Crystallizer casting powder for continuous casting of titanium-containing steel

A mold powder and continuous casting technology, which is applied in the field of continuous casting mold powder, can solve the problems of deteriorating the lubricating performance of mold powder, unfavorable for separation of slag and steel, and increasing the viscosity of mold powder, and achieves coordinated improvement effect and performance. It is not easy, and the effect of improving the properties of glass

Inactive Publication Date: 2016-06-08
TANGSHAN XINYANCHANG TECH CO LTD
View PDF8 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent 200710193114.2 discloses "Continuous Casting Mold Flux and Its Production Process for Titanium Slab Stainless Steel". In the invention, Fe 2 o 3 The content is ≤3%, by adding a certain amount of Fe 2 o 3 Can effectively weaken SiO 2 Reactive with Al and Ti in the steel, it can effectively reduce the surface defects of the slab, and the production rate is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Crystallizer casting powder for continuous casting of titanium-containing steel

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0017] The preparation method of the above-mentioned mold powder for continuous casting of titanium-containing steel comprises the following steps:

[0018] 1) Using fluorite, calcite, cement clinker, barium carbonate, quartz sand, cooked bauxite, lithium carbonate, boric anhydride, manganese trioxide and carbonaceous materials as raw materials, according to the composition and quality of the mold powder Sub-content, calculate the amount of each raw material, and weigh each raw material according to the calculated amount;

[0019] 2) Mix the fluorite, calcite, cement clinker, barium carbonate, quartz sand, cooked bauxite, lithium carbonate and boric anhydride weighed in step 1), and put them in a submerged arc furnace at 1350°C-1450°C to keep warm 30~40 minutes, so that the raw materials are melted evenly, and then cooled naturally to obtain the premelt;

[0020] 3) Crushing and grinding the premelted material obtained in step 2) so that the particle size of the ground premel...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides crystallizer casting powder for continuous casting of titanium-containing steel. The casting powder comprises, by weight, 5-35% of CaO1, 7-15% of SiO2, 10-30% of Al2O3, 3-15% of F-, 3-10% of Li2O, 5-20% of BaO5, 5-20% of Mn2O3, 2-12% of C, MgO with the amount smaller than or equal to 1.5% and Fe2O3 with the amount smaller than or equal to 2%. The melting point of the casting powder for continuous casting ranges from 960 DEG C to 1200 DEG C and 1300 DEG C, and viscosity ranges from 0.08 Pa.s to 0.18 Pa.s. Compared with a traditional slag system, the content of SiO2 is lower, and the content of Al2O3 is higher. Meanwhile, a certain amount of Mn2O3 is matched to serve as a strong oxidant, harm of interface solid coagulation of steel slag in a crystallizer in the continuous casting process of the titanium-containing steel is effectively eliminated or relieved, relative stability of performance of the casting powder is maintained, the number of continuous casting is increased, surface quality of casting blanks is improved, and the surface coping amount of the casting blanks is reduced.

Description

technical field [0001] The invention belongs to the technical field of mold powder for continuous casting, and in particular relates to mold powder for continuous casting of titanium-containing steel. Background technique [0002] During the titanium-containing casting process, due to the high content of aluminum, titanium, and nitrogen in molten steel, a large amount of TiN can be precipitated at the casting temperature and float to the steel slag interface, and SiO 2 At the same time, the components in the slag react with [Al] and [Ti] in the molten steel to increase the basicity of the slag system, and produce perovskite and other high melting point substances that are mixed with the steel slag and form at the steel slag interface in the crystallizer. Solid condensation leads to changes in the composition and performance of mold slag, and also hinders the normal supply of mold slag liquid slag. These factors are likely to cause problems such as breakouts, slag inclusions,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22D11/111
CPCB22D11/111
Inventor 李平王谦何生平陈卓
Owner TANGSHAN XINYANCHANG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap