A kind of high-infrared fast-curing powder coating for coil steel and preparation method thereof

A fast-curing, powder coating technology, applied in powder coatings, polyester coatings, coatings, etc., can solve the problems of poor compatibility between polyester resin and fluorocarbon polyester, improve poor compatibility and save costs , to ensure the effect of cross-linking density

Active Publication Date: 2017-12-22
GUANGZHOU KINTE IND
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the above-mentioned problems in the prior art, the present invention provides a high-infrared fast-curing powder coating for coil steel and its preparation method. By modifying the fluorocarbon resin with polyester resin, it not only improves the compatibility between polyester resin and fluorocarbon polyester In order to solve the problem of poor capacitance, the excellent properties of fluororesin are also fully utilized. Combined with advanced high-infrared curing technology, fluorocarbon-polyester powder coatings with fluorocarbon segments enriched on the surface have been successfully prepared, which greatly improves the coating quality. Excellent weather resistance, acid resistance, alkali resistance, oil resistance and other properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-infrared fast-curing powder coating for coil steel and preparation method thereof
  • A kind of high-infrared fast-curing powder coating for coil steel and preparation method thereof
  • A kind of high-infrared fast-curing powder coating for coil steel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A high-infrared fast-curing powder coating for coil steel, its composition and weight ratio are:

[0042]

[0043]

[0044] Polyester polyester resin parameters (acid value 30-36mgKOH / g, viscosity 3500±500mPa·S)

[0045] Preparation:

[0046] (1) Take polyester resin curing agent, leveling agent, benzoin, filler, pigment by weight, place mixing tank, fully mix and crush, obtain mixed premixed material;

[0047](2) The mixed premixed material is sent to a twin-screw extruder for extrusion, and the extrusion temperature is controlled between 90-120°C;

[0048] (3) The extruded material is compressed by a tablet machine, cooled, crushed, and sieved to obtain a powder coating with a particle size of 30-40um.

[0049] Coating curing process:

[0050] (1) Use the above-mentioned powder coating as an electrostatic spraying model, and the coating thickness is 50mm±10mm.

[0051] (2) Adjust the heating gear of the high-infrared curing instrument to the highest gear, pr...

Embodiment 2

[0053] A high-infrared fast-curing powder coating for coil steel, its composition and weight ratio are:

[0054]

[0055]

[0056] Polyester polyester resin parameters (acid value 30-36mgKOH / g, viscosity 3500±500mPa·S)

[0057] Get above-mentioned each component and make powder coating according to the preparation method of Example 1, then obtain the coating sample that is solidified and molded by this powder coating according to the coating process of Example 1, test the various properties of coating, the results are shown in Table 2 .

Embodiment 3

[0059] A high-infrared fast-curing powder coating for coil steel, its composition and weight ratio are:

[0060]

[0061] Polyester polyester resin parameters (acid value 30-36mgKOH / g, viscosity 3500±500mPa·S)

[0062] Get above-mentioned each component and make powder coating according to the preparation method of Example 1, then obtain the coating sample that is solidified and molded by this powder coating according to the coating process of Example 1, test the various properties of coating, the results are shown in Table 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
viscosityaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-infrared fast-curing powder coating for coil steel, which is prepared from polyester resin, low molecular weight polyester modified fluorocarbon resin, curing agent, leveling agent, benzoin, filler and pigment in parts by weight , the powder coating of the present invention improves the surface condition and performance requirements of the coating by using polyester resin with moderate viscosity and acid value to compound low molecular weight polyester modified fluorocarbon resin, and can be cured by high infrared heating for 15-30s. After curing The powder coating of the invention has good adhesion, and has excellent weather resistance and alkali resistance; the powder coating of the present invention has the characteristics of short curing time, excellent comprehensive performance, etc., and can realize energy saving and environmental protection.

Description

technical field [0001] The invention relates to the technical field of powder coatings, in particular to a high-infrared fast-curing powder coating for steel coils and a preparation method thereof. Background technique [0002] Powder coating is an indispensable process in various fields. One of the processes is the curing of the coating. The curing conditions and curing methods directly affect the film-forming quality of the powder coating in the film-forming process, and the quality of the coating will directly affect the coating quality. Decorative and durable during use. The traditional curing technology adopts hot air baking and gas furnace heating and baking, which has the disadvantages of large equipment footprint, high investment, low efficiency, and high energy consumption. In particular, the quality of baking and curing is generally poor in equipment that has been used for a long time, and the lower end of the workpiece in the furnace is not completely cured, whic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/00C09D5/03C09D7/12C08G63/682
Inventor 丁振刚高庆福杨小华
Owner GUANGZHOU KINTE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com