Anion composite powder suitable for building materials

A technology of composite powder and negative ions, which is applied in the field of composite powders, can solve the problems of low concentration of negative ions and poor efficacy and durability, and achieve the effects of low price, air purification and indoor odor elimination

Pending Publication Date: 2016-06-08
ZHUO DA NEW MATERIAL TECH GRP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] CN103805134A Chinese patent discloses a novel anion additive, the shortcoming of the obtained product is that the anion concentration produced is not high, and the efficacy persistence is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anion composite powder suitable for building materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment example 1

[0020] Weigh 30 parts of black tourmaline powder with a particle size of 30 μm, 1 part of wizard stone powder with a particle size of 15 μm, 1 part of sodium hexametaphosphate, 1 part of zinc oxide, 30 parts of rare earth, 30 parts of ferric oxide powder, and 8 parts of monazite powder Parts, mixed evenly by a dry powder mixer, you can get negative oxygen ion composite powder.

Embodiment example 2

[0022] Weigh 80 parts of black tourmaline powder with a particle size of 20 μm, 30 parts of wizard stone powder with a particle size of 40 μm, 8 parts of sodium hexametaphosphate, 5 parts of zinc oxide, 1 part of ferric oxide powder, and 1 part of monazite powder. The mixer mixes evenly, and the negative oxygen ion composite powder can be obtained.

Embodiment example 3

[0024] Weigh 40 parts of black tourmaline powder with a particle size of 10 μm, 20 parts of wizard stone powder with a particle size of 20 μm, 3 parts of sodium hexametaphosphate, 2 parts of zinc oxide, 5 parts of rare earth, 5 parts of ferric oxide powder, and 2 parts of monazite powder Parts, mixed evenly by a dry powder mixer, you can get negative oxygen ion composite powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anion composite powder suitable for building materials. The anion composite powder is prepared by the following components in parts by weight: 30 to 80 parts of black tourmaline powder, 1-30 parts of Qicai stone powder, 1-8 parts of sodium hexametaphosphate, 1-5 parts of zinc oxide, 0-30 parts of rare earth, 1-30 parts of ferriferrous oxide powder, and 1-8 parts of monazite powder. The technical scheme provided by the invention has the advantages that the production process is simple, the price of raw materials is low, an anion plate has durability, efficiency, and environmental protection, and the obtained anion plate as an environmental friendly anion additive can efficiently and stably release 2000 to 3800 anions / s.cm<2>, and can purify the air, and eliminate indoor odors and harmful gases.

Description

technical field [0001] The invention relates to a composite powder, in particular to an anion composite powder suitable for building materials. Background technique [0002] The impact of the living environment on the health of the people is constantly concerned. While people are pursuing luxurious and beautiful interior decoration, they are also concerned about the impact of indoor pollution on human health, the environmental protection of building materials, and the impact on human health. Therefore, various new building functional materials that are beneficial to health have emerged as the times require. [0003] Negative ion materials, as one of the representatives of new materials with multiple functions such as environmental protection and health, are widely used in textiles, ceramics, building materials and other fields. Since Aschkinass and Caspan affirmed that negative air ions have biological significance in 1902, and since Soviet scholars published a paper on usi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B24/04
CPCC04B40/0042C04B2111/00025C04B14/04C04B14/366C04B14/30C04B14/34C04B14/308C04B24/04
Inventor 杨卓舒刘建波车君超刘国强邝清林张磊
Owner ZHUO DA NEW MATERIAL TECH GRP