Environment-friendly water-based antirust liquid formula and application thereof

An anti-rust liquid and environment-friendly technology, applied in the field of metal surface treatment, can solve the problems of high cost, increase the use cost, increase the use concentration, etc., and achieve the effects of low cost, good film-forming effect and simple preparation method.

Inactive Publication Date: 2016-04-06
SUZHOU GAIDE FINE MATERIALS CO LTD
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the domestic water-based anti-rust liquid has the following problems: (1) The anti-rust effect in the typical stock environment is not ideal
Although there are many normal-temperature water-based anti-rust liquids in China, most steel mills generally heat the water-based anti-rust liquid to 50-70°C for immersion in order to improve the anti-rust effect when dipping ferrous metals. Coating, time-consuming and energy-consuming; (4) Higher cost
The anti-rust effect of the existing water-based anti-rust liquid is not ideal, and the manufacturer will recommend increasing the concentration to achieve the desired purpose, which increases the cost of use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A formulation of an environment-friendly water-based antirust solution, in parts by weight, comprising the following components:

[0034] 10 parts of phytic acid, 10 parts of konjac gum,

[0035] 3 parts of a-D-glucose pentaacetate,

[0036] 0.5 parts of carboxymethyl cellulose, 2 parts of sodium alginate,

[0037] 5 parts of sebacic acid, 1 part of triethanolamine,

[0038] 30 parts of deionized water, 1 part of antioxidant.

[0039] Its preparation method comprises the following steps:

[0040] (1) Mix and stir phytic acid, sodium alginate, sebacic acid and deionized water evenly to obtain a mixed solution;

[0041] (2) Warm up the mixed solution obtained in step (1) to 40°C, add konjac gum, carboxymethyl cellulose, and triethanolamine, ultrasonicate for 30 minutes at a power of 400W, continue to heat up to 70°C, add a-D-glucose five Acetate, anti-oxidant, stir evenly, get environment-friendly water-based anti-rust liquid.

Embodiment 2

[0043] A formulation of an environment-friendly water-based antirust solution, in parts by weight, comprising the following components:

[0044] 20 parts of phytic acid, 15 parts of konjac gum,

[0045] 12 parts of a-D-glucose pentaacetate,

[0046] 5.5 parts of carboxymethyl cellulose, 5 parts of sodium alginate,

[0047] 15 parts of sebacic acid, 5 parts of triethanolamine,

[0048] 80 parts of deionized water, 2 parts of antioxidant.

[0049] Its preparation method comprises the following steps:

[0050] (1) Mix and stir phytic acid, sodium alginate, sebacic acid and deionized water evenly to obtain a mixed solution;

[0051] (2) Warm up the mixed solution obtained in step (1) to 50°C, add konjac gum, carboxymethyl cellulose, and triethanolamine, ultrasonicate for 60 minutes at a power of 1000W, continue to heat up to 80°C, add a-D-glucose five Acetate, anti-oxidant, stir evenly, get environment-friendly water-based anti-rust liquid.

Embodiment 3

[0053] A formulation of an environment-friendly water-based antirust solution, in parts by weight, comprising the following components:

[0054] 12 parts of phytic acid, 11 parts of konjac gum,

[0055] 5 parts of a-D-glucose pentaacetate,

[0056] 1 part of carboxymethyl cellulose, 3 parts of sodium alginate,

[0057] 7 parts of sebacic acid, 2 parts of triethanolamine,

[0058] 40 parts of deionized water, 1.2 parts of antioxidant.

[0059] Its preparation method comprises the following steps:

[0060] (1) Mix and stir phytic acid, sodium alginate, sebacic acid and deionized water evenly to obtain a mixed solution;

[0061] (2) Warm up the mixed solution obtained in step (1) to 45°C, add konjac gum, carboxymethyl cellulose, and triethanolamine, ultrasonicate for 40 minutes at a power of 500W, continue to heat up to 75°C, add a-D-glucose five Acetate, anti-oxidant, stir evenly, get environment-friendly water-based anti-rust liquid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly water-based antirust liquid formula. The formula includes, by weight, 10-20 parts of phytic acid, 10-15 parts of konjac glucomannan, 3-12 parts of a-D-glucose pentaacetate, 0.5-5.5 parts of carboxymethyl cellulose, 2-5 parts of sodium alginate, 5-15 parts of sebacic acid, 1-5 parts of triethanolamine, 30-80 parts of deionized water and 1-2 parts of antioxidant. An antirust liquid preparing method is simple, the antirust effect is good, good rust prevention can be achieved at low concentration, no toxin exists, the antirust liquid is harmless to the human body and the environment, and the environment-friendly water-based antirust liquid formula can be applied to rust prevention in high-temperature and high-humidity environments for ethyl HT300 cast iron of hot-rolled steel plates and cold-rolled steel plates.

Description

Technical field: [0001] The invention relates to the technical field of metal surface treatment, in particular to an environment-friendly water-based antirust liquid formula. Background technique: [0002] In 2013, China's crude steel output reached 779 million tons, accounting for 48.5% of the global total. However, about 10 million tons of steel are scrapped due to corrosion every year in my country. Therefore, it is extremely important to develop environmentally friendly and efficient steel antirust products. Among many anti-rust products, water-based anti-rust liquid has attracted wide attention due to its non-toxic and environmentally friendly advantages of using solvent water instead of solvent oil. [0003] Water-based antirust agent is made of water as a solvent, adding various water-soluble corrosion inhibitors, chelating agents, film-forming agents, surfactants, stabilizers, defoamers, bactericides, etc., which can inhibit the chemical corrosion of metal products. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23F11/10
CPCC23F11/10
Inventor 李晓明
Owner SUZHOU GAIDE FINE MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products