Ceiba composite fiber and preparing method thereof

A composite fiber and kapok fiber technology, which is applied in textiles, papermaking, yarn, etc., can solve the problems of not being able to play the advantages of various fibers, low spinning tensile strength, and poor spinnability of kapok fiber, etc., to solve the problem of insufficient mechanical strength High, good wear resistance and pressure resistance, good texture effect

Inactive Publication Date: 2016-02-10
刘楚玲
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, kapok fiber has poor spinnability and is difficult to spin purely. Generally, it is blended with cotton, viscose or other cellulose fibers.
[0007] CN201010560000.9 discloses a manufacturing process of kapok fiber blended yarn. The raw materials include kapok fiber and many other fibers. Blended yarn, the process is more complicated, and it is easy to have the problem of low spinning tensile strength, which restricts its application; and CN201310189047.2 and CN201310189256.7 respectively disclose a blended yarn of cotton fiber, bamboo fiber and kapok fiber And a blended yarn of cotton fiber, kapok fiber and acetate fiber, which is only a simple compound of several fibers, and cannot give full play to the advantages of various fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of kapok composite fiber, is made up of the weight parts of following each component:

[0034] 45 parts of polyester fiber, 50 parts of hot-melt fiber, 5 parts of kapok fiber;

[0035] Its preparation method comprises the following steps:

[0036] a. Screening: select high-quality kapok to remove neps, impurities and fiber defects in the fibers;

[0037] b. Mixing: After tearing the raw materials into uniform small pieces, add 10%, 20%, and 50% of the kapok fiber weight into other raw materials in three times, and mix evenly;

[0038] c. Mixing into rolls: the water pumping speed is 500r / min, and the lap roller speed is 20r / min;

[0039] d. Carding into a web: the production quantity is 2g / m, the doffer speed is 10r / min, the Sikkim speed is 400r / min, and the licker-in speed is 600r / min;

[0040] e. Heat treatment: 130°C, keep for 1min, let the fibers fuse together;

[0041] f. cooling.

Embodiment 2

[0043] A kind of kapok composite fiber, is made up of the weight parts of following each component:

[0044] 20 parts of polyester fiber, 20 parts of three-dimensional hollow, 10 parts of hot-melt fiber, 50 parts of kapok fiber;

[0045] Its preparation method comprises the following steps:

[0046] a. Screening: select high-quality kapok to remove neps, impurities and fiber defects in the fibers;

[0047] b. Mixing: After tearing the raw materials into uniform small pieces, add 20%, 40%, and 60% of the kapok fiber weight into other raw materials in three times, and mix evenly;

[0048] c. Mixing into rolls: the water pumping speed is 800r / min, and the lap roller speed is 40r / min;

[0049] d. Carding into a web: the production quantity is 6g / m, the doffer speed is 30r / min, the Sikkim speed is 500r / min, and the licker-in speed is 700r / min;

[0050] e. Heat treatment: 180°C, keep for 3 minutes, let the fibers fuse together;

[0051] f. cooling.

Embodiment 3

[0053] A kind of kapok composite fiber, is made up of the weight parts of following each component:

[0054] 5 parts of hot-melt fiber, 95 parts of kapok fiber;

[0055] Its preparation method comprises the following steps:

[0056] a. Screening: select high-quality kapok to remove neps, impurities and fiber defects in the fibers;

[0057] b. Mixing: After tearing the raw materials into uniform small pieces, add 20%, 40%, and 60% of the kapok fiber weight into other raw materials in three times, and mix evenly;

[0058] c. Mixing into rolls: the water pumping speed is 800r / min, and the lap roller speed is 40r / min

[0059] d. Carding into a web: the production quantity is 6g / m, the doffer speed is 30r / min, the Sikkim speed is 500r / min, and the licker-in speed is 700r / min;

[0060] e. Heat treatment: 135°C, keep for 2 minutes, let the fibers fuse together;

[0061] f. cooling.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a ceiba composite fiber and a preparing method thereof, and belongs to the technical field of textile material production. The ceiba composite fiber is prepared from, by weight, 5 parts to 95 parts of polyester fibers or three-dimensional hollow fibers or hot melting fibers and 5 parts to 95 parts of ceiba fibers. The preparing method includes the steps of screening, mixing, mixing coiling, net combing forming, heating treating, cooling and the like. The ceiba composite fiber has the advantages of being large in tensile strength, good in wear resistance and pressure resistance, good in bulkiness, softness and evenness and the like; the preparing method is simple and convenient in technology, low in yield cost and suitable for industrial production.

Description

technical field [0001] The invention relates to a kapok composite fiber and a preparation method thereof, in particular to a fiber material prepared by compounding kapok fiber and polyester fiber or hollow three-dimensional or hot-melt fiber, belonging to the field of chemical material processing. Background technique [0002] Since the 20th century, chemical fibers have been produced with the development of polymer materials. The advent of chemical fibers has changed the history that humans have only used natural fibers as the only textile fiber raw material for thousands of years, and has opened up broad prospects for obtaining new textile fibers with better performance. In the past two decades, my country's chemical fiber industry has achieved rapid development. According to the data from the official website, my country's chemical fiber output was 104 tons in 1985 and 24.57 million tons in 2007. Since the development of natural fibers is limited by natural conditions, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04
Inventor 刘楚玲
Owner 刘楚玲
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More