Cloth inspecting machine

A cloth inspection machine and surface treatment technology, applied in the field of cloth inspection machine, to achieve excellent abrasion resistance

Inactive Publication Date: 2016-02-24
CHANGSHU NUO XIN DA MACHINERY EQUIP CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the existing cloth inspecting machine, the wear resistance, corrosion resistance, rust resistance, heat resistance, cold resistance and weather resistance of the metal shaft need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A cloth inspection machine, which includes a metal rotating shaft, the metal rotating shaft undergoes surface treatment, and the surface treatment includes the following steps:

[0021] 1) Add 1 to 2 parts by mass of hydroxyethyl cellulose, 0.8 parts by mass of tripotassium citrate, 3.4 parts by mass of phosphoric acid, 0.9 parts by mass of sodium bifluoride, 2.6 parts by mass of phosphine carboxylic acid, and 1.7 parts by mass of 13 parts by mass of deionized water. 3-phenyl-2-propyl acrylate, 2.6 parts by mass of distearyl dimethyl ammonium chloride, stirred and mixed evenly to prepare a surface treatment working solution;

[0022] 2) Raise the temperature of the surface treatment working solution to 54°C;

[0023] 3) Immerse the metal shaft in the surface treatment working solution for 33 minutes, take it out and dry it.

Embodiment 2

[0025] A cloth inspecting machine, which includes a metal shaft, and the metal shaft is subjected to surface treatment, and the surface treatment includes the following steps:

[0026] 1) 1 mass part of hydroxyethyl cellulose, 0.8 mass parts of tripotassium citrate, 3.4 mass parts of phosphoric acid, 0.9 mass parts of sodium bifluoride, 2.6 mass parts of phosphine carboxylic acid, 1.7 mass parts of 3- Phenyl-2-propyl acrylate, 2.6 parts by mass of distearyl dimethyl ammonium chloride, stirred and mixed uniformly to obtain a surface treatment working solution;

[0027] 2) Raise the temperature of the surface treatment working solution to 54°C;

[0028] 3) Immerse the metal shaft in the surface treatment working solution for 33 minutes, take it out and dry it.

Embodiment 3

[0030] A cloth inspecting machine, which includes a metal shaft, and the metal shaft is subjected to surface treatment, and the surface treatment includes the following steps:

[0031] 1) 2 mass parts of hydroxyethyl cellulose, 0.8 mass parts of tripotassium citrate, 3.4 mass parts of phosphoric acid, 0.9 mass parts of sodium bifluoride, 2.6 mass parts of phosphine carboxylic acid, 1.7 mass parts of 3- Phenyl-2-propyl acrylate, 2.6 parts by mass of distearyl dimethyl ammonium chloride, stirred and mixed uniformly to obtain a surface treatment working solution;

[0032] 2) Raise the temperature of the surface treatment working solution to 54°C;

[0033] 3) Immerse the metal shaft in the surface treatment working solution for 33 minutes, take it out and dry it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cloth inspecting machine. The machine comprises a metal rotating shaft which is subjected to surface treatment, wherein the surface treatment comprises the following steps: 1) feeding 1 to 2 parts by mass of hydroxyethyl cellulose, 0.8 part by mass of tripotassium citrate anhydrous, 3.4 parts by mass of phosphoric acid, 0.9 part by mass of sodium hydrogenfluoride, 2.6 parts by mass of phosphono carboxylic acid, 1.7 parts by mass of 3-phenyl-2-propyl acrylate, and 2.6 parts by mass of dimethyl distearyl ammonium chloride to 13 parts by mass of deionized water, and uniformly stirring and mixing to obtain a surface treatment working solution; 2) heating the surface treatment working solution until the temperature is 54 DEG C; 3) soaking the metal rotating shaft in the surface treatment working solution for 33 minutes, and then moving out and drying the metal rotating shaft. According to the cloth inspecting machine, the metal rotating shaft is subjected to surface treatment, so that the cloth inspecting machine is outstanding in friction resistance, corrosion resistance, rustproofing performance, heat resistance, cold resistance and weather resistance.

Description

technical field [0001] The invention relates to a cloth inspecting machine. Background technique [0002] In the existing cloth inspecting machine, the abrasion resistance, corrosion resistance, rust resistance, heat resistance, cold resistance and weather resistance of the metal rotating shaft need to be improved. Contents of the invention [0003] The object of the present invention is to provide a cloth inspecting machine, the metal rotating shaft of which is surface-treated and has excellent abrasion resistance, corrosion resistance, rust resistance, heat resistance, cold resistance and weather resistance. [0004] In order to achieve the above object, the technical solution of the present invention is to design a cloth inspection machine, which includes a metal rotating shaft, and the metal rotating shaft has undergone surface treatment, and the surface treatment includes the following steps: [0005] 1) Add 1 to 2 parts by mass of hydroxyethyl cellulose, 0.8 parts b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C22/36
CPCC23C22/36
Inventor 钱学军
Owner CHANGSHU NUO XIN DA MACHINERY EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com