A kind of usy molecular sieve and preparation method thereof

A molecular sieve and molar ratio technology, applied in molecular sieve catalysts, chemical instruments and methods, physical/chemical process catalysts, etc., can solve problems such as poor hydrothermal stability, nano Y-type molecular sieves that cannot be widely promoted, and crystal channel topology collapse. , to achieve the effects of strong anti-coking ability, good catalytic activity and diffusion performance

Active Publication Date: 2017-08-22
CHINA PETROLEUM & CHEM CORP +1
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the poor hydrothermal stability of the synthesized nano Y-type molecular sieve, the crystal channel topology completely collapsed during the hydrothermal treatment process.
Therefore, nano Y-type molecular sieves cannot be widely promoted in practical applications.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of usy molecular sieve and preparation method thereof
  • A kind of usy molecular sieve and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) According to the molar ratio of n (Na 2 O): n (Al 2 o 3 ): n (SiO 2 ): n (H 2 O)=18.4:1:19.8:370, under stirring, add sodium aluminate, sodium hydroxide, water, and water glass to the beaker in turn to form a mixed solution, and then age at 30°C for 1 day to obtain the directing agent .

[0027] (2) According to the molar ratio of each material in the gel (excluding the added nano Y-type molecular sieve) is n (NaOH): n (Al 2 o 3 ): n (SiO 2 ): n (H 2 O)=14:1:24:520. Under the condition of stirring, add water, aluminum source, sodium hydroxide and water glass into the beaker in order to form a mixed solution, then add nano Y-type molecular sieve and the directing agent prepared in step (1), stir well Constant temperature crystallization at 100°C for 60 hours. Then after cooling, washing, suction filtration and drying, Y-Y composite molecular sieves are obtained, wherein the quality of the added nanometer Y-type molecular sieve accounts for 8wt% of t...

Embodiment 2

[0032] (1) According to the molar ratio of n (Na 2 O): n (Al 2 o 3 ): n (SiO 2 ): n (H 2 O)=18:1:19:350, under stirring, add sodium aluminate, sodium hydroxide, water, and water glass to the beaker in turn to form a mixed solution, and then age at 35°C for 1 day to prepare the directing agent .

[0033] (2) According to the molar ratio of each material in the gel (excluding the added nano Y-type molecular sieve) is n (NaOH): n (Al 2 o 3 ): n (SiO 2 ): n (H 2 O)=15:1:21:580. Under the condition of stirring, add water, sodium aluminate, sodium hydroxide and water glass into the beaker in turn to form a mixed solution, then add nano Y-type molecular sieve and the directing agent prepared in step (1), stir well and pour the condensed The glue was crystallized at a constant temperature of 95°C for 48 hours. Then after cooling, washing, suction filtration and drying, Y-Y composite molecular sieves are obtained, wherein the quality of the added nanometer Y-type mole...

Embodiment 3

[0038] (1) According to the molar ratio of n (Na 2 O): n (Al 2 o 3 ): n (SiO 2 ): n (H 2 O)=18:1:19:330, under stirring, add sodium aluminate, sodium hydroxide, water, and water glass to the beaker in turn to form a mixed solution, and then age at 50°C for 0.5 days to obtain the directing agent .

[0039] (2) According to the molar ratio of each material in the gel (excluding the added nano Y-type molecular sieve) is n (NaOH): n (Al 2 o 3 ): n (SiO 2 ): n (H 2 O)=15:1:24:600. Under the condition of stirring, add water, sodium aluminate, sodium hydroxide and water glass into the beaker in turn to form a mixed solution, then add nano Y-type molecular sieve and the directing agent prepared in step (1), stir well and pour the condensed The glue was crystallized at a constant temperature of 98° C. for 48 hours. Then after cooling, washing, suction filtration and drying, Y-Y composite molecular sieves are obtained, wherein the quality of the nano Y-type molecular s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
crystal sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a USY molecular sieve, the USY molecular sieve has a hollow structure, the molar ratio of silica / alumina in the molecular sieve is 4.5-25, the grain size is 0.5-1.2 μm, and the specific surface area is 420-800 m 2 / g, the pore volume is 0.33~0.82ml / g, and the average pore diameter is 1.5~4.0nm. The USY molecular sieve has more exposed reactive centers, greatly shortens the diffusion distance of reactants, and improves the catalytic performance of the molecular sieve.

Description

technical field [0001] The invention relates to a USY molecular sieve and a preparation method thereof. Background technique [0002] Y-type molecular sieve is formed by octahedral molecular sieve cages interpenetrating with each other along three crystal axis directions through twelve-membered rings. It is an excellent catalyst active component, not only has high cracking activity, but also has good selectivity. Therefore, the discovery and use of Y-type molecular sieve has epoch-making significance in the field of catalysis. [0003] Since Y-type molecular sieves with a low silicon-aluminum ratio (the molar ratio of silicon oxide to aluminum oxide is between 3 and 4.2) do not have good hydrothermal stability, they have not been widely studied and widely used in the actual synthesis process and application. attention. The high silicon-aluminum ratio Y-type molecular sieve (the molar ratio of silicon oxide to aluminum oxide is above 4.3) has good hydrothermal stability and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/24B01J29/08
Inventor 秦波杜艳泽柳伟张晓萍王凤来
Owner CHINA PETROLEUM & CHEM CORP