A kind of plant fiber reinforced bio-based thermosetting resin composite material

A technology of resin composite material and plant fiber, which is applied in the field of plant fiber reinforced bio-based thermosetting resin composite material and its preparation, can solve the problems of environmental pollution and high price, and achieve the improvement of bending strength and flexural modulus, good bending strength, Effect of improving flexural strength and flexural modulus

Active Publication Date: 2018-01-12
FUJIAN AGRI & FORESTRY UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a plant fiber reinforced bio-based thermosetting resin composite material and its preparation method to solve the problems of using a large amount of expensive petroleum-based resin raw materials and the release of toxic substances during the preparation process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of plant fiber reinforced bio-based thermosetting resin composite material
  • A kind of plant fiber reinforced bio-based thermosetting resin composite material
  • A kind of plant fiber reinforced bio-based thermosetting resin composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Raw materials: raw bamboo fiber (average length 22.81 mm, average width 150 μm), purchased from Fujian Haibosi Chemical Technology Co., Ltd.; acrylate epoxy soybean oil (AESO) (model: F03; viscosity (23°C): 8000~20000 cps; acid value: ≤12 mgKOH / g), purchased from Jiangsu Litian Technology Co., Ltd.; isosorbide, methacrylic anhydride (MAA) and tert-butyl peroxybenzoate (TBPB) were purchased from Sigma-Aldrich (Shanghai) Trading Co., Ltd.

[0043] The preparation method of bamboo fiber reinforced bio-based thermosetting resin composite material comprises the following steps:

[0044] (1) Synthesis process of isosorbide methacrylate (IM): put isosorbide in a round bottom flask, then add MAA and 4-dimethylaminopyridine, wherein the molar ratio of MAA to isosorbide is 3 : The consumption of 1,4-dimethylaminopyridine is 5% of the amount of isosorbide substance; the flask is placed in an ultrasonic water bath, magnetically stirred at 500 rpm, 60°C for 12h, and the ultrasonic ...

Embodiment 2

[0049] Raw materials: bamboo fiber (average length 22.81 mm, average width 150 μm), purchased from Fujian Haibosi Chemical Technology Co., Ltd.; acrylate epoxy soybean oil (AESO) (model: F03; viscosity (23 ℃): 8000~20000 cps; acid value: ≤12 mgKOH / g), purchased from Jiangsu Litian Technology Co., Ltd.; isosorbide, methacrylic anhydride (MAA) and tert-butyl peroxybenzoate (TBPB) were purchased from Sigma-Aldrich (Shanghai) Trading Co., Ltd.

[0050] The preparation method of bamboo fiber reinforced modified bio-based thermosetting resin composite material comprises the following steps:

[0051] (1) Synthesis process of modified bio-based thermosetting resin: put isosorbide in a round bottom flask, then add MAA and 4-dimethylaminopyridine, wherein the molar ratio of MAA to isosorbide is 3:1,4 - The amount of dimethylaminopyridine is 5% of the amount of isosorbide; the flask is placed in an ultrasonic water bath, magnetically stirred at 500 rpm, 60 °C for 12 h, and the ultrasoni...

Embodiment 3

[0055] Raw materials: hemp fiber (average length 22.81 mm, average width 150 μm), purchased from Fujian Haibosi Chemical Technology Co., Ltd.; acrylate epoxy soybean oil (AESO) (model: F03; viscosity (23°C): 8000~20000 cps; acid value: ≤12 mgKOH / g), purchased from Jiangsu Litian Technology Co., Ltd.; isosorbide, methacrylic anhydride (MAA) and tert-butyl peroxybenzoate (TBPB) were purchased from Sigma-Aldrich (Shanghai) Trading Co., Ltd.

[0056] The preparation method of the hemp fiber reinforced bio-based thermosetting resin composite material comprises the following steps:

[0057](1) Synthesis process of isosorbide methacrylate (IM): put isosorbide in a round bottom flask, then add MAA and 4-dimethylaminopyridine, wherein the molar ratio of MAA to isosorbide is 3 : The consumption of 1,4-dimethylaminopyridine is 5% of the amount of isosorbide substance; the flask is placed in an ultrasonic water bath, magnetically stirred at 500 rpm, 60°C for 12h, and the ultrasonic power...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
bending strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a plant fiber reinforced bio-based thermosetting resin composite and a preparation method thereof. Bio-based reactive solvent iosorbide-methacrylate is blended with acrylated epoxidized soybean oil to prepare bio-based thermosetting resin, and plant fibers, the bio-based thermosetting resin and an initiator are subjected to thermo-compression formation to obtain the plant fiber reinforced bio-based thermosetting resin composite. The plant fiber reinforced bio-based thermosetting resin composite and a plant fiber reinforced modified bio-based thermosetting resin composite prepared by the method have good bending strength, bending modulus and bending strain performance.

Description

technical field [0001] The invention belongs to the technical field of natural plant fiber-reinforced resin composite materials, and in particular relates to a plant fiber-reinforced bio-based thermosetting resin composite material and a preparation method thereof. Background technique [0002] In natural plant fiber reinforced polymer composites, the most commonly used thermosetting resins are epoxy resins, phenolic resins and unsaturated polyester resins. Generally, these thermosetting resins have good mechanical properties, chemical corrosion resistance and process performance, but the environmental and air pollution problems caused by the volatilization of added toxic substances (such as formaldehyde, styrene, etc.) during use has attracted great attention. In addition, the continuous depletion of petroleum resources has forced people to seek and develop new renewable bio-based resins. Acrylate Epoxidized Soybean Oil (AESO) is obtained by reacting soybean oil with acry...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L97/02C08L91/00C08K5/103
CPCC08L91/00C08L97/02C08K5/103
Inventor 邱仁辉刘文地谢天顺陈涵林华忠支伟班阳吴锐张伟
Owner FUJIAN AGRI & FORESTRY UNIV