Novel active carbon, and preparation method and applications thereof

A kind of activated carbon, a new technology, applied in the field of new activated carbon and its preparation, can solve the problems of immature technology and achieve the effect of reducing pollution

Inactive Publication Date: 2016-03-16
承德虹亚活性炭有限责任公司
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing activated carbon preparation method using waste materials is not mature, and the activated carbon is used to manufacture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel active carbon, and preparation method and applications thereof
  • Novel active carbon, and preparation method and applications thereof
  • Novel active carbon, and preparation method and applications thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A preparation method of a novel activated carbon material, comprising the following preparation steps:

[0035] 1) 1) Selection of coconut shell raw materials: Put the coconut shells into the rolling sieve, and use the rolling sieve to remove sand and dust to obtain the coconut shell raw materials:

[0036] 2) Carbonization of raw materials: put the coconut shell raw material obtained in step 1) into a carbonization and activation integrated kiln, the carbonization and activation integrated kiln includes a carbonization section and an activation section, and the coconut shell raw material is calcined at a high temperature of 400°C to obtain a carbonized material ;

[0037] 3) Activation of the carbonization material: the carbonization material obtained in step 2) enters the activation section of the carbonization and activation integrated kiln, and high-pressure steam is passed into the carbonization and activation integrated kiln, and the activation is performed at a t...

Embodiment 2

[0043] A preparation method of a novel activated carbon material, comprising the following preparation steps:

[0044] 1) Selection of coconut shell raw materials: Put the coconut shells into the rolling sieve, and use the rolling sieve to remove sand and dust to obtain the coconut shell raw materials:

[0045] 2) Carbonization of raw materials: put the coconut shell raw material obtained in step 1) into a carbonization and activation integrated kiln, the carbonization and activation integrated kiln includes a carbonization section and an activation section, and the coconut shell raw material is calcined at a high temperature of 450° C. to obtain a carbonized material ;

[0046] 3) Activation of carbonized material: the carbonized material obtained in step 2) enters the activation section of the integrated carbonization and activation kiln, and high-pressure steam is passed into the integrated carbonization and activation kiln, and the temperature is kept at 890°C for activati...

Embodiment 3

[0052] A preparation method of a novel activated carbon material, comprising the following preparation steps:

[0053] 1) Selection of coconut shell raw materials: Put the coconut shells into the rolling sieve, and use the rolling sieve to remove sand and dust to obtain the coconut shell raw materials:

[0054] 2) Carbonization of raw materials: put the coconut shell raw material obtained in step 1) into a carbonization and activation integrated kiln, the carbonization and activation integrated kiln includes a carbonization section and an activation section, and the coconut shell raw material is calcined at a high temperature of 500°C to obtain carbonized material ;

[0055] 3) Activation of carbonized material: the carbonized material obtained in step 2) enters the activation section of the integrated carbonization and activation kiln, and high-pressure steam is passed into the integrated carbonization and activation kiln, and the temperature is kept at 950°C for activation t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a novel active carbon, and a preparation method and applications thereof. The preparation method comprises following steps: 1) careful selection of a coconut shell raw material; 2) carbonization of an obtained raw material; 3) activation of a carbonization production; 4) smashing and sieving of an obtained activation product; 5) water washing or acid washing; and 6) subpackaging. High quality coconut shell is taken as a raw material; and the novel active carbon is obtained via deep activation and a unique technology, and is capable of removing gaseous pollutants and harmful repugnant substances in the indoor air, reducing pollution, and purifying the air. The novel active carbon can be applied to the field of toys for children, and can be used for filtering the air so as to avoid microorganism breeding and infectious diseases, maintaining the freshness of the air around children, improving immunity of infants and young children, helping infants and young children fall asleep, and avoiding skin itch and eczema.

Description

technical field [0001] The invention relates to the field of activated carbon production, in particular to a novel activated carbon and its preparation method and application. Background technique [0002] There are a large number of micropores invisible to the naked eye in activated carbon materials. The micropores in 1 gram of activated carbon materials can reach a surface area of ​​800-3000 square meters after being expanded, and even higher for special purposes. It is these highly developed pore structures like human capillaries that enable activated carbon to have excellent adsorption properties. The existing activated carbon preparation method using waste materials is not mature, and the activated carbon is used to manufacture Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a new type of activated carbon preparation method, which has a simple preparation process and easy material selection, and uses waste ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01B31/10A63H3/02A61N5/06C01B32/336
CPCA63H3/02A61N5/0613A61N2005/066C01P2006/12
Inventor 方桂兰
Owner 承德虹亚活性炭有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com