Hybrid supermolecule room temperature phosphorescent material and preparation method thereof

A room temperature phosphorescence, supramolecular technology, applied in luminescent materials, chemical instruments and methods, chemical/physical processes, etc., can solve the problems of long time, heavy metal ion environmental pollution, harsh conditions, etc., to avoid quenching and inhibit thermal motion. , reducing the effect of non-radiative transitions

Inactive Publication Date: 2016-06-22
HUAZHONG UNIV OF SCI & TECH
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If you use inert gas to remove oxygen, it will cause a large number of bubbles in the system, and the time for ventilation and deoxygenation will be long (2-3 hours); although the time is short when using sodium sulfite to remove oxygen, the conditions are harsh, and generally need to be in neutral or weakly acidic conditions and the addition of heavy metal ions will lead to environmental pollution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hybrid supermolecule room temperature phosphorescent material and preparation method thereof
  • Hybrid supermolecule room temperature phosphorescent material and preparation method thereof
  • Hybrid supermolecule room temperature phosphorescent material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] This embodiment provides a hybrid supramolecular room temperature phosphorescent material, and its preparation method is as follows: take a clean beaker, add 10mL5×10 -5 mol / LPd-TCPP solution in DMSO, 25mL5×10 -4 mol / L Gemini surfactant 11-6-11 aqueous solution, at a stirring speed of 300 rpm, heated in a water bath to 80°C, kept warm for 8 minutes, and added 65mL2.8×10 -1 The DMSO solution of mol / LDBS was continuously stirred at a speed of 300 rpm for 5 minutes, then cooled to room temperature, and the obtained supramolecular gel was the hybrid supramolecular room temperature phosphorescent material of the present invention.

Embodiment 2

[0029] This example provides a hybrid supramolecular room temperature phosphorescent material and its preparation method, the preparation method is as follows: take a clean beaker, add 15mL5 × 10 -5 mol / LPd-TCPP solution in DMSO, 40mL5×10 -4 mol / L Gemini surfactant 9-8-9 aqueous solution, at a stirring speed of 300 rpm, heated in a water bath at 50°C for 1min, kept warm for 10 minutes, added 45mL2.8×10 -1 The DMSO solution of mol / LDBS is continuously stirred at a speed of 300 rpm for 5 minutes, and then the supramolecular gel obtained by static cooling is the hybrid supramolecular room temperature phosphorescent material of the present invention.

Embodiment 3

[0031] This embodiment provides a hybrid supramolecular room temperature phosphorescent material, and its preparation method is as follows: take a clean beaker, add 5mL5×10 -5 mol / LPd-TCPP solution in DMSO, 15mL5×10 -4 mol / L Gemini surfactant 17-10-17 aqueous solution, at a stirring speed of 300 rpm, heated at 90°C in a water bath, kept warm for 8 minutes, and added 80mL2.8×10 -1 The DMSO solution of mol / LDBS was continuously stirred at a speed of 300 rpm for 5 minutes, then cooled to room temperature, and the obtained supramolecular gel was the hybrid supramolecular room temperature phosphorescent material of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hybrid supermolecule room temperature phosphorescent material and a preparation method thereof. The material is prepared through adding Pd-TCPP into DBS supermolecule gel hybridized by a gemini surfactant. The material can obtain high-intensity room temperature phosphorescence; more importantly, in the material preparation process, the additional addition of deoxygenization or heavy metal addition is not needed; a simple and convenient method is used for obtaining the room temperature phosphorescent material. Compared with the non-hybrid supermolecule gel not adding the gemini surfactant, the material adapts to a wider luminous pH range which can reach pH 2 to 7. The material is hopeful to be used in the fields of sensors and anti-counterfeiting materials.

Description

technical field [0001] The invention belongs to the field of luminescent materials, and in particular relates to a hybrid supramolecular room temperature phosphorescent material and a preparation method thereof. Background of the invention [0002] Due to the larger Stokes shift and longer lifetime of phosphorescence, it can avoid the interference of excitation light, short-lived fluorescence and scattered light, and obtain lower detection limits. In order to control the non-radiative transition of phosphorescent molecules, obtaining phosphorescence usually requires low temperature conditions, which greatly limits the application of phosphorescence. The later developed room temperature phosphorescence is widely used in the fields of life science, environmental science, clinical medicine and industrial energy because its luminescence no longer requires harsh low temperature conditions. Room temperature phosphorescent materials usually need to remove oxygen to prevent phospho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K11/02C09K11/06B01F17/18C09K23/18
CPCC09K11/025C09K11/06C09K2211/1074C09K2211/1007C09K2211/1029C09K23/00
Inventor 王宏朱婷玉杨亚江解孝林郑成赋廖永贵
Owner HUAZHONG UNIV OF SCI & TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com