Kenixiao material and use method thereof

A technology that suppresses mud effect and mass fraction is applied in the direction of earthwork drilling, mining equipment, tunnels, etc. It can solve the problems that cannot be used to fill the shield gap, the cavity cannot be filled, and any construction cannot be continued, so as to reduce output The effect of reducing the cost of the hole, solving the gushing problem, and avoiding ground subsidence

Inactive Publication Date: 2016-09-21
沈阳市百德旺建筑材料科技有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Now the shield machine industry generally uses cement slurry and water glass as the material for back grouting and secondary grouting of the shield machine. These two materials can effectively fill the gap above the segment, but they cannot be used for filling. The gap above the shield body, because the shield machine will be stuck after the cement slurry solidifies, and no further construction can be continued
Therefore, there is no way to fill the void above the shield body, and the problem of ground subsidence has been unavoidable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The purpose of this embodiment is to provide a new type of mud-restraining material, which is suitable for filling the gap between the shield body of the shield machine and the formation.

[0029] This embodiment specifically provides a kind of gram mud effect material, including material A and material B, wherein, material A is the basic material, including the following mass fraction substances: modified inorganic calcium carbonate 85.5 ~ 99.5%, calcareous cellulose 14.5% ~0.5%;

[0030] Material B is an auxiliary material, including the following mass fraction substances: 0.5-10% plasticizer, 0.1-3% thickener, 2-20% penetrant, 2-20% waterproof agent, 0.5-10% stabilizer, Water 50~80%.

[0031] Specifically, material A includes the following mass fraction substances: modified inorganic calcium carbonate 90.5~97.5%, calcareous cellulose 9.5~2.5%; material B includes the following mass fraction substances: plasticizer 4~6%, thickening 1~2% agent, 8~12% penetrating agen...

Embodiment 2

[0049] In addition to this embodiment,

[0050] Material A includes the following mass fraction substances: 94% modified inorganic calcium carbonate, 6% calcareous cellulose;

[0051] Material B includes the following mass fraction substances: 4.5% plasticizer, 1% thickener, 11% penetrating agent, 11% waterproofing agent, 2% stabilizer, 70.5% water;

[0052] All the other formulas, proportioning, methods of use, technical solutions, and implementation effects are the same as in Example 1.

Embodiment 3

[0054] In addition to this embodiment,

[0055] Material A includes the following mass fraction substances: 96% modified inorganic calcium carbonate, 4% calcareous cellulose;

[0056] Material B includes the following mass fraction substances: 6% plasticizer, 2% thickener, 9% penetrating agent, 9% waterproof agent, 4% stabilizer, 70% water;

[0057] All the other formulas, proportioning, methods of use, technical solutions, and implementation effects are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a Kenixiao material. A material A is a base material comprising the following substances in percentage by mass: 95.5% of modified inorganic calcium carbonate, and 4.5% of calcium cellulose; and a material B is an auxiliary material comprising the following substances in percentage by mass: 5% of a plasticizer, 1.5% of a thickener, 10% of a penetrant, 10% of a waterproof agent, 3% of a stabilizer, and 70.5% of water. A use method of the Kenixiao material comprises the steps of: mixing the material A with water, preparing the material B, mixing all the materials, performing injection, and performing cleaning. The Kenixiao material disclosed by the invention has the characteristics of high water tightness, rapid molding, capabilities of never being solidified and becoming viscous quickly. By utilization of an original grouting pump on a shield tunneling machine, the Kenixiao material disclosed by the invention is injected to the periphery of a shield body by virtue of an advanced grouting hole to fill up gaps above the shield body, so that accidents of land subsidence and the like during construction of the shield tunneling machine can be effectively avoided, then the capability of preventing potential safety hazards is improved, and personnel casualties and property losses are reduced.

Description

technical field [0001] The invention relates to a building material, and in particular provides a novel mud-restraining material and a using method. Background technique [0002] At present, all shield tunneling methods will encounter an unavoidable problem that is ground subsidence. The large amount of ground subsidence will cause accidents such as ground subsidence, building collapse, and underground pipeline rupture. Since the diameter of the cutter head of the shield machine is larger than the diameter of the shield body, the diameter of the hole formed after the cutter head is excavated is larger than the diameter of the shield body, and a hole is conveniently formed on the shield body. If the void is not filled in time, ground subsidence will occur. Now the shield machine industry generally uses cement slurry and water glass as the material for back grouting and secondary grouting of the shield machine. These two materials can effectively fill the gap above the segme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/28E21D9/08
CPCC04B26/285E21D9/08
Inventor 李梦晨
Owner 沈阳市百德旺建筑材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap