Composite component for promoting sewage flocculation

A technology for sewage treatment and coal gangue, applied in water/sewage treatment, water/sludge/sewage treatment, flocculation/sedimentation water/sewage treatment, etc. Sewage turbidity, simple and practical preparation method, and effect of improving sewage treatment efficiency

Pending Publication Date: 2016-06-15
叶君芝
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitations of technical conditions, the current domestic sewage treatment is still costly and inefficient. Many enterprises have to sacrifice the environment for their own survival, resulting in the deterioration of water resource pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1: the preparation of composite component

[0022] Raw material weight ratio:

[0023] Montmorillonite, 25 parts; Calcite, 20 parts; Attapulgite, 35 parts; Wollastonite, 15 parts; Borax, 15 parts; Heavy calcium carbonate, 10 parts; Talc powder, 10 parts; Mica powder and coal gangue The mixture, 7 parts; The ratio of the weight parts of described mica powder and coal gangue is 6:1.

[0024] Preparation:

[0025] Step S1, grinding the dried calcite, wollastonite, and ground calcium carbonate together to a fineness of 0.1-0.2mm;

[0026] Step S2, grinding the dried attapulgite, borax, and talcum together to a fineness of 0.08-0.1 mm;

[0027] Step S3, grinding the dried mica powder and coal gangue together to a fineness of 0.06-0.08 mm;

[0028] In step S4, the fine powders ground in steps S1, S2, and S3 are evenly mixed, and the finished product is packaged.

[0029] How to use: Add 0.8kg of composite components per 100kg of sewage.

Embodiment 2

[0030] Embodiment 2: the preparation of composite component

[0031] Raw material weight ratio:

[0032] Calcite, 15 parts; attapulgite, 30 parts; wollastonite, 10 parts; borax, 10 parts; heavy calcium carbonate, 5 parts; The weight ratio of mica powder and coal gangue is 5:1.

[0033] Preparation:

[0034] Step S1, grinding the dried calcite, wollastonite, and ground calcium carbonate together to a fineness of 0.1-0.2 mm;

[0035] Step S2, grinding the dried attapulgite, borax, and talcum together to a fineness of 0.08-0.1 mm;

[0036] Step S3, grinding the dried mica powder and coal gangue together to a fineness of 0.06-0.08mm;

[0037] In step S4, the fine powders ground in steps S1, S2, and S3 are evenly mixed, and the finished product is packaged.

[0038] How to use: Add 1kg of composite components per 100kg of sewage.

Embodiment 3

[0039] Embodiment 3: the preparation of composite component

[0040] Raw material weight ratio:

[0041] Calcite, 25 parts; attapulgite, 40 parts; wollastonite, 20 parts; borax, 20 parts; heavy calcium carbonate, 15 parts; The weight ratio of mica powder and coal gangue is 7:1.

[0042] Preparation:

[0043] Step S1, grinding the dried calcite, wollastonite, and ground calcium carbonate together to a fineness of 0.1-0.2mm;

[0044] Step S2, grinding the dried attapulgite, borax, and talcum together to a fineness of 0.08-0.1mm;

[0045] Step S3, grinding the dried mica powder and coal gangue together to a fineness of 0.06-0.08mm;

[0046] In step S4, the fine powders ground in steps S1, S2, and S3 are evenly mixed, and the finished product is packaged.

[0047] How to use: Add 0.6kg of composite components per 100kg of sewage.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite component for promoting sewage flocculation, which comprises the following raw materials in parts by weight: montmorillonite, 20-30 parts; calcite, 15-25 parts; attapulgite, 30-40 parts; wollastonite , 10-20 parts; borax, 10-20 parts; heavy calcium carbonate, 5-15 parts; talc powder, 5-15 parts; the mixture of mica powder and coal gangue, 6-8 parts; The ratio of parts by weight of gangue is 5-7:1. The composite component of the invention can well play the role of flocculation, effectively remove organic matter and heavy metal ions in the water body, reduce sewage turbidity, and improve sewage treatment efficiency. The preparation method provided by the invention is simple and practical, easy for large-scale preparation, and suitable for popularization.

Description

technical field [0001] The invention belongs to the field of environmental protection and relates to sewage treatment, in particular to a composite component for promoting sewage flocculation. Background technique [0002] With the rapid development of my country's economy, people's living standards have been greatly improved, but accompanied by increasingly serious environmental pollution problems. Monitoring data show that 13 of the 15 major urban river sections that the 7 major rivers flow through are seriously polluted, the quality of surface water and groundwater in many cities has deteriorated, and drinking water sources are threatened by pollution; It has reached 45 billion tons, basically discharged directly without treatment, causing serious pollution of my country's water resources, which has reached the level that must be treated. my country has taken environmental protection as its basic national policy, and environmental protection has increasingly become an imp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C02F1/52C02F101/30C02F101/20
CPCC02F1/5236C02F1/5263C02F2101/20C02F2101/30C02F2209/11
Inventor 叶君芝
Owner 叶君芝
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com