Alginate cotton ball

A technology of alginate and alginate fiber, which is applied in medical science, bandages, absorbent pads, etc. It can solve the problems of difficult to meet the preparation requirements of balls, hard and brittle alginate fibers, and difficulty in forming strips, and achieve easy Take it out, stop bleeding quickly, and promote wound healing

Active Publication Date: 2016-04-20
厦门百美特生物材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, alginate fibers are hard and brittle, with poor cohesion, and it is difficult to card into slivers by pure spinning, and it is difficult to meet the preparation requirements of balls

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1: the preparation of alginate cotton ball

[0015] Alginate fiber 25% by mass, absorbent cotton fiber 75% by mass, and alginate cotton balls were prepared through opening, carding, sliver making, and ball making. It is used for tooth extraction to stop bleeding, and the pressure to stop bleeding only takes 6 minutes, which is better than cotton balls.

Embodiment 2

[0016] Embodiment 2: the preparation of alginate cotton ball

[0017] Alginate fiber 50% by mass, absorbent cotton fiber 50% by mass, and alginate cotton balls were prepared through opening, carding, sliver making, ball making and the like. It is used for tooth extraction to stop bleeding, and the pressure to stop bleeding only takes 3 minutes, which is better than cotton balls.

Embodiment 3

[0018] Embodiment 3: the preparation of alginate cotton ball

[0019] Alginate fiber 75% by mass, absorbent cotton fiber 25% by mass, and alginate cotton balls were prepared through opening, carding, sliver making, ball making and the like. For tooth extraction hemostasis surgery, the compression hemostasis time only takes 90 seconds, which is better than cotton balls.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an alginate cotton ball. The alginate cotton ball is prepared from the production technologies that degreasing cotton fiber and alginate fiber are mixed, and opening, carding, strip manufacturing and ball manufacturing are performed. The medical dressing combining absorbent ball usability and alginate dressing functionality is obtained, and is particularly applicable to tooth extraction hemostasis.

Description

technical field [0001] The invention relates to a medical dressing, in particular to an alginate cotton ball. Background technique [0002] The alginate dressing made of alginate fiber has the characteristics of high water absorption, easy gelation, and the release of calcium / zinc ions to promote blood coagulation, so it has the effects of rapid hemostasis, protection of nerve endings, pain relief, anti-adhesion, and promotion of wound healing , is an excellent modern new dressing, which is being paid more and more attention and popularized. [0003] At present, the most convenient and most commonly used method for tooth extraction hemostasis is to use cotton balls made of absorbent cotton fibers to stop bleeding. Patients need to compress for more than 40 minutes to effectively stop bleeding, which takes a long time and causes intense pain. A small number of patients with thrombocytopenia use gelatin sponge dressings for hemostasis after tooth extraction. The hemostatic ef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/40A61L15/44
CPCA61L15/40A61L15/44A61L2300/232A61L2300/418
Inventor 刘松林邱冬刘澄胜林丽雯蓝煌琴吴晓玲黄福龙
Owner 厦门百美特生物材料科技有限公司