutes to obtain carbon Crude;

[0061] c. Put the crude carbon product into a container, cut off the air, and introduce fluorin...

Embodiment 3

[0065] image 3 The method for purifying carbon in the bone-containing tissue of a living body provided by Embodiment 3 of the present invention is shown. The bone-containing tissue is selected from the ashes of all adults, including the following steps:

[0066] a. Grinding the ashes to a particle size of 18 μm to obtain 500 g of powder;

[0067] b. The powder is dissolved in a 50% by weight phosphoric acid solution, and then the resulting mixture is poured into a blender, processed at a speed of 100rpm for 60min, and then the mixture is poured out, and mixed with 5% by weight of sodium hydroxide The solution undergoes a neutralization reaction, adjusts the pH value to 6, filters, and then uses distilled water to wash and filter the solid matter, then put the solid matter in a constant temperature drying oven, and dry it at 130°C for 30 minutes to obtain a crude carbon product;

[0068] c. Put the crude carbon obtained in an Acheson furnace and purify at 2500°C for 1 hour; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a purification method for carbon in bone-containing tissue of a life entity, and relates to the technical field of carbon purification. The purification method for the carbon in the bone-containing tissue of the life entity comprises the steps of grinding, pickling, further purifying and purity detecting. According to the purification method for the carbon in the bone-containing tissue of the life entity, the carbon can be extracted from the life entity, and the extracted carbon is high in purity and meets the diamond cultivation requirements.

Description

technical field [0001] The invention relates to the technical field of carbon purification, in particular to a method for purifying carbon in bone-containing tissue of a living body. Background technique [0002] The deceased will be cremated, and the ashes after cremation become their only certificate, and also the spiritual sustenance for their family members and friends to remember the deceased. Based on the relatives' consideration for the deceased, in the existing technology, there is an operation of extracting the carbon from the ashes of the deceased obtained after cremation to make diamonds for their loved ones to wear, and then remembering the deceased, realizing spiritually, The wish of the dead to be with them. However, in the extraction operation in the prior art, in order to extract the carbon that meets the purity requirements of diamond cultivation, most of the dead are cremated in a low temperature area, and the cremation is not complete. For their relatives...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B31/02
Inventor 刘逸舟戴乐德王健
Owner 刘逸舟
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com