Plugging-resistant freeze-resistant pervious concrete pavement brick and manufacturing method

A technology of permeable concrete and its production method, which is applied in the field of civil engineering, can solve the problems of reduced strength of pavement bricks, reduced permeability of permeable concrete, and clogged pores, and achieve the effect of improving the overall strength

Inactive Publication Date: 2016-03-09
SHANDONG UNIV
View PDF6 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the large amount of suspended particles (such as silt, debris, etc.) contained in the surface runoff generated by rainfall, these mineral or organic fine particles will continue to enter the pores of the permeable pavement with the water flow, causing the pores to be blocked and the permeability of the permeable concrete to decrease continuously, resulting in It is difficult for permeable pavement to perform its drainage function, and eventually it evolves into a non-permeable pavement, which shortens its service life and increases the possibility of urban flooding and freeze-thaw disasters
[0003] At the same time, due to the large amount of rain and snow in winter in northern my country, the pavement bricks contain more pores. In the case of repeated freezing and thawing in winter, the strength of the pavement bricks will be reduced or even damaged.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Plugging-resistant freeze-resistant pervious concrete pavement brick and manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Embodiment 1: An anti-clogging and frost-resistant permeable concrete pavement brick, including an anti-clogging surface layer 1 and a base layer 2, and the anti-clogging surface layer 1 is located above the base layer 2;

[0045] The material components and proportions of the surface layer are: cement 80kg, coarse sand 310kg, silica fume 7kg, VAE emulsion 6kg, water 25kg, water reducer 0.8kg;

[0046] The material components and ratio of the base layer are: 90kg of cement, 220kg of gravel, 70kg of coarse sand, 8kg of silica fume, 8kg of VAE emulsion, 0.1kg of polyethylene fiber, 25kg of water and 0.8kg of water reducer.

[0047] The making method of above-mentioned pavement brick is:

[0048] A. Make base material in advance: mix water, water reducing agent and VAE emulsion to form a mixed aqueous solution, and set aside; put stones, coarse sand and polyethylene fiber into the mixer and stir for 20 seconds, add 1 / 3 of the mixed aqueous solution, and stir for 10 seconds...

Embodiment 2

[0056] Embodiment 2: An anti-clogging and frost-resistant permeable concrete pavement brick, including an anti-clogging surface layer 1 and a base layer 2, and the anti-clogging surface layer 1 is located above the base layer 2;

[0057] The material components and proportions of the surface layer are: 100kg of cement, 360kg of coarse sand, 11kg of silica fume, 10kg of VAE emulsion, 35kg of water, and 1.2kg of water reducing agent;

[0058] The material components and ratio of the base layer are: 110kg of cement, 260kg of gravel, 110kg of coarse sand, 12kg of silica fume, 12kg of VAE emulsion, 0.4kg of polyethylene fiber, 35kg of water and 1.2kg of water reducer.

[0059] The making method of above-mentioned pavement brick is:

[0060] A. Make base material in advance: mix water, water reducing agent and VAE emulsion to form a mixed aqueous solution, and set aside; put stones, coarse sand and polyethylene fiber into the mixer and stir for 40 seconds, add 1 / 3 of the mixed aqueo...

Embodiment 3

[0067] Embodiment 3: An anti-clogging and frost-resistant permeable concrete pavement brick, including an anti-clogging surface layer 1 and a base layer 2, and the anti-clogging surface layer 1 is located above the base layer 2;

[0068] The material components and proportions of the surface layer are: cement 85kg, coarse sand 320kg, silica fume 8kg, VAE emulsion 7kg, water 27kg and water reducing agent 0.9kg;

[0069] The material components and ratio of the base layer are: 95kg of cement, 230kg of gravel, 80kg of coarse sand, 9kg of silica fume, 9kg of VAE emulsion, 0.2kg of polyethylene fiber, 27kg of water and 0.9kg of water reducer.

[0070] The making method of above-mentioned pavement brick is:

[0071] A. Make base material in advance: mix water, water reducing agent and VAE emulsion to form a mixed aqueous solution, and set aside; put stones, coarse sand and polyethylene fiber into the mixer and stir for 20 seconds, add 1 / 3 of the mixed aqueous solution, and stir for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a plugging-resistant freeze-resistant pervious concrete pavement brick. The plugging-resistant freeze-resistant pervious concrete pavement brick mainly comprises a plugging-resistant surface layer and a base layer, wherein the plugging-resistant surface layer is positioned on the base layer and consists of the following materials components in a compounding ratio and in parts by weight: 80-100 parts of cement, 310-360 parts of coarse sand, 7-11 parts of silica fume, 6-10 parts of VAE emulsion, 25-35 parts of water and 0.8-1.2 parts of a water reducing agent; the base layer consists of the following material components in the compounding ratio and in parts by weight: 90-110 parts of cement, 220-260 parts of pebbles, 70-110 parts of coarse sand, 8-12 parts of silica fume, 8-12 parts of VAE emulsion, 0.1-0.4 of polyethylene fibers, 25-35 parts of water and 0.8-1.2 parts of a water reducing agent. New material components are designed, so that the concrete brick provided by the invention has good pervious freeze-thaw resistant effects and is not easy to plug.

Description

technical field [0001] The invention relates to the technical field related to civil engineering, in particular to an anti-clogging, frost-resistant and permeable concrete pavement brick and a manufacturing method thereof. Background technique [0002] Permeable paving bricks originated in the Netherlands and have been applied in the United States and Japan at the same time. There are a large number of penetrating pores inside the coarse aggregate skeleton of the pavement brick, which makes the pavement have good water permeability, and can quickly allow a large amount of rainwater to seep into the ground, thereby effectively reducing or eliminating urban rainstorm and flood disasters. However, due to the large amount of suspended particles (such as silt, debris, etc.) contained in the surface runoff generated by rainfall, these mineral or organic fine particles will continue to enter the pores of the permeable pavement with the water flow, causing the pores to be blocked an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): E01C5/06E01C11/22C04B38/00C04B28/04C04B18/14C04B24/26C04B111/76
CPCC04B28/04C04B2111/00284C04B2111/76E01C5/065E01C11/225C04B14/06C04B18/146C04B24/2623C04B2103/302C04B38/00C04B20/0076C04B16/0625Y02W30/91
Inventor 张炯崔新壮卞辉王慧李莉黄丹汤潍泽
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap