A kind of preparation method of lamellar porous graphene oxide and product thereof

A graphene and lamellar technology, which is applied in the field of preparation of lamellar porous graphene oxide, can solve the problems of limiting the application of directional freezing method, random nucleation process, etc., and achieves the effects of sufficient raw materials, low cost and simple preparation method.

Active Publication Date: 2017-11-17
ZHEJIANG UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, due to the existence of a single temperature gradient in the traditional directional freezing method, the nucleation process of ice crystals on the bottom surface of the crystal is random, resulting in multi-dimensional small-scale orientations on the section perpendicular to the freezing direction.
This shortcoming severely limits the application of directional freezing for applications requiring large-area oriented lamellar porous structures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of lamellar porous graphene oxide and product thereof
  • A kind of preparation method of lamellar porous graphene oxide and product thereof
  • A kind of preparation method of lamellar porous graphene oxide and product thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] (1) Dissolve 20mg GO and 10mgPVA in 4ml H at 20°C 2 O, Ultrasound in an ultrasonic cell pulverizer for 5 minutes to fully dissolve, and vacuum remove air bubbles to obtain a homogeneous solution, wherein the concentration of GO in the solution is 5.0mg / mL, and the concentration of the binder in the solution is 2.5mg / mL;

[0050] (2) Place the solution obtained in step (1) in a container with a wedge-shaped silicone rubber device. The slope of the wedge-shaped silicone rubber device is 15°, and use frozen ethanol (-90°C) as the cold source to perform two-way freezing to obtain the intermediate product;

[0051] (3) Freeze-drying the intermediate product obtained in step (2) for 24 hours to remove the solvent to obtain lamellar porous graphene oxide, which has a regular layered porous structure with large-area orientation.

Embodiment 2

[0053] (1) Dissolve 20mg GO and 20mgPVA in 4ml H at 20°C 2 O, Ultrasound in an ultrasonic cell pulverizer for 5 minutes to fully dissolve, and vacuum remove air bubbles to obtain a homogeneous solution, wherein the concentration of GO in the solution is 5.0 mg / mL, and the concentration of the binder in the solution is 5.0 mg / mL;

[0054] (2) Place the solution obtained in step (1) in a container with a wedge-shaped silicone rubber device. The slope of the wedge-shaped silicone rubber device is 15°, and use frozen ethanol (-90°C) as the cold source to perform two-way freezing to obtain the intermediate product;

[0055] (3) Freeze-drying the intermediate product obtained in step (2) for 24 hours to remove the solvent to obtain porous graphene oxide, which has a regular layered porous structure with large-area orientation.

Embodiment 3

[0057] (1) Dissolve 20mg GO and 40mgPVA in 4ml H at 20°C 2 O, Ultrasound in an ultrasonic cell pulverizer for 5 minutes to fully dissolve, remove air bubbles in a vacuum to obtain a homogeneous solution, wherein the concentration of GO in the solution is 5.0mg / mL, and the concentration of the binder in the solution is 10.0mg / mL;

[0058] (2) The solution obtained in step (1) is placed in a container with a wedge-shaped silicone rubber device, the slope of the wedge-shaped silicone rubber device is 15°, and it is subjected to two-way freezing with frozen ethanol (-90° C.) as a cold source to obtain mid product;

[0059] (3) Freeze-drying the intermediate product obtained in step (2) for 24 hours to remove the solvent to obtain porous graphene oxide, which has a regular layered porous structure with large-area orientation.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
pore sizeaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of lamellar porous graphene oxide. The preparation method comprises the following steps: (1) dissolving graphene oxide and a binding agent into water to prepare a precursor solution; (2) putting the precursor solution into a container and carrying out a bidirectional freezing reaction to obtain an intermediate product, wherein a wedge-shaped device is arranged at the bottom of the container; (3) freezing and drying the intermediate product obtained by the step (2) to remove a solvent, so as to obtain the lamellar porous graphene oxide. The invention further relates to the lamellar porous graphene oxide. The method is simple to operate; the lamellar porous graphene oxide prepared by a bidirectional freezing method has a regular large-area and biaxial orientated lamellar porous structure.

Description

technical field [0001] The invention relates to the field of preparation of porous materials, in particular to a method for preparing sheet-layer porous graphene oxide and its products. Background technique [0002] Porous material is a material with a network structure of interpenetrating or closed pores, mainly composed of a continuous solid phase forming the basic framework of the material itself and a fluid phase forming pores. Compared with continuum materials, porous materials generally have the advantages of low relative density, high specific strength, high specific surface area, sound insulation, heat insulation, and good permeability. Its application scope is far beyond single-functional materials, and it has important applications in tissue engineering, catalyst carrier, adsorption carrier, barrier material, foam material, separation filter material, electrode material, etc., and is gradually attracting people's attention. [0003] According to the size of the po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B32/198
CPCC01B2204/04C01B2204/32C01P2004/03
Inventor 杨苗高微微赵骞谢涛柏浩
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com