Nanopowder coating with super abrasion resistance

A powder coating, super wear-resistant technology, applied in powder coatings, polyester coatings, coatings, etc., can solve the problems of affecting the smoothness and gloss of the coating film, low powder application rate, and the appearance quality of the coating film. The effect of high rate, excellent film-forming performance and excellent wear resistance

Inactive Publication Date: 2016-07-06
TAICANG JIDA SPRAY COATING CO LTD
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing powder coatings are prone to orange peel during film formation, which affects the smoothness and gloss of the coating film, and the appearance quality of the coating film decreases, and the powder coating rate is low due to the gravity of the powder coating itself.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A nanometer super wear-resistant powder coating, including raw materials: polyester resin, nanometer silicon carbide, nanometer silicon nitride, titanium dioxide, curing agent, barium sulfate, leveling agent, brightening agent and electrifying agent, according to the mass percentage Calculated, polyester resin accounts for 55%, nano silicon carbide 15%, nano silicon nitride 5%, titanium dioxide 8%, curing agent 5%, barium sulfate 6%, leveling agent 2%, brightener 2% 2%, energizer accounts for 2%.

[0012] Wherein, the polyester resin adopts hydroxyl polyester resin, and its acid value is 35 mgKOH / g.

[0013] The particle size of the nanometer super wear-resistant powder coating is 55 nm.

Embodiment 2

[0015] A nanometer super wear-resistant powder coating, including raw materials: polyester resin, nanometer silicon carbide, nanometer silicon nitride, titanium dioxide, curing agent, barium sulfate, leveling agent, brightening agent and electrifying agent, according to the mass percentage Calculated, polyester resin accounts for 59%, nano silicon carbide 12%, nano silicon nitride 4%, titanium dioxide 12%, curing agent 3%, barium sulfate 4%, leveling agent 4%, brightener 4% 1%, 1% of the booster.

[0016] Wherein, the polyester resin adopts hydroxyl polyester resin, and its acid value is 36 mgKOH / g.

[0017] The particle size of the nanometer super wear-resistant powder coating is 65 nm.

Embodiment 3

[0019] A nanometer super wear-resistant powder coating, including raw materials: polyester resin, nanometer silicon carbide, nanometer silicon nitride, titanium dioxide, curing agent, barium sulfate, leveling agent, brightening agent and electrifying agent, according to the mass percentage Calculate, polyester resin accounts for 60%, nano silicon carbide 12%, nano silicon nitride 4%, titanium dioxide 11%, curing agent 2%, barium sulfate 5%, leveling agent 2%, brightener 2% 3%, 1% of the booster.

[0020] Wherein, the polyester resin adopts hydroxyl polyester resin, and its acid value is 38 mgKOH / g.

[0021] The particle size of the nanometer super wear-resistant powder coating is 90 nm.

[0022] The invention discloses a nanometer super wear-resistant powder coating. By adding low-density wear-resistant materials nanometer silicon carbide and nanometer silicon nitride in a reasonable proportion to polyester resin, the obtained powder coating has excellent wear resistance. an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
particle diameteraaaaaaaaaa
acid valueaaaaaaaaaa
Login to view more

Abstract

The invention discloses a nanometer super wear-resistant powder coating, which comprises the following raw materials: polyester resin, low-density nanometer wear-resistant powder, titanium dioxide, curing agent, barium sulfate, leveling agent, brightener and charging agent, according to Calculated by mass percentage, polyester resin accounts for 55%-60%, low-density nano wear-resistant powder accounts for 15%-20%, titanium dioxide accounts for 8%-12%, curing agent accounts for 2%-5%, and barium sulfate accounts for 4%. -6%, leveling agent accounts for 2%-4%, brightener accounts for 1%-3%, and booster accounts for 1%-2%. The low-density nano-nano powder is made of nano-silicon carbide and nano-silicon nitride mixture. Through the above method, the present invention has excellent wear resistance and film-forming performance, and the powder coating rate is high when electrostatic spraying is adopted, and the obtained film layer can be uniform, smooth and smooth.

Description

technical field [0001] The invention relates to the field of powder coatings, in particular to a nanometer super wear-resistant powder coating. Background technique [0002] Powder coating is a new type of solvent-free 100% solid powdered environmentally friendly coating. It has the advantages of high coating efficiency, good protection and decorative performance, etc., and has received extensive attention all over the world, thus achieving sustained and rapid development. Especially in the aspect of aluminum alloy building materials, compared with the surface treatment methods of anodizing and electrophoretic coating, the pollution degree of water and air and energy consumption are obviously reduced, the mechanical properties of the coating film are greatly improved, and the service life is longer than that of ordinary anodized aluminum materials. It is 1 times higher and has rich colors, which can better reflect the diversification and individualization of buildings. There...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D5/03C09D7/12
CPCC09D167/00C08K3/22C08K3/30C08K3/34C08K13/02C08K2003/2241C08K2003/3045C08K2201/011C08K2201/014C09D5/033C09D7/40C09D7/61
Inventor 朱文吉
Owner TAICANG JIDA SPRAY COATING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap