Anti-skid treatment process of floor tiles

A technology for anti-skid treatment and floor tiles, which is applied in the field of building ceramics, can solve the problems of small friction coefficient and the surface of floor tiles is easy to be slippery, etc., and achieves the effect of easy cleaning and solving wet and slippery in contact with water.

Inactive Publication Date: 2016-01-27
淄博新空间陶瓷有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to solve this problem, many manufacturers in our country generally adopt the method of engraving a concave pattern on the mold, or printing a layer of thick pattern on the surface of the floor tile with screen printing technology. However, due to the glazed surface of the floor tile itself The unique glass property has a small friction coefficient, and it is still slippery especially after encountering water. Therefore, even if there are some uneven patterns on the surface of the floor tiles, it still cannot fundamentally solve the problem that the surface of the floor tiles is easy to be slippery.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-skid treatment process of floor tiles
  • Anti-skid treatment process of floor tiles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Dry glaze formula: 40% quartz powder, 36% potassium feldspar powder, 5% calcite, 5% boric acid, 2% potassium nitrate, 10% barium carbonate, 2% zinc oxide. After the dry glaze of this formula is processed into granules, the percentage of sieves larger than 20 mesh is 3%, 20-40 mesh is 42%, 40-60 mesh is 42%, and 60 mesh is sieved. The above accounted for 13%.

[0026] Add the processed dry glaze to the surface glaze according to the proportion of 20% of the surface glaze, stir evenly, and then apply glaze on the floor tiles of 30cm*30cm according to the glaze amount of 55 grams per tile, the firing temperature is 1150 ° C, and the firing cycle is 40 Minutes, the anti-slip particles on the surface of the fired product are clearly visible, and the hand feel is obvious. After the dirt absorption test, it does not absorb dirt at all, and other physical and chemical indicators fully meet the national standards.

Embodiment 2

[0028] Dry glaze formula: 44% quartz powder, 30% potassium feldspar powder, 5% calcite, 5% boric acid, 2% potassium nitrate, 10% barium carbonate, 4% zinc oxide. After the dry glaze of this formula is processed into granules, the percentage of sieves larger than 20 mesh is 4.5%, 20-40 mesh is 44%, 40-60 mesh is 41%, and 60 mesh is 4.5%. Above the sieve accounted for 10.5%.

[0029] Add the processed dry glaze to the surface glaze according to the proportion of 28% of the surface glaze, stir evenly, and then apply glaze on the floor tiles of 30cm*30cm according to the glaze amount of 48 grams per tile, the firing temperature is 1180 ° C, and the firing cycle is 45 Minutes, the anti-slip particles on the surface of the fired product are dense, clearly visible, and the handle feels obvious. After the dirt absorption test, it does not absorb dirt at all, and other physical and chemical indicators fully meet the national standards.

Embodiment 3

[0031] Dry glaze formula: quartz powder 41%, potassium feldspar powder 36%, calcite 5%, boric acid 5%, potassium nitrate 2%, barium carbonate 9%, zinc oxide 2%. After the dry glaze of this formula is processed into granules, the percentage of sieves larger than 20 mesh is 2%, 20-40 mesh is 35%, 40-60 mesh is 50%, and 60 mesh is sieved. Above the sieve accounted for 13%.

[0032] Add the processed dry glaze to the surface glaze according to the proportion of 12% of the surface glaze, stir evenly, and then apply glaze on the floor tiles of 30cm*30cm according to the glaze amount of 68 grams per tile, the firing temperature is 1120°C, and the firing cycle is 35 Minutes, the non-slip particles on the surface of the fired product are relatively dispersed, the particles are clear and obvious, and the handle has a good protruding effect. After the dirt absorption test, it does not absorb dirt at all, and other physical and chemical indicators fully meet the national standards.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of architectural ceramics, and particularly relates to an anti-skid treatment process of floor tiles. The process comprises the steps that a dry granular glaze is melt into glass granules through a frit furnace, and then grinding is conducted, dry granular glaze powder is obtained and added to a floor tile surface glaze to be evenly stirred; the materials are evenly applied to the surfaces of floor tiles through a glaze applying machine, and the floor tiles are obtained through sintering of a kiln furnace. According to the anti-skid treatment process of the floor tiles, a floor tile surface glaze formula is regulated, and the dry granular glaze is doped into the surface glaze, so that after the floor tile surface glaze is sintered and formed, the dry granular glaze still exists on the glaze surface in a small granular state, when a person steps on the floor tiles, a large number of friction points are increased, and therefore the problem that the floor tile glaze surfaces are wet and slippery when water exists on the floor tiles is thoroughly solved; in addition, according to produced products, attractiveness of an original product is not affected, cleaning is easy, and the produced products completely meet national standards.

Description

technical field [0001] The invention belongs to the technical field of building ceramics, and in particular relates to an anti-slip treatment process for floor tiles. Background technique [0002] At present, there are many companies producing ceramic floor tiles in our country. The rooms decorated with ceramic floor tiles are clean and bright, durable and easy to clean. Therefore, using ceramic floor tiles for decoration has become the first choice for all families. However, a problem is unavoidably encountered in use, that is, because there is often water on the ground in the kitchen and bathroom, people step on it and it is very slippery, and it is easy to fall. Especially the elderly are prone to falls. Every year, many elderly people fall and get injured due to slippery ground. Therefore, producing a kind of non-slip floor tile has just become inevitable trend in the future. In order to solve this problem, many manufacturers in our country generally adopt the method o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/86
Inventor 李峰芝胡温钢
Owner 淄博新空间陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com