Bracket for orthodontics and preparation method thereof
A technology for orthodontics and brackets, applied in the field of orthodontic brackets and their preparation, can solve the problems of weak ceramic material strength, color staining and discoloration, affecting treatment results, etc., and achieves excellent mechanical properties and is not easy to discolor.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] A bracket for orthodontics, comprising the following raw materials in parts by mass: 50 parts of alumina powder, 8 parts of carbon fiber, 10 parts of calcium phosphate, 1 part of dispersant, 1 part of plasticizer, and 2 parts of adhesive 1 part, antibacterial agent 1 part. Wherein, the binder is methyl cellulose and vinyl alcohol, and the particle size of the alumina powder is less than 1 μm.
[0023] A kind of preparation method for the bracket for orthodontics described above, comprises the steps:
[0024] (1) According to the mass ratio, mix each raw material at 160-180°C for 1 hour;
[0025] (2) After mixing evenly, carry out injection molding by the mold of bracket;
[0026] (3) Sinter the molded green body by hot isostatic pressing for 6-10 hours, and control the temperature rise of the furnace side wall surface to ≤50°C;
[0027] (4) Grinding and polishing with diamond paste to obtain the bracket for orthodontics.
Embodiment 2
[0029] A bracket for orthodontics, comprising the following raw materials in parts by mass: 56 parts of alumina powder, 9 parts of carbon fiber, 12 parts of calcium phosphate, 1.5 parts of dispersant, 1.4 parts of plasticizer, and 3 parts of adhesive 1 part, antibacterial agent 1 part. Wherein, the binder is vinyl alcohol, and the particle size of the alumina powder is less than 1 μm.
[0030] A kind of preparation method for the bracket for orthodontics described above, comprises the steps:
[0031] (1) According to the mass ratio, mix each raw material at 160-180°C for 1 hour;
[0032] (2) After mixing evenly, carry out injection molding by the mold of bracket;
[0033] (3) Sinter the molded green body by hot isostatic pressing for 6-10 hours, and control the temperature rise of the furnace side wall surface to ≤50°C;
[0034] (4) Grinding and polishing with diamond paste to obtain the bracket for orthodontics.
Embodiment 3
[0036] A bracket for orthodontics, comprising the following raw materials in parts by mass: 64 parts of alumina powder, 11 parts of carbon fiber, 15 parts of calcium phosphate, 2 parts of dispersant, 2 parts of plasticizer, and 4 parts of adhesive 1 part, antibacterial agent 1 part. Wherein, the binder is methyl cellulose and vinyl alcohol, and the particle size of the alumina powder is less than 1 μm.
[0037] A kind of preparation method for the bracket for orthodontics described above, comprises the steps:
[0038] (1) According to the mass ratio, mix each raw material at 160-180°C for 1 hour;
[0039] (2) After mixing evenly, carry out injection molding by the mold of bracket;
[0040] (3) Sinter the molded green body by hot isostatic pressing for 6-10 hours, and control the temperature rise of the furnace side wall surface to ≤50°C;
[0041] (4) Grinding and polishing with diamond paste to obtain the bracket for orthodontics.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap