Bra pad prepared from PU (polyurethane) flexible adhesive

A soft, bra-like technology, applied in applications, clothing, brassieres, etc., can solve problems such as high labor costs, poor softness, and easy deformation of pads, and achieve the effects of saving manpower and material resources, increasing production cycle, and improving production efficiency

Inactive Publication Date: 2016-08-24
柯永展 +2
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, more than 90% of the material of bra pads on the market is sponge. The big problem with pads made of sponge is that they are easily deformed and not durable after washing, and the shape will disappear soon after washing many times.
The sponge processing process is complicated, such as cutting, cotton digging, high-temperature shaping, trimming, etc. The labor cost is high, and there is a lot of waste, which will also cause environmental pollution around the processing
Since the sponge is molded by high-stability hot ironing, the softness and hardness of the side of the pad and the middle position are very different. It is relatively hard and soft, which affects the comfort and breathability of wearing, and it cannot be complemented at any time according to the characteristics of the human body.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0021] The bra liner made of a kind of PU soft glue of the present invention, the raw material that selects comprises:

[0022] Polyether polyurethane resin 93.5-99.2% (main material), of which, diphenylmethane diisocyanate (MDI) 15.8-21.5% (black material), polyether polyol 75.5-79.8% (white material) , butanediol is 1.85-2.8% (white material), catalyst 0.05-0.3% (white material), cyclopentane physical foaming agent 0.2-0.45% (white material).

[0023] The p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bra pad prepared from a PU (polyurethane) flexible adhesive. The bra pad is prepared from 93.5-99.2% of polyether-type polyurethane resin (main body material). The main body material comprises 15.8-21.5% of diphenylmethane diisocyanate (MDI) (black material), 75.5-79.8% of polyether glycol (white material), 1.85-2.8% of butanediol (white material), 0.05-0.3% of catalyst (white material) and 0.2-0.45% of cyclopentane physical foaming agent (white material). The polyether-type polyurethane resin, black materials and white materials are proportionally mixed thoroughly to obtain the required PU flexible adhesive. The prepared PU flexible adhesive is injected into a mold with the temperature of 50-55 DEG C and subjected to primary foam forming. The PU flexible adhesive has the skin-like sensation, and the bra pad is subjected to integral forming through the mold, thereby saving abundant human and material resources and enhancing the efficiency.

Description

technical field [0001] The invention relates to the technical field of bra pad production, in particular to a bra pad made of PU soft glue. Background technique [0002] At present, more than 90% of the material of bra pads on the market is sponge. The big problem with pads made of sponge is that they are easily deformed and not durable after washing, and the shape will disappear soon after washing many times. The sponge processing process is complicated, such as cutting, cotton digging, high-temperature shaping, trimming, etc. The labor cost is high, and there are many waste materials, which will also cause environmental pollution around the processing. Since the sponge is molded by high-stability hot ironing, the softness and hardness of the side of the pad and the middle position are very different. It is relatively hard and soft, which affects the comfort and breathability of wearing, and it cannot be complemented at any time according to the characteristics of the human...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/08C08G18/66C08G18/48C08G18/32C08J9/14A41C3/14
Inventor 柯永展柯永龙徐富强
Owner 柯永展
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products