Manufacturing method for color glaze coated glass and color glaze coated glass

A technology of coated glass and manufacturing method, applied in glass manufacturing equipment, glass tempering, manufacturing tools and other directions, can solve the problems of poor acid and alkali resistance, poor coating adhesion, short service life, etc., to improve production efficiency and improve tightness The effect of high degree and convenient processing

Active Publication Date: 2016-01-27
XINYI GLASS ENG (DONGGUAN) CO LTD
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the original coated glass has defects such as single color, poor coating adhesion, easy to fall off, and poor acid and alkali resistance, so the service life is short and cannot meet the current requirements for the use of coated glass.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method for color glaze coated glass and color glaze coated glass
  • Manufacturing method for color glaze coated glass and color glaze coated glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0025] Such as figure 1 and figure 2 As shown, the manufacturing method of a kind of colored glaze coated glass provided by the embodiment of the present invention, the manufacturing method comprises:

[0026] Cutting process: first select the original glass sheet 11 to be processed, and cut the original glass sheet 11 according to production requirements (such as requirements for size and shape), so that the original glass sheet 11 meets the requirements for preliminary processing.

[0027] Washing and grinding process: since the original glass sheet 11 is cut, there will be sharp edges. In ord...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the glass manufacturing technology field, and discloses a manufacturing method for color glaze coated glass and color glaze coated glass. The manufacturing method comprises steps: a cutting procedure is carried out, namely, a glass original sheet is selected and cut; a washing and grinding procedure is carried out, namely, the glass original sheet is ground and washed; a printing procedure is carried out, namely, a screen printing plate is selected and washed, printing oil is blended, and a pattern is printed on the surface of the glass original sheet; a toughening procedure is carried out, namely, the surface of the glass original sheet is cleaned, the glass original sheet is conveyed to a toughening furnace and heated, then is outputted after heating and cooled rapidly to a normal temperature, and glaze layer is formed; a coating procedure is carried out, namely, coating layers with different colors are plated on the glaze layer according to needs. The color glaze coated glass is manufactured through the above manufacturing method. The manufacturing method is simple, and the production efficiency is high. The color glaze coated glass manufactured through the method has good acid-base resistance, has a good adhesive force, and is durable and wear-resistant. The color is changeable, the sunshade effect is raised, and usage requirement of the coated glass are met.

Description

technical field [0001] The invention belongs to the technical field of glass manufacturing, and in particular relates to a method for manufacturing colored glaze coated glass and colored glaze coated glass. Background technique [0002] Coated glass is coated with one or more layers of metal, alloy or metal compound films on the surface of the glass to change the optical properties of the glass to meet certain requirements. In today's society, coated glass products have been widely used, such as high-speed rail, car windows, or floor walls. [0003] However, the original coated glass has defects such as single color, poor coating adhesion, easy to fall off, and poor acid and alkali resistance, so the service life is short and cannot meet the current requirements for the use of coated glass. Contents of the invention [0004] The object of the present invention is to overcome the above-mentioned deficiencies in the prior art and provide a method for manufacturing colored g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C17/34C03B27/04
CPCY02P40/57
Inventor 董清世卢业明郭盛斌李明军
Owner XINYI GLASS ENG (DONGGUAN) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com