Stainless steel welding wire and preparation method thereof

A technology of stainless steel and stainless steel strips, applied in welding equipment, welding media, manufacturing tools, etc., can solve the problems of high strength and fatigue resistance, achieve good welding performance, high welding efficiency, and improve high-temperature durability

Inactive Publication Date: 2016-03-09
TIANJIN QINGXINXIANG TECH DEV CO LTD
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a stainless steel welding wire and its preparation method to solve the technical problem that the high strength and fatigue resistance of the stainless steel welding wire in the prior art cannot be combined

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stainless steel welding wire and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] figure 1 A schematic structural view of the stainless steel welding wire and its preparation method provided by the embodiments of the present invention; figure 1 As shown, the stainless steel welding wire provided in this embodiment is composed of a flux core 1 and a stainless steel strip 2 wrapping the flux core 1, and the flux core 1 accounts for 35% of the total weight of the stainless steel welding wire;

[0042] Drug core 1 comprises the following weight ratio components:

[0043] Ti48%~50%, Si10%~13%, Mn10%~12%, KBF 4 10%-12%, Nb5%-7%, Mo5%-6%, Mg3%-4%, N1%-2%, and the rest is Fe.

[0044] In the alternative of the present embodiment, the stainless steel band 2 comprises the following weight ratio components:

[0045] Cr23%~25%, Ni19%~20%, Cu6%~8%, Mg5%~6%, Mo1%~2%, Si0.4%~0.8%, C0.3%~0.5%, Nb0.3% ~0.5%, N0.3%~0.4%, S0.005%~0.01%, P0.005%~0.01%, and the rest is Fe.

[0046] In an alternative solution of this embodiment, the drug core 1 is filled in the stain...

Embodiment 2

[0063] The stainless steel welding wire provided in this embodiment is composed of a flux core 1 and a stainless steel strip 2 wrapping the flux core 1, and the flux core 1 accounts for 30% of the total weight of the stainless steel welding wire;

[0064] Drug core 1 comprises the following weight ratio components:

[0065] Ti45%~48%, SiO 2 13%~15%, Mn12%~14%, KBF 4 12%-13%, Nb5%-8%, Mo5%-7%, MgO4%-5%, N1%-2%, and the rest is Al.

[0066] In the alternative of the present embodiment, the stainless steel band 2 comprises the following weight ratio components:

[0067] Cr22%~23%, Ni18%~19%, Cu5%~6%, Mg5%~6%, Mo2%~3%, Si0.5%~0.8%, C0.3%~0.5%, Nb0.3% ~0.5%, N0.3%~0.4%, S0.005%~0.01%, P0.005%~0.01%, and the rest is Fe.

[0068] In the alternative of this embodiment, the preparation method of drug core 1 includes the following steps:

[0069] Vacuum furnace smelting, forging, drawing, solution heat treatment, continuous drawing, mechanical cleaning;

[0070] During the smeltin...

Embodiment 3

[0081] The stainless steel welding wire provided in this embodiment is composed of a flux core 1 and a stainless steel strip 2 wrapping the flux core 1, and the flux core 1 accounts for 25% of the total weight of the stainless steel welding wire;

[0082] Drug core 1 comprises the following weight ratio components:

[0083] Ti40%~45%, Si13%~15%, Mn13%~14%, KBF 4 12% to 13%, Nb7% to 8%, Mo6% to 7%, Mg4% to 5%, N1% to 2%, and the rest is Al.

[0084] In the alternative of the present embodiment, the stainless steel band 2 comprises the following weight ratio components:

[0085] Cr20%~22%, Ni18%~29%, Cu4%~5%, Mg4%~5%, Mo2%~3%, Si0.4%~0.8%, C0.3%~0.5%, Nb0.3% ~0.5%, N0.3%~0.4%, S0.005%~0.01%, P0.005%~0.01%, and the rest is Fe.

[0086] In the alternative of this embodiment, the preparation method of drug core 1 includes the following steps:

[0087] Vacuum furnace smelting, forging, drawing, solution heat treatment, continuous drawing, mechanical cleaning;

[0088] During th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of welding materials, in particular to a stainless steel welding wire and a preparation method thereof. The stainless steel welding wire consists of a flux core and a stainless steel strip for wrapping the flux core; the flux core accounts for 25-35% of the total weight of the stainless steel welding wire; and the flux core contains the following components in percentage by weight: 40-50% of Ti or TiO2, 10-20% of Si or SiO2, 10-20% of Mn, 10-15% of KBF4, 5-10% of Nb, 5-8% of Mo, 3-5% of Mg or MgO, 1-2% of N, and the balance of Al or Fe. The stainless steel welding wire, provided by the invention, applies a flux-cored wire to melt and weld a particle reinforced composite material, can conveniently adjust the components and the filling rate of wrapped powder according to different welding requirements, and has the advantages of high strength and fatigue resistance.

Description

technical field [0001] The invention relates to the technical field of welding materials, in particular to a stainless steel welding wire and a preparation method thereof. Background technique [0002] Stainless steel welding wire and its preparation method can be divided into stainless steel solid welding wire and stainless steel flux cored welding wire, among which stainless steel flux cored welding wire can be used for welding stainless steel easily and efficiently like carbon steel and low alloy steel flux cored welding wire, stainless steel flux cored welding wire The application of welding wire is mainly based on MAG welding. Compared with manual welding, it can increase the deposition speed; it has a wide range of adaptation to current and voltage, and it is easier to set welding conditions, and it is easy to perform semi-automatic and automatic welding. It has extremely important application value and broad application prospects in the fields of electrical appliances...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23K35/16B23K35/30B23K35/368B23K35/40
CPCB23K35/0266B23K35/0277B23K35/3053B23K35/368B23K35/40
Inventor 于乾坤
Owner TIANJIN QINGXINXIANG TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap