A kind of method of recycling permanent magnet ferrite waste
A technology for recycling permanent ferrite and waste materials, which is applied in the direction of magnetism of inorganic materials, can solve problems such as inhomogeneous particle size distribution of slurry for molding, large particle size dispersion of grinding materials, and decreased mechanical strength, etc. Excellent mechanical strength, low cost, and good consistency of magnetic properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example
[0057] Examples 1 to 5
[0058] Prepare some pre-sintered materials for Y30H-2, and use jaw crusher, tubular crusher or vibrating crusher to further finely smash the waste magnetic tiles of Y30H-2 to an average particle size similar to the pre-sintered material. , that is, after 2 to 5 μm, it will be used later, and the grinding material falling off during rough grinding of the Y30H-2 product will be used after magnetic separation and impurity removal treatment.
[0059] The addition amount of the main and auxiliary materials is carried out according to Table 5, and 0.5% of sorbitol is added as a dispersant according to the mass fraction. When the material is 0.8μm±0.01μm, the material is discharged. After the material is discharged, the moisture content of the slurry is controlled at 40%, and it is formed by wet magnetic field pressing with Yibin Dazheng Electron 100T automatic press. The forming pressure is 4.5MPa, and the pressure holding time is 6 seconds. The magnetizing...
Example Embodiment
[0072] The load-bearing test curve of the product obtained in Example 1 is as follows figure 2 shown.
[0073] The ultimate bearing load of the product obtained in Example 1 is 286kgf.
Example
[0074] Comparative Examples 1 to 4
[0075] Prepare some rough grinding materials that are not removed and set aside for use. In addition, the main and auxiliary materials are implemented according to Table 5, and the rest are implemented according to Implementation 1. The obtained products, the typical data of parameters such as qualified rate, product magnetic properties, porosity and load bearing limit are shown in Table 6.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap